Title: Effect of Pick Spacing and Warp and Weft Volume Fraction on Intrinsic Residual Stresses in 3D Woven Composites
Three panels of 3D woven carbon fiber/RTM6 epoxy composites with a ply-to-ply weave with 12x12 (warp/weft) picks per inch (ppi), 10x12 ppi, and 10x8 ppi were fabricated by resin transfer molding. Realistic finite element models of each weave architecture were constructed using Dynamic Fabric Mechanics Analyzer. The resin properties were isotropic and linear elastic and dependent on temperature. The resin-infiltrated fiber tow properties were estimated using homogenization based on Hashin and Shapery formulas. The model was considered to be at zero stress at the 165C curing temperature. The stresses resulting from cooling the composite to 25C were estimated using the resin temperature-dependent properties and the temperature independent properties of the tows. The displacement fields resulting from holes drilled through the middle of the top warp or weft yarn were estimated by virtually drilling a hole in the finite element model and were measured on the specimens using electronic speckle pattern interferometry. In general, the measured displacements transverse to the yarn were lower than the predicted displacements. This suggests the resin in the infiltrated yarns relieves some of the stress by permanently deforming during cooling. The measured displacements along the yarn were approximately the same for the 12x12 ppi,, lower for the 10x12 ppi, and significantly higher for the 10x8 ppi.  more » « less
Award ID(s):
1662098
NSF-PAR ID:
10300601
Author(s) / Creator(s):
; ; ; ;
Date Published:
Journal Name:
Proceedings of the 34th ASC Technical Conference
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Intrinsic residual stresses in woven composites result from the coefficient of thermal expansion mismatch between the fibers and the matrix. Extrinsic residual stresses result from large scale thermal gradients during curing and cooling. Intrinsic residual stresses in 3D woven composites are sometimes severe enough to cause micro-cracking in the matrix. They are also expected to impact the fatigue resistance and the impact resistance. To the best of our knowledge, there have been no spatially resolved measurements of the intrinsic residual stress field as a function of position in the repeating weave pattern. We used digital image correlation (DIC) and electronic speckle pattern interferometry (ESPI) to measure the surface displacement field resulting from drilling a 1 mm diameter hole at four selected locations in two different 3D woven composite architectures that represent low and high through-the-thickness constraint. The two methods are used because the displacements sometimes on the lower end of the resolution for the DIC method and the displacement gradients are sometimes too steep to resolve the fringes for the ESPI method. Finite element models constructed with realistic fiber geometry using Dynamic Fabric Mechanic Analyzer software were utilized to estimate the residual stress field from cooling from the curing temperature. Holes were manually inserted by deactivating the elements in the hole region and the resultant displacement fields were compared to the measurements. In general, the measured displacement fields were lower in magnitude than the model predictions. In some cases, the sign of the predicted displacement field is opposite to the observed field which could be attributed to differences between the actual hole location and the hole in the model. 
    more » « less
  2. Transparent wood composites (TWCs) are a new class of light-transmitting wood-based materials composed of a delignified wood template that is infiltrated with a refractive- index-matched polymer resin. Recent research has focused primarily on the fabrication and characterization of single-ply TWCs. However, multi-ply composite laminates are of interest due to the mechanical advantages they impart compared to the single ply. In this work, 1- and 2-ply [0°/90°] TWC laminates were fabricated using a delignified wood template (C) and an acetylated delignified wood template (AC). The optical and mechanical properties of resultant C and AC TWC laminates were determined using ultraviolet-visible spectroscopy (UV-Vis) and tensile testing (5× replicates), respectively. In addition, the ability of classical lamination plate theory and simple rule of mixtures to predict multi-ply tensile modulus and strength, respectively, from ply-level mechanical properties were investigated and are reported herein. Experimental results highlight tradeoffs that exist between the mechanical and optical responses of both unmodified and chemically modified TWCs. Template acetylation reduced the stiffness and strength in the 0° fiber direction by 2.4 GPa and 58.9 MPa, respectively, compared to the unmodified samples. At high wavelengths of light (>515 nm), AC samples exhibited higher transmittance than the C samples. Above 687 nm, the 2-ply AC sample exhibited a higher transmittance than the 1-ply C sample, indicating that thickness-dependent optical constraints can be overcome with improved interfacial interactions. Finally, both predictive models were successful in predicting the elastic modulus and tensile strength response for the 2-ply C and AC samples. 
    more » « less
  3. null (Ed.)
