Developing cost effective electrocatalysts with high oxygen evolution reaction (OER) activity is essential for large‐scale application of many electrochemical energy systems. Although the impacts of either lattice strain or oxygen defects on the OER performance of oxide catalysts have been extensively investigated, the effects of both factors are normally treated separately. In this work, the coupled effects of both strain and oxygen deficiency on the electrocatalytic activity of La0.7Sr0.3CoO3−δ(LSC) thin films grown on single crystal substrates (LaAlO3 (LAO) and SrTiO3 (STO)) are investigated. Electrochemical tests show that the OER activities of LSC films are higher under compression than under tension, and are diminished as oxygen vacancies are introduced by vacuum annealing. Both experimental and computational results indicate that the LSC films under tension (e.g., LSC/STO) have larger oxygen deficiency than the films under compression (e.g., LSC/LAO), which attribute to smaller oxygen vacancy formation energy. Such strain‐induced excessive oxygen vacancies in the LSC/STO increases the
Developing low‐cost, high‐performance electro‐catalysts is essential for large‐scale application of electrochemical energy devices. In this article, reported are the findings in understanding and controlling oxygen defects in PrBa0.5Sr0.5Co1.5Fe0.5O5+
- Award ID(s):
- 1742828
- NSF-PAR ID:
- 10460354
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 29
- Issue:
- 34
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract eg state occupancy and enlarges the energy gap between the O 2p and Co 3d band, resulting in lower OER activity. Understanding the critical role of strain–defect coupling is important for achieving the rational design of highly active and durable catalysts for energy devices. -
more » « less
Abstract Designing highly active and robust catalysts for the oxygen evolution reaction is key to improving the overall efficiency of the water splitting reaction. It has been previously demonstrated that evaporation induced self‐assembly (EISA) can be used to synthesize highly porous and high surface area cerate‐based fluorite nanocatalysts, and that substitution of Ce with 50% rare earth (RE) cations significantly improves electrocatalyst activity. Herein, the defect structure of the best performing nanocatalyst in the series are further explored, Nd2Ce2O7, with a combination of neutron diffraction and neutron pair distribution function analysis. It is found that Nd3 +cation substitution for Ce in the CeO2fluorite lattice introduces higher levels of oxygen Frenkel defects and induces a partially reduced RE1.5Ce1.5O5 +
x phase with oxygen vacancy ordering. Significantly, it is demonstrated that the concentration of oxygen Frenkel defects and improved electrocatalytic activity can be further enhanced by increasing the compositional complexity (number of RE cations involved) in the substitution. The resulting novel compositionally‐complex fluorite– (La0.2Pr0.2Nd0.2Tb0.2Dy0.2)2Ce2O7is shown to display a low OER overpotential of 210 mV at a current density of 10 mAcm−2in 1M KOH, and excellent cycling stability. It is suggested that increasing the compositional complexity of fluorite nanocatalysts expands the ability to tailor catalyst design. -
more » « less
Abstract Sn‐based materials are identified as promising catalysts for the CO2electroreduction (CO2RR) to formate (HCOO−). However, their insufficient selectivity and activity remain grand challenges. A new type of SnO2nanosheet with simultaneous N dopants and oxygen vacancies (
V O‐rich N‐SnO2NS) for promoting CO2conversion to HCOO−is reported. Due to the likely synergistic effect of N dopant andV O, theV O‐rich N‐SnO2NS exhibits high catalytic selectivity featured by an HCOO−Faradaic efficiency (FE) of 83% at− 0.9 V and an FE of> 90% for all C1 products (HCOO−and CO) at a wide potential range from −0.9 to− 1.2 V. Low coordination Sn–N moieties are the active sites with optimal electronic and geometric structures regulated byV Oand N dopants. Theoretical calculations elucidate that the reaction free energy of HCOO* protonation is decreased on theV O‐rich N‐SnO2NS, thus enhancing HCOO−selectivity. The weakened H* adsorption energy also inhibits the hydrogen evolution reaction, a dominant side reaction during the CO2RR. Furthermore, using the catalyst as the cathode, a spontaneous Galvanic Zn‐CO2cell and a solar‐powered electrolysis process successfully demonstrated the efficient HCOO−generation through CO2conversion and storage. -
more » « less
Abstract Recent emphasis on carbon dioxide utilization has necessitated the exploration of different catalyst compositions other than copper-based systems that can significantly improve the activity and selectivity towards specific CO2 reduction products at low applied potential. In this study, a binary CoTe has been reported as an efficient electrocatalyst for CO2reduction in aqueous medium under ambient conditions at neutral pH. CoTe showed high Faradaic efficiency and selectivity of 86.83 and 75%, respectively, for acetic acid at very low potential of − 0.25 V vs RHE. More intriguingly, C1 products like formic acid was formed preferentially at slightly higher applied potential achieving high formation rate of 547.24 μmol cm−2 h−1 at − 1.1 V vs RHE. CoTe showed better CO2RR activity when compared with Co3O4, which can be attributed to the enhanced electrochemical activity of the catalytically active transition metal center as well as improved intermediate adsorption on the catalyst surface. While reduced anion electronegativity and improved lattice covalency in tellurides enhance the electrochemical activity of Co, high d-electron density improves the intermediate CO adsorption on the catalyst site leading to CO2reduction at lower applied potential and high selectivity for C2products. CoTe also shows stable CO2RR catalytic activity for 50 h and low Tafel slope (50.3 mV dec–1) indicating faster reaction kinetics and robust functionality. Selective formation of value-added C2products with low energy expense can make these catalysts potentially viable for integration with other CO2capture technologies thereby, helping to close the carbon loop.
-
more » « less
Abstract In this work, an organic‐inorganic hybrid crystal, violet‐crystal (VC), was used to etch the nickel foam (NF) to fabricate a self‐standing electrode for the water oxidation reaction. The efficacy of VC‐assisted etching manifests the promising electrochemical performance towards the oxygen evolution reaction (OER), requiring only ~356 and ~376 mV overpotentials to reach 50 and 100 mA cm−2, respectively. The OER activity improvement is attributed to the collectively exhaustive effects arising from the incorporation of various elements in the NF, and the enhancement of active site density. Furthermore, the self‐standing electrode is robust, exhibiting a stable OER activity after 4,000 cyclic voltammetry cycles, and ~50 h. The anodic transfer coefficients (
α a) show that the first electron transfer step is the rate‐determining step on the surface of NF‐VCs‐1.0 (NF etched by 1 g of VCs) electrode, while the chemical step involving dissociation following the first electron transfer step is identified as the rate‐limiting step in other electrodes. The lowest Tafel slope value observed in the NF‐VCs‐1.0 electrode indicates the high surface coverage of oxygen intermediates and more favorable OER reaction kinetics, as confirmed by high interfacial chemical capacitance and low charge transport/interfacial resistance. This work demonstrates the importance of VCs‐assisted etching of NF to activate the OER, and the ability to predict reaction kinetics and rate‐limiting step based onα avalues, which will open new avenues to identify advanced electrocatalysts for the water oxidation reaction.