Title: Effect of Cellulose Reducing Ends on the Reinforcing Capacity of Powdered Cellulose in Polypropylene Composites
Powdered cellulose-reinforced (20 wt%) polypropylene composites were prepared by melt compounding and subsequent injection moldings. We assessed the effect of cellulose reducing ends on the capacity of powdered cellulose to reinforce polypropylene composites after seven days exposure to air circulation during the conditioning of samples. Tensile tests on the composites were performed at 5.08 mm/min. Fourier transform infrared spectroscopy revealed some changes that occurred within the composites by demonstrating a practical decrease in –C=O (1744 cm−1) absorption band intensity. A thermogravimetric analysis indicated differences within the thermal behavior of the prepared composites, showing a higher onset of degradation. Scanning electron microscopy of the fracture areas, together with load–extension curves, further characterized the development of interfacial cellulose/matrix adhesion as well as the brittle and ductile behavior of the composites. The results indicate that the thermal and tensile properties of powdered cellulose/polypropylene are improved by decreasing the amount of cellulose reducing ends in the system.  more » « less
Award ID(s):
1738669
NSF-PAR ID:
10174437
Author(s) / Creator(s):
; ;
Date Published:
Journal Name:
Journal of Composites Science
Volume:
3
Issue:
4
ISSN:
2504-477X
Page Range / eLocation ID:
98
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ( , Journal of materials science)
    null (Ed.)
    Fully biodegradable unidirectional green composites with excellent tensile properties were fabricated by combining one of the highest specific strength liquid crystalline cellulose (LCC) fibers as the reinforcement and microfibrillated cellulose (MFC) strengthened nonedible avocado seed starch (AVS)-based resin. MFC/AVS resin was crosslinked using 1,2,3,4-butane tetracarboxylic acid as well as plasticized using sorbitol or glycerol. Combination of alkali, mechanical and thermal treatments improved LCC fiber fracture stress from 1.5 GPa to over 1.9 GPa and Young’s modulus from 49 to 64 GPa. While the type and amount of plasticizer used changed the fracture strain of MFC/AVS resin, they also showed significant influence on the mechanical properties of the unidirectional composites. These composites prepared by hand lay-up, based on modified LCC fibers resulted in fracture stress of over 380 MPa and Young’s modulus of 19.5 GPa with less than 40% fiber content. Results suggest that there is scope to improve the properties further by using higher fiber content and automated manufacturing. These ‘green’ composites with excellent strength and stiffness may be used in many applications such as construction, automobile and others. 
    more » « less
  2. ; ( , Polymer Composites)

    Thermoplastic polyamide 6 composites reinforced with flax fiber fabric and kraft pulp cellulose mat were prepared by anionicin situring‐opening polymerization (ROP) using a special vacuum‐assisted resin infusion process. The effects of the polymerization initiator, fiber alkali pre‐treatment, fiber type, polymerization temperature, and surface modification of fibers with organosilane coupling agents on the ROP reaction, polymer conversion and the physical and mechanical properties of the composites were investigated. The results showed that a combination of alkali pre‐treatment and the use of relatively less reactive magnesium bromide based anionic initiator gave a successful ROP reaction and high polymer conversion. Analysis of the physical and mechanical properties of the composite panels showed that optimal mechanical properties could be achieved by using a polymerization temperature of 150°C while polymerization at higher temperatures lowered both the flexural and tensile properties due to generation of more internal microvoids, as well as, decreased crystallinity of the matrix. In addition, it was found that optimal mechanical properties of the composites could be obtained using 2 wt% aminopropyltriethoxysilane (APS) coupling agent while higher APS concentrations negatively impacted the interfacial adhesion, resulting in lower mechanical properties. POLYM. COMPOS., 40:1104–1116, 2019. © 2018 Society of Plastics Engineers

