One of the most significant drawbacks of metal oxide (MOS) based chemiresistive gas sensors is the requirement of high operating temperature (250–450 °C), which results in significant power consumption and shorter lifetime. To develop room temperature (21±2 °C) MOS chemiresistive gas sensors, the sensing performance of different MOS nanostructures (i.e., tin (IV) oxide (SnO2) nanoparticles (NPs), indium (III) oxide (In2O3) NPs, zinc oxide (ZnO) NPs, tungsten trioxide (WO3) NPs, copper oxide (CuO) nanotubes (NTs), and indium tin oxide (In90Sn10O3 (ITO)) NPs) were systematically investigated toward different toxic industrial chemicals (TICs) (i.e., nitrogen dioxide (NO2), ammonia (NH3), hydrogen sulfide (H2S), carbon monoxide (CO), sulfur dioxide (SO2) and volatile organic compounds (VOCs) (i.e., acetone (C3H6O), toluene (C6H5CH3), ethylbenzene (C6H5CH2CH3), and p-xylene (C6H4(CH3)2)) in the presence and absence of 400 nm UV light illumination. Sensing performance enhancement through photoexcitation is strongly dependent on the target analytes. Under 400 nm UV photoexcitation at 76.0 mW/cm2 intensity, room temperature (21±2 °C) NO2 sensing was readily achieved where SnO2 NPs exhibited the highest sensor response (S = 474.4 toward 10 ppmm (parts per million by mass)) with good recovery followed by ZnO NPs > In2O3 NPs > ITO NPs. Meanwhile, indirect bandgap n-type WO3 NPs showed limited NO2 sensing performance under illumination, whereas p-type CuO NTs showed relatively good sensing response. The most significant improvements in SnO2 compared to other MOS nanoparticles might be attributed to the highest number of photogeneration electrons, which rapidly reacted with adsorbed species to enhance the reaction kinetics. WO3 NPs showed a unique sensing response toward aromatic compounds (e.g., ethylbenzene and p-xylene) under UV illumination, where maximum sensitivity was achieved under 36 mW/cm2 irradiation. Changing light intensity from 0.0 to 36.4 mW/cm2, WO3 showed 15.4-fold and 6.3-fold enhancement in sensing response toward 25 ppmm ethylbenzene and 100 ppmm p-xylene, respectively. 400 nm optical excitation has a limited effect on the sensing performance toward CO, SO2, toluene, and acetone.
more »
« less
Effect of (100) and (001) Hexagonal WO3 Faceting on Isoprene and Acetone Gas Selectivity
The hexagonal WO3 polymorph, h-WO3, has attracted attention due to its interatomic channels, allowing for a greater degree of intercalation compared to other WO3 polymorphs. Our research group has previously demonstrated h-WO3 to be a highly sensitive gas sensing material for a flu biomarker, isoprene. In this work, the gas sensing performance of this polymorph has been further investigated in two distinct configurations of the material produced by different processing routes. The first sample was synthesized using Na2WO4·2H2O and showed (100) faceting. The second sample was synthesized using WCl6 and showed (001) faceting. The gas sensing response of the nanostructured films deposited using the (100) textured h-WO3 sample 1 had a higher response to acetone at 350 °C. The (001) textured h-WO3 sample 2 favored isoprene at 350 °C. The selectivity of the latter to isoprene is explained in terms of the dangling bonds present on the (001) facets. The tungsten and oxygen dangling bonds present on the (001) plane favor the adsorption of the isoprene molecule over that of the acetone molecule due to the oxygen containing dipole present in the acetone molecule.
