Abstract Hydrolytically degradable poly(β‐thioether ester ketal) thermosets are synthesized via radical‐mediated thiol‐ene photopolymerization using three novel dialkene acyclic ketal monomers and a mercaptopropionate based tetrafunctional thiol. For all thermoset compositions investigated, degradation behavior is highly tunable based on the structure of the incorporated ketal and pH. Complete degradation of the thermosets is observed upon exposure to acidic and neutral pH, and under high humidity conditions. Polymer networks composed of cross‐link junctions based on acyclic dimethyl ketals degrade the quickest, whereas networks containing acyclic cyclohexyl ketals undergo hydrolytic degradation on a longer timescale. Thermomechanical analysis reveals low glass transition temperatures and moduli typical of thioether‐based thermosets.
more »
« less
Hydrolytically degradable poly(β-thioether ester ketal) thermosets via radical-mediated thiol–ene photopolymerization
Thiol–ene photopolymerization was exploited for the synthesis of poly(β-thioether ester ketal) networks capable of undergoing complete degradation under acid and/or basic conditions. Using the design of four novel bisalkene diketal monomers, we demonstrate the ability to tune degradation profiles under acidic conditions with timescales dictated by the structure of the diketal linker, while hydrolysis of the β-thioether ester functionality dominates the degradation profile under basic conditions irrespective of the diketal structure. All four poly(β-thioether ester ketal) networks exhibited degradation behavior characteristic of a surface erosion process. The networks showed mechanical (low modulus) and thermomechanical properties (low T g ) typical of thiol–ene thermosets with minimal influence from the structure of the diketal linkage. To highlight the advantages of endowing a step-growth network with ketal linker chemistry, we demonstrated the ability to recover diketone precursors from the thermoset degradation by-products and recycle these compounds into building blocks for additional thermoset materials.
more »
« less
- PAR ID:
- 10172681
- Date Published:
- Journal Name:
- Polymer Chemistry
- Volume:
- 10
- Issue:
- 41
- ISSN:
- 1759-9954
- Page Range / eLocation ID:
- 5635 to 5644
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Thermoset networks are chemically cross-linked materials that exhibit high heat resistance and mechanical strength; however, the permanently cross-linked system makes end-of-life degradation difficult. Thermosets that are inherently degradable and made from renewably derived starting materials are an underexplored area in sustainable polymer chemistry. Here, we report the synthesis of novel sugar- and terpene-based monomers as the enes in thiol–ene network formation. The resulting networks showed varied mechanical properties depending on the thiol used during cross-linking, ranging from strain-at-breaks of 12 to 200%. Networks with carveol or an isosorbide-based thiol incorporated showed plastic deformation under tensile stress testing, while geraniol-containing networks demonstrated linear stress–strain behavior. The storage modulus at the rubbery plateau was highly dependent on the thiol cross-linker, showing an order of magnitude difference between commercial PETMP, DTT, and synthesized Iso2MC. Thermal degradation temperatures were low for the networks, primarily below 200 °C, and the Tg values ranged from −17 to 31 °C. Networks were rapidly degraded under basic conditions, showing complete degradation after 2 days for nearly all synthesized thermosets. This library demonstrates the range of thermal and mechanical properties that can be targeted using monomers from sugars and terpenes and expands the field of renewably derived and degradable thermoset network materials.more » « less
-
null (Ed.)Photoinduced thiol-catalyzed hydrogen abstraction and β-scission of acyclic benzylidene acetals is demonstrated as a new route to “command-destruct” polymer thermosets. Using this approach, we show that poly(thioether acetal) networks synthesized via thiol–ene photopolymerization rapidly degrade to alkyl benzoate byproducts when triggered with light, transitioning from solid to liquid within seconds. The light-driven construction and destruction processes, accessible via distinct differences in kinetics, are readily amenable for photopatterning, additive/subtractive manufacturing and wavelength-selective applications.more » « less
-
null (Ed.)The development of tunable and degradable crosslinked-polyanhydride networks from renewably derived itaconic anhydrides and multifunctional thiols is presented. Itaconic acid was initially converted to ethyl itaconic anhydride and isoamyl itaconic anhydride via a two-step synthetic procedure on hundred-gram scale with minimal purification. Dinorbornene-functionalized derivatives were prepared via cycloaddition chemistry, and photoinitiated thiol–ene polymerization reactions were explored using commercially available tetra- and hexa-functional thiols, all using solvent-free syntheses. The thiol–ene reaction kinetics of different monomer compositions were characterized by real-time Fourier transform infrared (RT-FTIR) spectroscopy, with the norbornene functionalized derivatives exhibiting the highest reactivity towards thiol–ene photopolymerizations. The thermal and mechanical characteristics of the thermosets were analyzed and the viscoelastic behavior was investigated by dynamic mechanical analysis to understand the influence of the ester functionality and choice of crosslinker on the material properties. The anhydride backbone was found to be susceptible to controlled degradation under physiologically-(phosphate-buffered saline) and environmentally-relevant (artificial seawater) testing conditions over a period of 60 days at 50 °C. This work demonstrates that itaconic acid may be a useful feedstock in the generation of degradable polyanhydride networks via thiol–ene photopolymerization.more » « less
-
null (Ed.)Poly(ester-amide)s (PEAs) have been prepared from (glucose-derived) β-methyl-δ-valerolactone (MVL) by reaction of MVL-derived diamidodiols with diacid chlorides in solution to form poly(ester-amide)s having alternating diester-diamide subunits. The PEAs formed by this method exhibit plastic properties and are of sufficiently high molecular weight to be tough, ductile materials (stress at break: 41–53 MPa, strain at break: 530–640%). The length of the methylene linker unit ( n = 1,2,3) between amide groups of the diamidodiols affects the Young's modulus; longer linkers reduce the stiffness of the materials. This allows tuning of the properties by judicious choice of precursors. MVL was also converted to a diacid chloride that was then used to prepare a PEA that is 76 wt% MVL-derived. The degradation rates of suspensions of these new PEAs in basic aqueous media were benchmarked and their instability in aqueous acid was also observed. NMR studies were used to detect the hydrolytic degradation products of both these PEAs as well as a structurally simpler analog.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/c9py01082c