MXenes offer high metallic conductivity and redox capacitance that are attractive for high‐power, high‐energy storage devices. However, they operate limitedly under high anodic potentials due to irreversible oxidation. Pairing them with oxides to design asymmetric supercapacitors may expand the voltage window and increase the energy storage capabilities. Hydrated lithium preintercalated bilayered V2O5(
Free-standing bilayered vanadium oxide films synthesized by liquid exfoliation of chemically preintercalated δ-Li x V 2 O 5 · n H 2 O
A free-standing film composed of bilayered vanadium oxide nanoflakes is for the first time synthesized using a new low-energy process. The precursor powder, δ-Li x V 2 O 5 · n H 2 O, was prepared using a simple sol–gel based chemical preintercalation synthesis procedure. δ-Li x V 2 O 5 · n H 2 O was dispersed and probe sonicated in N -methyl pyrrolidone to exfoliate the bilayers followed by vacuum filtration resulting in the formation of a free-standing film with obsidian color. X-ray diffraction showed lamellar ordering of a single-phase material with a decreased interlayer distance compared to that of the precursor powder. Scanning electron microscopy images demonstrated stacking of the individual nanoflakes. This morphology was further confirmed with scanning transmission electron microscopy that showed highly malleable nanoflakes consisting of ∼10–100 vanadium oxide bilayers. One of the most important consequences of this morphological rearrangement is that the electronic conductivity of the free-standing film, measured by the four-probe method, increased by an order of magnitude compared to conductivity of the pressed pellet made of precursor powder. X-ray photoelectron spectroscopy measurements showed the coexistence of both V 5+ and V 4+ oxidation states in the exfoliated sample, possibly contributing to the change in electronic conductivity. The developed approach provides the ability to maintain the phase purity and crystallographic order during the exfoliation process, coupled with the formation of a free-standing film of enhanced conductivity. The produced bilayered vanadium oxide nanoflakes can be used as the building blocks for the synthesis of versatile two-dimensional heterostructures to create innovative electrodes for electrochemical energy storage applications.
more »
« less
- Award ID(s):
- 1752623
- NSF-PAR ID:
- 10223692
- Date Published:
- Journal Name:
- Materials Advances
- Volume:
- 2
- Issue:
- 8
- ISSN:
- 2633-5409
- Page Range / eLocation ID:
- 2711 to 2718
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract δ ‐Lix V2O5·n H2O) is attractive for aqueous energy storage due to its high Li capacity at high potentials; however, its poor cyclability remains a challenge. To overcome its limitations and achieve a wide voltage window and excellent cyclability, it is combined with V2C and Nb4C3MXenes. Asymmetric supercapacitors employing lithium intercalated V2C (Li‐V2C) or tetramethylammonium intercalated Nb4C3(TMA‐Nb4C3) MXenes as the negative electrode, and aδ ‐Lix V2O5·n H2O composite with carbon nanotubes as the positive electrode in 5m LiCl electrolyte operate over wide voltage windows of 2 and 1.6 V, respectively. The latter shows remarkably high cyclability—capacitance retention of ≈95% after 10 000 cycles. This work highlights the importance of selecting appropriate MXenes to achieve a wide voltage window and a long cycle life in combination with oxide anodes to demonstrate the potential of MXenes beyond Ti3C2in energy storage. -
Metastable materials that represent excursions from thermodynamic minima are characterized by distinctive structural motifs and electronic structure, which frequently underpins new function. The binary oxides of hafnium present a rich diversity of crystal structures and are of considerable technological importance given their high dielectric constants, refractory characteristics, radiation hardness, and anion conductivity; however, high-symmetry tetragonal and cubic polymorphs of HfO 2 are accessible only at substantially elevated temperatures (1720 and 2600 °C, respectively). Here, we demonstrate that the core–shell arrangement of VO 2 and amorphous HfO 2 promotes outwards oxygen diffusion along an electropositivity gradient and yields an epitaxially matched V 2 O 3 /HfO 2 interface that allows for the unprecedented stabilization of the metastable cubic polymorph of HfO 2 under ambient conditions. Free-standing cubic HfO 2 , otherwise accessible only above 2600 °C, is stabilized by acid etching of the vanadium oxide core. In contrast, interdiffusion under oxidative conditions yields the negative thermal expansion material HfV 2 O 7 . Variable temperature powder X-ray diffraction demonstrate that the prepared HfV 2 O 7 exhibits pronounced negative thermal expansion in the temperature range between 150 and 700 °C. The results demonstrate the potential of using epitaxial crystallographic relationships to facilitate preferential nucleation of otherwise inaccessible metastable compounds.more » « less
-