    3D woven carbon/epoxy composites are often produced using resin transfer molding technique which includes epoxy curing at elevated temperatures. The process may lead to accumulation of the intrinsic residual stresses during cooling of the material caused by the mismatch between carbon and epoxy coefficients of thermal expansion. This paper deals with implementation of mesoscale finite element models to evaluate intrinsic residual stresses in 3D woven composites. The stresses are determined by correlation of the surface displacements observed after drilling 1-mm diameter blind holes with the corresponding predictions of the models. We investigated how a numerical representation of the composite plate surface affects the correlation between the experimental measurements and numerical predictions and how it influences the evaluation of the process-induced residual stresses. It has been shown for ply-to-ply woven composites with different pick spacing that the absence of the resin layer leads to more accurate interpretation of the experimental measurements. The prediction of the average residual stress in the matrix phase of the composite was found to be sensitive to the surface representation accuracy, however, the residual stress magnitude and distribution was not affected fundamentally. 
    more » « less
  4. null (Ed.)
    3D woven composites are well known for their high strength, dimensional stability, delamination, and impact resistance. They are often used in aerospace, energy, and automotive industries where material parts can experience harsh service conditions including substantial variations in temperature. This may lead to significant thermal deformations and thermally-induced stresses in the material. Additionally, 3D woven composites are often produced using resin transfer molding (RTM) technique which involves curing the epoxy resin at elevated temperatures leading to accumulation of the processing-induced residual stress. Thus, understanding of effective thermal behavior of 3D woven composites is essential for their successful design and service. In this paper, the effective thermal properties of 3D woven carbon-epoxy composite materials are estimated using mesoscale finite element models previously developed for evaluation of the manufacturing-induced residual stresses. We determine effective coefficients of thermal expansion (CTEs) of the composites in terms of the known thermal and mechanical properties of epoxy resin and carbon fibers. We investigate how temperature sensitivity of the thermal and mechanical properties of the epoxy influences the overall thermal properties of the composite. The simulations are performed for different composite reinforcement morphologies including ply-to-ply and orthogonal. It is shown that even linear dependence of epoxy’s stiffness and CTE on temperature results in a nonlinear dependence on temperature of the overall composite’s CTE. 
    more » « less
  5. Due to the incapability of one-dimensional (1D) and two-dimensional (2D) models in simulating the frontal polymerization (FP) process in laminated composites with multiple fiber angles (e.g., cross-ply, angle-ply), modeling a three-dimensional (3D) domain, which is more representative of practical applications, provides critical guidance in the control and optimization of the FP process. In this paper, subroutines are developed to achieve the 3D modeling of FP in unidirectional and cross-ply carbon fiber laminates with finite element analysis, which are validated against the experimental data. The 3D model is employed to study the effect of triggering direction in relevance to the fiber direction on the FP process, which cannot be studied using traditional 1D/2D models. Our findings suggest that triggering in the fiber direction leads to a higher front velocity, in comparison to cases where front was triggered in the direction perpendicular to the fiber. Moreover, the average front velocity in cross-ply laminates is on average 20~25% lower than that in unidirectional laminates. When triggered using two opposite fronts in the in-plane direction, the maximum temperature of the thermal spike in the cross-ply laminate, when two fronts merge, is about 100 °C lower than that in the unidirectional laminate. In cross-ply laminates, a sloped pattern forms across the thickness direction as the front propagates in the in-plane direction, as opposed to the traditionally observed uniform propagation pattern in unidirectional cases. Furthermore, the effect of thermal conductivity is studied using two additional composite laminates with glass (1.14 W/m·K) and Kevlar fibers (0.04 W/m·K). It is shown that the frontal velocity, degree of cure, and the thermal spike temperature decrease as the thermal conductivity reduces. 
    more » « less