more »
« less
- Award ID(s):
- 2029847
- PAR ID:
- 10233960
- Date Published:
- Journal Name:
- Sensors
- Volume:
- 21
- Issue:
- 5
- ISSN:
- 1424-8220
- Page Range / eLocation ID:
- 1690
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
In an attempt to grow 8-hydroxyquinoline–acetaminophen co-crystals from equimolar amounts of conformers in a chloroform–ethanol solvent mixture at room temperature, the title compound, C 9 H 7 NO, was obtained. The molecule is planar, with the hydroxy H atom forming an intramolecular O—H...N hydrogen bond. In the crystal, molecules form centrosymmetric dimers via two O—H...N hydrogen bonds. Thus, the hydroxy H atoms are involved in bifurcated O—H...N hydrogen bonds, leading to the formation of a central planar four-membered N 2 H 2 ring. The dimers are bound by intermolecular π–π stacking [the shortest C...C distance is 3.2997 (17) Å] and C—H...π interactions into a three-dimensional framework. The crystal grown represents a new monoclinic polymorph in the space group P 2 1 / n . The molecular structure of the present monoclinic polymorph is very similar to that of the orthorhombic polymorph (space group Fdd 2) studied previously [Roychowdhury et al. (1978). Acta Cryst. B 34 , 1047–1048; Banerjee & Saha (1986). Acta Cryst. C 42 , 1408–1411]. The structures of the two polymorphs are distinguished by the different geometries of the hydrogen-bonded dimers, which in the crystal of the orthorhombic polymorph possess twofold axis symmetry, with the central N 2 H 2 ring adopting a butterfly conformation.more » « less
-
The rates of diabetes throughout the world are rising rapidly, impacting nearly every country. New research is focused on better ways to monitor and treat this disease. Breath acetone levels have been defined as a biomarker for diabetes. The development of a method to monitor and diagnose diabetes utilizing breath acetone levels would provide a fast, easy, and non-invasive treatment option. An ideal material for point-of-care diabetes management would need to have a high response to acetone, high acetone selectivity, low interference from humidity, and be able to operate at room temperature. Chemiresistive gas sensors are a promising method for sensing breath acetone due to their simple fabrication and easy operation. Certain semiconductor materials in chemiresistive sensors can react to acetone in the air and produce changes in resistance that can be correlated with acetone levels. While these materials have been developed and show strong responses to acetone with good selectivity, most of them must operate at high temperatures (compared to RT), causing high power consumption, unstable device operation, and complex device design. In this paper, we systematically studied a series of 2-dimensional MXene-based nanocomposites as the sensing materials in chemiresistive sensors to detect 2.86 ppm of acetone at room temperature. Most of them showed great sensitivity and selectivity for acetone. In particular, the 1D/2D CrWO/Ti3C2 nanocomposite showed the best sensing response to acetone: nine times higher sensitivity than 1D KWO nanowires. To determine the sensing selectivity, a CrWO/Ti3C2 nanocomposite-based sensor was exposed to various common vapors in human breath. The result revealed that it has excellent selectivity for acetone, and far lower responses to other vapors. All these preliminary results indicate that this material is a promising candidate for the creation of a point-of-care diabetes management device.more » « less
-
In this report, CeO 2 and SiO 2 supported 1 wt% Ru catalysts were synthesized and studied for dry reforming of methane (DRM) by introducing non-thermal plasma (NTP) in a dielectric barrier discharge (DBD) fixed bed reactor. From quadrupole mass spectrometer (QMS) data, it is found that introducing non-thermal plasma in thermo-catalytic DRM promotes higher CH 4 and CO 2 conversion and syngas (CO + H 2 ) yield than those under thermal catalysis only conditions. According to the H 2 -TPR, CO 2 -TPD, and CO-TPD profiles, reducible CeO 2 supported Ru catalysts presented better activity compared to their irreducible SiO 2 supported Ru counterparts. For instance, the molar concentrations of CO and H 2 were 16% and 9%, respectively, for plasma-assisted thermo-catalytic DRM at 350 °C, while no apparent conversion was observed at the same temperature for thermo-catalytic DRM. Highly energetic electrons, ions, and radicals under non-equilibrium and non-thermal plasma conditions are considered to contribute to the activation of strong C–H bonds in CH 4 and C–O bonds in CO 2 , which significantly improves the CH 4 /CO 2 conversion during DRM reaction at low temperatures. At 450 °C, the 1 wt% Ru/CeO 2 nanorods sample showed the highest catalytic activity with 51% CH 4 and 37% CO 2 conversion compared to 1 wt% Ru/CeO 2 nanocubes (40% CH 4 and 30% CO 2 ). These results clearly indicate that the support shape and reducibility affect the plasma-assisted DRM reaction. This enhanced DRM activity is ascribed to the surface chemistry and defect structures of the CeO 2 nanorods support that can provide active surface facets, higher amounts of mobile oxygen and oxygen vacancy, and other surface defects.more » « less
-
Abstract Crystallographically anisotropic two-dimensional (2D) molybdenum disulfide (MoS 2 ) with vertically aligned (VA) layers is attractive for electrochemical sensing owing to its surface-enriched dangling bonds coupled with extremely large mechanical deformability. In this study, we explored VA-2D MoS 2 layers integrated on cellulose nanofibers (CNFs) for detecting various volatile organic compound gases. Sensor devices employing VA-2D MoS 2 /CNFs exhibited excellent sensitivities for the tested gases of ethanol, methanol, ammonia, and acetone; e.g. a high response rate up to 83.39% for 100 ppm ethanol, significantly outperforming previously reported sensors employing horizontally aligned 2D MoS 2 layers. Furthermore, VA-2D MoS 2 /CNFs were identified to be completely dissolvable in buffer solutions such as phosphate-buffered saline solution and baking soda buffer solution without releasing toxic chemicals. This unusual combination of high sensitivity and excellent biodegradability inherent to VA-2D MoS 2 /CNFs offers unprecedented opportunities for exploring mechanically reconfigurable sensor technologies with bio-compatible transient characteristics.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.3390/s21051690