     
    more » « less
  3. ; ; ; ; ( , Energy Science & Engineering)
    Abstract

    The quantum of research in the area of supercapacitors is typically focused on the electrode materials. As such, there are many opportunities for the optimization of the other components, such as the separators, to further increase the power, efficiency, and longevity of supercapacitors. To contribute to this field of research, we present an innovative alternative for the fabrication of separators; using polymer/ceramic composites (PCC) based on polyvinylidene fluoride (PVDF) and polypropylene (PPG) mixed with different alkaline earth metal‐based titanates (eg barium, calcium, and strontium). ThePCCseparators were prepared via phase inversion precipitation technique, a feasible and scalable method for the fabrication of these composites. Different additives were used to modulate the porosity and thus, improve the charge transfer rates. Then, a heating process ensured a uniform organization of the composites. Furthermore, we tested the effect of thermally annealing the ceramics on the separators’ performance. The precursor materials and thePCC's were extensively characterized by means of X‐ray diffraction (XRD) and scanning electron microscopy (SEM). The electrochemical, mechanical, and dielectric properties of thePCC's were measured and compared to common commercial separators used today. Results suggest that thermal treatment improves tensile strength of the separators by at least ca. 60% without compromising the similar electrochemical profile to the commercial separators (44.52 ± 2.82 Ω vs 67.65 ± 29.01 Ω). Lastly, all of the fabricatedPCC's showed higher dielectric constants (4.52 in average for the as prepared separators and 2.99 for the heatedPCC's) than the polymer based commercial separators (2.2).

     
    more » « less
  4. ( , Materials)
    Herein, we report the production of ionic polymer-metal composites (IPMCs) hybridized with cellulose nanofibrils (CNF) as a partial substitute for Nafion®. The aim is not only to reduce the production cost and enhance respective mechanical/thermal properties but also to bestow a considerable degree of biodegradability to such products. Formulations with di erent CNF/Nafion® ratios were produced in a thin-film casting process. Crack-free films were air-dried and plated by platinum (Pt) through an oxidation-reduction reaction. The produced hybrids were analyzed in terms of thermal stability, mechanical and morphological aspects to examine their performance compared to the Nafion-based IPMC prior to plating process. Results indicated that films with higher CNF loadings had improved tensile strengths and elastic moduli but reduced ductility. Thermogravimetric analysis (TGA) showed that the incorporation of CNF to the matrix reduced its thermal stability almost linearly, however, the onset of decomposition point remained above 120 C, which was far above the temperature the composite membrane is expected to be exposed to. The addition of a cross-linking agent to the formulations helped with maintaining the integrity of the membranes during the plating process, thereby improving surface conductivity. The focus of the current study was on the physical and morphological properties of the films, and the presented data advocate the potential utilization of CNF as a nontoxic and sustainable bio-polymer for blending with perfluorosulfonic acid-based co-polymers, such as Nafion®, to be used in electroactive membranes. 
    more » « less
  5. ; ; ( , Journal of Applied Polymer Science)
    ABSTRACT

    Cellulose nanocrystal (CNCs)‐reinforced poly(lactic acid) (PLA) nanocomposites were prepared using twin screw extrusion followed by injection molding. Masterbatch approach was used to achieve more efficient dispersion of CNCs in PLA matrix. Modified CNCs (b‐CNCs) were prepared using benzoic acid as a nontoxic material through a green esterification method in a solvent‐free technique. Transmission electron microscopy images did not exhibit significant differences in the structure of b‐CNCs as compared with unmodified CNCs. However, a reduction of 6.6–15.5% in the aspect ratio of b‐CNCs was observed. The fracture surface of PLA‐b‐CNCs nanocomposites exhibited rough and irregular pattern which confirmed the need of more energy for fracture. Pristine CNCs showed a decrease in the thermal stability of nanocomposites, however, b‐CNCs nanocomposites exhibited higher thermal stability than pure PLA. The average storage modulus was improved by 38 and 48% by addition of CNCs and b‐CNCs in PLA, respectively. The incorporation of b‐CNCs increased Young's modulus, ultimate tensile stress, elongation at break, and impact strength by 27.02, 10.90, 4.20, and 32.77%, respectively, however, CNCs nanocomposites exhibited a slight decrease in ultimate strength and elongation at break. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci.2018,135, 46468.

     
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email