Copper oxide nanostructures are widely used for various applications due to their unique optical and electrical properties. In this work, we demonstrate an atmospheric laser-induced oxidation technique for the fabrication of highly electrochemically active copper oxide hierarchical micro/nano structures on copper surfaces to achieve highly sensitive non-enzymatic glucose sensing performance. The effect of laser processing power on the composition, crystallinity, microstructure, wettability, and color of the laser-induced oxide on copper (LIO-Cu) surface was systematically studied using scanning electron microscopy (SEM), grazing incidence X-ray diffraction (GI-XRD), Raman spectroscopy, energy dispersive X-ray spectroscopy (EDX), EDX-mapping, water contact angle measurements, and optical microscopy. Results of these investigations showed a remarkable increase in copper oxide composition by increasing the laser processing power. The pore size distribution and surface area of the pristine and LIO-Cu sample estimated by N 2 adsorption–desorption data showed a developed mesoporous LIO-Cu structure. The size of the generated nano-oxides, crystallinity, and electroactivity of the LIO-Cu were observed to be adjustable by the laser processing power. The electrocatalytic activity of LIO-Cu surfaces was studied by means of cyclic voltammetry (CV) within a potential window of −0.8 to +0.8 V and chronoamperometry in an applied optimized potential of +0.6 V, in 0.1 M NaOH solution and phosphate buffer solution (PBS), respectively. LIO-Cu surfaces with optimized laser processing powers exhibited a sensitivity of 6950 μA mM −1 cm −2 within a wide linear range from 0.01 to 5 mM, with exceptional specificity and response time (<3 seconds). The sensors also showed excellent response stability over a course of 50 days that was originated from the binder-free robust electroactive film fabricated directly onto the copper surface. The demonstrated one-step LIO processing onto commercial metal films, can potentially be applied for tuneable and scalable roll-to-roll fabrication of a wide range of high surface area metal oxide micro/nano structures for non-enzymatic biosensing and electrochemical applications.more » « less
-
more » « less
Abstract Initially, vanadium dioxide seems to be an ideal first-order phase transition case study due to its deceptively simple structure and composition, but upon closer inspection there are nuances to the driving mechanism of the metal-insulator transition (MIT) that are still unexplained. In this study, a local structure analysis across a bulk powder tungsten-substitution series is utilized to tease out the nuances of this first-order phase transition. A comparison of the average structure to the local structure using synchrotron x-ray diffraction and total scattering pair-distribution function methods, respectively, is discussed as well as comparison to bright field transmission electron microscopy imaging through a similar temperature-series as the local structure characterization. Extended x-ray absorption fine structure fitting of thin film data across the substitution-series is also presented and compared to bulk. Machine learning technique, non-negative matrix factorization, is applied to analyze the total scattering data. The bulk MIT is probed through magnetic susceptibility as well as differential scanning calorimetry. The findings indicate the local transition temperature (
$$T_c$$ $$T_c$$ $$_2\, \rightarrow$$ $$_6$$ $$_{13} \, \rightarrow$$ $$_2$$ $$_5$$ -
Here, we demonstrate a two-step electrosynthesis approach for the preparation of silver pyrovanadate, Ag 4 V 2 O 7 in thin-film form. In the first, cathodic step, polycrystalline Ag was deposited on fluorine doped tin oxide (FTO) substrate from a non-aqueous bath. Aqueous pyrovanadate species were then generated by aging of a CO 2 -infused sodium orthovanadate (Na 3 VO 4 ) solution for three weeks. Silver ions were subsequently generated in situ in this medium using anodic stripping of the Ag/ITO films from the first step. Interfacial precipitation of the Ag + ions with the pyrovanadate species afforded the targeted product in phase pure form. The various stages of the electrosynthesis were monitored in situ via the combined use of voltammetry, electrochemical quartz crystal nanogravimetry (EQCN), and coulometry. The Ag 4 V 2 O 7 thin films were characterized by a variety of experimental techniques, including X-ray diffraction, laser Raman spectroscopy, diffuse reflectance spectroscopy, scanning electron microscopy, and high-resolution transmission electron microscopy. Surface photovoltage spectroscopy, ambient-pressure photoemission spectroscopy, and Kelvin probe contact potential difference (work function) measurements afforded information on the energy band structure of the p -type Ag 4 V 2 O 7 semiconductor. Finally, the electrochemical and photoelectrochemical properties of the electrosynthesized Ag 4 V 2 O 7 thin films were studied in both aqueous and non-aqueous electrolytes.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/D1MA00085C