A novel processing method that creates and preserves ceramic nanoparticles in solid oxide electrodes during co-sintering at traditional sintering temperatures is introduced. Specifically, carbon templated samarium-doped ceria nanoparticles (nSDC) were successfully integrated with commercial lanthanum strontium cobalt ferrite (LSCF) and commercial SDC powders, producing LSCF-SDC-nSDC cathodes upon processing. The effect of nSDC concentration on cathode electrocatalytic activity was investigated at low operational temperatures, 600 °C–700 °C, with symmetrical cells. Low nSDC loadings, ≤5 wt% nSDC, significantly decreased cell polarization resistance whereas higher loadings increased it. The best electrochemical performance was achieved with 5 wt% nSDC, lowering the polarization resistance by 41% at 600 °C. Fuel cell tests demonstrate that adding 5 wt% nSDC increased the maximum fuel cell power density by 38%. Electrochemical impedance spectra showed substantial improvements in both fuel cell polarization resistance and ohmic resistance, indicating that nSDC increased the electrocatalytically active area of the cathode. This work demonstrates a simple, novel method for effectively increasing electrocatalytic activity of solid oxide electrodes at low operational temperatures.
more »
« less
Lowering the Impedance of Lanthanum Strontium Manganite-Based Electrodes with Lanthanum Oxychloride and Lanthanum Scavenging Chloride Salts
The impact of infiltrating chloride salts on the electrochemical behavior of lanthanum strontium manganite-yttria stabilized zirconia (LSM-YSZ) cathodes was investigated under solid oxide fuel cell operation. Infiltrating a lanthanum chloride solution resulted in the formation of a lanthanum oxychloride (LaOCl) phase. A LaOCl phase also formed by infiltrating an ammonium chloride solution; however, lanthanum was scavenged from the LSM phase to form LaOCl. The third infiltrating solution, a combination of zirconium chloride and yttrium nitrate, formed LaOCl by scavenging lanthanum from LSM and produced YSZ nanoparticles. Electrochemical impedance spectroscopy results suggest that LaOCl improves oxygen adsorption kinetics compared to a baseline LSM-YSZ cathode, reducing the low frequency impedance by 30%. In addition, scavenging lanthanum from LSM improved oxygen ion diffusion polarization as indicated by the observed 40% reduction in high frequency impedance and improved serial ohmic resistance by 19%. Finally, YSZ nanoparticles further reduced the high frequency impedance and ohmic resistance by 45% and 23%, respectively. The findings reveal new strategies for lowering the impedance of LSM-YSZ cathodes.
more »
« less
- Award ID(s):
- 1651186
- PAR ID:
- 10304555
- Publisher / Repository:
- The Electrochemical Society
- Date Published:
- Journal Name:
- Journal of The Electrochemical Society
- Volume:
- 168
- Issue:
- 11
- ISSN:
- 0013-4651
- Page Range / eLocation ID:
- Article No. 114508
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
This paper addresses the use of Ce 0.8 Gd 0.2 O 2−δ (GDC) infiltration into the Ni–(Y 2 O 3 ) 0.08 (ZrO 2 ) 0.92 (YSZ) fuel electrode of solid oxide cells (SOCs) for improving their electrochemical performance in fuel cell and electrolysis operation. Although doped ceria infiltration into Ni–YSZ has recently been shown to improve the electrode performance and stability, the mechanisms defining how GDC impacts electrochemical characteristics are not fully delineated. Furthermore, the electrochemical characteristics have not yet been determined over the full range of conditions normally encountered in fuel cell and electrolysis operation. Here we present a study of both symmetric and full cells aimed at understanding the electrochemical mechanisms of GDC-modified Ni–YSZ over a wide range of fuel compositions and temperatures. Single-step GDC infiltration at an appropriate loading substantially reduced the polarization resistance of Ni–YSZ electrodes in electrolyte-supported cells, as measured using electrochemical impedance spectroscopy (EIS) at various temperatures (600–800 °C) in a range of H 2 O–H 2 mixtures (3–90 vol% H 2 O). Fuel-electrode-supported cells had significant concentration polarization due to the thick Ni–YSZ supports. A distribution of relaxation times approach is used to develop a physically-based electrochemical model; the results show that GDC reduces the reaction resistance associated with three-phase boundaries, but also appears to improve oxygen transport in the electrode. Increasing the H 2 O fraction in the H 2 –H 2 O fuel mixture reduced both the three-phase boundary resistance and the gas diffusion resistance for Ni–YSZ; with GDC infiltration, the electrode resistance showed less variation with fuel composition. GDC infiltration improved the performance of fuel-electrode-supported full cells, which yielded a maximum power density of 2.28 W cm −2 in fuel cell mode and an electrolysis current density at 1.3 V of 2.22 A cm −2 , both at 800 °C.more » « less
