  • Lithium-activated SnS–graphene alternating nanolayers enable dendrite-free cycling of thin sodium metal anodes in carbonate electrolyte
Title: Lithium-activated SnS–graphene alternating nanolayers enable dendrite-free cycling of thin sodium metal anodes in carbonate electrolyte
Sodium metal battery (SMB, NMB) anodes can become dendritic due to an electrochemically unstable native Na-based solid electrolyte interphase (SEI). Herein Li-ion activated tin sulfide graphene nanocomposite membrane (A-SnS–G) is employed as an artificial SEI layer, allowing cyclability of record-thin 100 μm Na metal foils. The thin Na metal is prepared by a self-designed metallurgical rolling protocol. A-SnS–G is initially placed onto the polypropylene (PP) separator but becomes in situ transferred onto the Na metal surface. Symmetric metal cells protected by A-SnS–G achieve low-overpotential extended high-rate cycling in a standard carbonate electrolyte (EC : DEC = 1 : 1, 5% FEC). Accumulated capacity of 1000 mA h cm −2 is obtained after 500 cycles at 4 mA cm −2 , with accumulated capacity-to-foil capacity (A/F) ratio of 90.9. This is among the most favorable cycle life, accumulated capacity, and anode utilization combinations reported. Protection by non-activated SnS–G membrane yields significantly worse cycling, albeit still superior to the baseline unprotected sodium. Post-mortem and dedicated light optical analysis indicate that metal swelling, dendrite growth and dead metal formation is extensive for the unprotected sample, but is suppressed with A-SnS–G. Per XPS, post-100 cycles near-surface structure of A-SnS–G is rich in metallic Sn alloys and inorganic carbonate salts. Even after 300 cycles, Li-based SEI components ROCO 2 -Li, Li 2 CO 3 and LiF are detected with A-SnS–G. As a proof of principle, an SMB with a high mass loading (6 mg cm −2 ) NVP cathode and a A-SnS–G protected anode delivered extended cyclability, achieving 74 mA h g −1 after 400 cycles at 0.4C.  more » « less
Award ID(s):
1938833
NSF-PAR ID:
10233963
Author(s) / Creator(s):
; ; ; ; ; ; ;
Date Published:
Journal Name:
Energy & Environmental Science
Volume:
14
Issue:
1
ISSN:
1754-5692
Page Range / eLocation ID:
382 to 395
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ( , Advanced Energy Materials)
    Abstract

    The interrelation is explored between external pressure (0.1, 1, and 10 MPa), solid electrolyte interphase (SEI) structure/morphology, and lithium metal plating/stripping behavior. To simulate anode‐free lithium metal batteries (AF‐LMBs) analysis is performed on “empty” Cu current collectors in standard carbonate electrolyte. Lower pressure promotes organic‐rich SEI and macroscopically heterogeneous, filament‐like Li electrodeposits interspersed with pores. Higher pressure promotes inorganic F‐rich SEI with more uniform and denser Li film. A “seeding layer” of lithiated pristine graphene (pG@Cu) favors an anion‐derived F‐rich SEI and promotes uniform metal electrodeposition, enabling extended electrochemical stability at a lower pressure. State‐of‐the‐art electrochemical performance is achieved at 1MPa: pG‐enabled half‐cell is stable after 300 h (50 cycles) at 1 mA cm−2rate −3 mAh cm−2capacity (17.5 µm plated/stripped), with cycling Coulombic efficiency (CE) of 99.8%. AF‐LMB cells with high mass loading NMC622 cathode (21 mg cm−2) undergo 200 cycles with a CE of 99.4% at C/5‐charge and C/2‐discharge (1C = 178 mAh g−1). Density functional theory (DFT) highlights the differences in the adsorption energy of solvated‐Li+onto various crystal planes of Cu (100), (110), and (111), versus lithiated/delithiated (0001) graphene, giving insight regarding the role of support surface energetics in promoting SEI heterogeneity.

     
    more » « less
  2. ; ; ; ; ( , Chemical engineering journal)
    Suffering from critical instability of lithium (Li) anode, the most commercial electrolytes, carbonate-ester electrolytes, have been restrictedly used in high-energy Li metal batteries (LMBs) despite of their broad implementation in lithium-ion batteries. Here, abundant, natural corn protein, zein, is exploited as a novel additive to stabilize Li anode and effectively prolong the cycling life of LMBs based on carbonate-ester electrolyte. It is discovered that the denatured zein is involved in the formation of solid electrolyte interphase (SEI), guides Li+ deposition and repairs the cracked SEI. In specific, the zein-rich SEI benefits the anion immobilization, enabling uniform Li+ deposition to diminish dendrite growth; the preferential zein-Li reaction effectively repairs the cracked SEI, protecting Li from parasite reactions. The resulting symmetrical Li cell exhibits a prolonged cycling life to over 350 h from <200 h for pristine cell at 1 mA cm􀀀 2 with a capacity of 1 mAh cm^ 2. Paired with LiFePO4 cathode, zein additive markedly improves the electrochemical performance including a higher capacity of 130.1 mAh g^ 1 and a higher capacity retention of ~ 80 % after 200 cycles at 1 C. This study demonstrates a natural protein to be an effective additive for the most commercial electrolytes for advancing performance of LMBs. 
    more » « less
  3. ; ; ; ; ; ; ; ; ( , Advanced Materials)
    Abstract

    Repeated cold rolling and folding is employed to fabricate a metallurgical composite of sodium–antimony–telluride Na2(Sb2/6Te3/6Vac1/6) dispersed in electrochemically active sodium metal, termed “NST‐Na.” This new intermetallic has a vacancy‐rich thermodynamically stable face‐centered‐cubic structure and enables state‐of‐the‐art electrochemical performance in widely employed carbonate and ether electrolytes. NST‐Na achieves 100% depth‐of‐discharge (DOD) in 1mNaPF6in G2, with 15 mAh cm−2at 1 mA cm−2and Coulombic efficiency (CE) of 99.4%, for 1000 h of plating/stripping. Sodium‐metal batteries (SMBs) with NST‐Na and Na3V2(PO4)3 (NVP) or sulfur cathodes give significantly improved energy, cycling, and CE (>99%). An anode‐free battery with NST collector and NVP obtains 0.23% capacity decay per cycle. Imaging and tomography using conventional and cryogenic microscopy (Cryo‐EM) indicate that the sodium metal fills the open space inside the self‐supporting sodiophilic NST skeleton, resulting in dense (pore‐free and solid electrolyte interphase (SEI)‐free) metal deposits with flat surfaces. The baseline Na deposit consists of filament‐like dendrites and “dead metal”, intermixed with pores and SEI. Density functional theory calculations show that the uniqueness of NST lies in the thermodynamic stability of the Na atoms (rather than clusters) on its surface that leads to planar wetting, and in its own stability that prevents decomposition during cycling.

     
    more » « less
  4. ; ; ; ( , Angewandte Chemie International Edition)
    Abstract

    Solid polymer electrolytes based on plastic crystals are promising for solid‐state sodium metal (Na0) batteries, yet their practicality has been hindered by the notorious Na0‐electrolyte interface instability issue, the underlying cause of which remains poorly understood. Here, by leveraging a model plasticized polymer electrolyte based on conventional succinonitrile plastic crystals, we uncover its failure origin in Na0batteries is associated with the formation of a thick and non‐uniform solid electrolyte interphase (SEI) and whiskery Na0nucleation/growth. Furthermore, we design a new additive‐embedded plasticized polymer electrolyte to manipulate the Na0deposition and SEI formulation. For the first time, we demonstrate that introducing fluoroethylene carbonate (FEC) additive into the succinonitrile‐plasticized polymer electrolyte can effectively protect Na0against interfacial corrosion by facilitating the growth of dome‐like Na0with thin, amorphous, and fluorine‐rich SEIs, thus enabling significantly improved performances of Na//Na symmetric cells (1,800 h at 0.5 mA cm−2) and Na//Na3V2(PO4)3full cells (93.0 % capacity retention after 1,200 cycles at 1 C rate in coin cells and 93.1 % capacity retention after 250 cycles at C/3 in pouch cells at room temperature). Our work provides valuable insights into the interfacial failure of plasticized polymer electrolytes and offers a promising solution to resolving the interfacial instability issue.

     
    more » « less
  5. ; ; ; ( , Angewandte Chemie)
    Abstract

    Solid polymer electrolytes based on plastic crystals are promising for solid‐state sodium metal (Na0) batteries, yet their practicality has been hindered by the notorious Na0‐electrolyte interface instability issue, the underlying cause of which remains poorly understood. Here, by leveraging a model plasticized polymer electrolyte based on conventional succinonitrile plastic crystals, we uncover its failure origin in Na0batteries is associated with the formation of a thick and non‐uniform solid electrolyte interphase (SEI) and whiskery Na0nucleation/growth. Furthermore, we design a new additive‐embedded plasticized polymer electrolyte to manipulate the Na0deposition and SEI formulation. For the first time, we demonstrate that introducing fluoroethylene carbonate (FEC) additive into the succinonitrile‐plasticized polymer electrolyte can effectively protect Na0against interfacial corrosion by facilitating the growth of dome‐like Na0with thin, amorphous, and fluorine‐rich SEIs, thus enabling significantly improved performances of Na//Na symmetric cells (1,800 h at 0.5 mA cm−2) and Na//Na3V2(PO4)3full cells (93.0 % capacity retention after 1,200 cycles at 1 C rate in coin cells and 93.1 % capacity retention after 250 cycles at C/3 in pouch cells at room temperature). Our work provides valuable insights into the interfacial failure of plasticized polymer electrolytes and offers a promising solution to resolving the interfacial instability issue.

     
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email