-
null (Ed.)Sr(Ti 0.3 Fe 0.7 )O 3−δ (STF) and the associated exsolution electrodes Sr 0.95 (Ti 0.3 Fe 0.63 Ru 0.07 )O 3−δ (STFR), or Sr 0.95 (Ti 0.3 Fe 0.63 Ni 0.07 )O 3−δ (STFN) are alternatives to Ni-based cermet fuel electrodes for solid oxide electrochemical cells (SOCs). They can provide improved tolerance to redox cycling and fuel impurities, and may allow direct operation with hydrocarbon fuels. However, such perovskite-oxide-based electrodes present processing challenges for co-sintering with thin electrolytes to make fuel electrode supported SOCs. Thus, they have been mostly limited to electrolyte-supported SOCs. Here, we report the first example of the application of perovskite oxide fuel electrodes in novel oxygen electrode supported SOCs (OESCs) with thin YSZ electrolytes, and demonstrate their excellent performance. The OESCs have La 0.8 Sr 0.2 MnO 3−δ –Zr 0.92 Y 0.16 O 2−δ (LSM–YSZ) oxygen electrode-supports that are enhanced via infiltration of SrTi 0.3 Fe 0.6 Co 0.1 O 3−δ , while the fuel electrodes are either Ni-YSZ, STF, STFN, or STFR. Fuel cell power density as high as 1.12 W cm −2 is obtained at 0.7 V and 800 °C in humidified hydrogen and air with the STFR electrode, 60% higher than the same cell made with a Ni-YSZ electrode. Electrolysis current density as high as −1.72 A cm −2 is obtained at 1.3 V and 800 °C in 50% H 2 O to 50% H 2 mode; the STFR cell yields a value 72% higher than the same cell made with a Ni-YSZ electrode, and competitive with the widely used conventional Ni-YSZ-supported cells. The high performance is due in part to the low resistance of the thin YSZ electrolyte, and also to the low fuel electrode polarization resistance, which decreases with fuel electrode in the order: Ni-YSZ > STF > STFN > STFR. The high performance of the latter two electrodes is due to exsolution of catalytic metal nanoparticles; the results are discussed in terms of the microstructure and properties of each electrode material, and surface oxygen exchange resistance values are obtained over a range of conditions for STF, STFN, and STFN. The STF fuel electrodes also provide good stability during redox cycling.more » « less
-
Most of the measurements of electrode polarization resistance are conducted using electrochemical impedance spectroscopy (EIS). The electrochemical devices, however, are typically used in a DC mode. The objective of the present work was to measure electrode polarization resistance using both EIS and DC techniques. A solid cylinder of 8YSZ of diameter ~1.17 cm and length ~5.00 cm was made by powder pressing followed by sintering. LSM + YSZ electrodes were applied on the two end surfaces of the cylinder upon which gold mesh was placed. Four Pt electrodes/probes were painted along the circumference. During DC measurements, DC voltage was applied across the end electrodes and potentials were measured at all four probes. The current was also measured. From these measurements electrode polarizations were estimated separately for the two electrodes as a function of current. EIS was conducted across the two end electrodes as well as across electrode-1 and probe-2, and across probe-2 and electrode-2. This allowed the determination of the polarization resistances of the two electrodes separately. Point by point additions of the electrode-1/probe-2 and probe-2/electrode-2 spectra matched the electrode-1/electrode-2 spectra. There was good agreement between the DC and the EIS measurements.more » « less
-
Stimuli-responsive supramolecular assemblies are dynamic systems that can reversibly switch between different states upon external stimuli. In this context, metal coordination offers a reliable strategy for the preparation of stimuli responsive supramolecular architectures. Herein we report the preparation of a solvent-responsive cavitand-lanthanum coordination complex. A tetra-phosphonate cavitand has been functionalized with four hydroxyl moieties at the upper rim to form a pre-organized octadentate ligand capable of binding lanthanum salts. Exploiting the orthogonal recognition sites, two different complex architectures are formed in acetonitrile and acetone, respectively. The complexes have been characterized in solution by NMR spectroscopy, ITC experiments, while at the solid state, the single crystal structure of the acetonitrile derivative has been determined. Furthermore, as observed by DOSY-NMR spectroscopy, small quantities of acetone in acetonitrile are sufficient to trigger assembly interconversion.more » « less