Title: Coupling of 3D Porous Hosts for Li Metal Battery Anodes with Viscous Polymer Electrolytes
As the energy storage markets demand increased capacity of rechargeable batteries, Li metal anodes have regained major attention due to their high theoretical specific capacity. However, Li anodes tend to have dendritic growth and constant electrolyte consumption upon cycling, which lead to safety concerns, low Coulombic efficiency, and short cycle life of the battery. In this work, both conductive and non-conductive 3D porous hosts were coupled with a viscous (melt) polymer electrolyte. The cross-section of the hosts showed good contact between porous hosts and the melt polymer electrolyte before and after extensive cycling, indicating that the viscous electrolyte successfully refilled the space upon Li stripping. Upon deep Li deposition/stripping cycling (5 mAh cm-2), the non-conductive host with the viscous electrolyte successfully cycled, while conductive host allowed rapid short circuiting. Post-mortem cross-sectional imaging showed that the Li deposition was confined to the top layers of the host. COMSOL simulations indicated that current density was higher and more restricted to the top of the conductive host with the polymer electrolyte than the liquid electrolyte. This resulted in quicker short circuiting of the polymer electrolyte cell during deep cycling. Thus, the non-conductive 3D host is preferred for coupling with the melt polymer electrolyte.  more » « less
Award ID(s):
1904196
NSF-PAR ID:
10312742
Author(s) / Creator(s):
; ; ; ; ; ;
Date Published:
Journal Name:
Journal of The Electrochemical Society
ISSN:
0013-4651
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ( , Advanced Functional Materials)
    Abstract

    Porous carbon scaffolds can host lithium (Li) metal anodes to potentially enable stable Li metal batteries. However, the poor Li metal wettability on the carbon surface has inhibited the uniform distribution of metallic Li on most carbon scaffolds. Herein, this work reports a lithiophilic top layer through mild surface ozonolysis and ammoniation methods can universally facilitate the infiltration of liquid Li metal into most carbon matrices. Based on this finding, thin, a lightweight Li@carbon film (CF) composite anode with a high practical capacity of 3222 mAh g−1and suppressed volume expansion and dendrite formation is reported. It is observed that the deep stripping/plating pre‐cycling yields dense, trunky Li metal in the Li@CF composite, which allows for favorable long‐term cycling performance. The full cell combining the thin Li@CF composite anode and a high‐mass‐loading, cobalt‐free cathode can deliver high reversible capacity, good cycle stability, and good rate capability in the conventional carbonate electrolyte. The present study further establishes the relationship between lithiophilicity and hydrophilicity for carbon materials as well as provides insights into improving the liquid Li metal infiltration into other carbon scaffolds.

     
    more » « less
  2. ; ; ; ; ; ; ; ( , Sustainable Energy & Fuels)
    Lithium metal as an anode has been widely accepted due to its higher negative electrochemical potential and theoretical capacity. Nevertheless, the existing safety and cyclability issues limit lithium metal anodes from practical use in high-energy density batteries. Repeated Li deposition and dissolution processes upon cycling lead to the formation of dendrites at the interface which results in reduced Li availability for electrochemical reactions, disruption in Li transport through the interface and increased safety concerns due to short circuiting. Here, we demonstrate a novel strategy using Ionic Liquid Crystals (ILCs) as the electrolyte cum pseudo-separator to suppress dendrite growth with their anisotropic properties controlling Li-ion mass transport. A thermotropic ILC with two-dimensional Li-ion conducting pathways was synthesized and characterized. Microscopic and spectroscopic analyses elucidate that the ILC formed with a smectic A phase, which can be utilized for wide temperature window operation. The results of electrochemical studies corroborate the efficacy of ILC electrolytes in mitigating dendrite formation even after 850 hours and it is further substantiated by numerical simulation and the mechanism involved in dendritic suppression was deduced. 
    more » « less
  3. ; ; ; ; ; ; ; ( , Advanced Functional Materials)
    Abstract

    A vertically aligned carbon nanofiber (VACNF) array with unique conically stacked graphitic structure directly grown on a planar Cu current collector (denoted as VACNF/Cu) is used as a high‐porosity 3D host to overcome the commonly encountered issues of Li metal anodes. The excellent electrical conductivity and highly active lithiophilic graphitic edge sites facilitate homogenous coaxial Li plating/stripping around each VACNF and forming a uniform solid electrolyte interphase. The high specific surface area effectively reduces the local current density and suppresses dendrite growth during the charging/discharging processes. Meanwhile, this open nanoscale vertical 3D structure eliminates the volume changes during Li plating/stripping. As a result, highly reversible Li plating/stripping with high coulombic efficiency is achieved at various current densities. A low voltage hysteresis of 35 mV over 500 h in symmetric cells is achieved at 1 mA cm−2with an areal Li plating capacity of 2 mAh cm−2, which is far superior to the planar Cu current collector. Furthermore, a Li–S battery using a S@PAN cathode and a lithium‐plated VACNF/Cu (VACNF/Cu@Li) anode with slightly higher capacity (2 mAh cm−2) exhibits an excellent rate capability and high cycling stability with no capacity fading over 600 cycles.

     
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al ( , Advanced Energy Materials)
    Abstract

    Traditional challenges of poor cycling stability and low Coulombic efficiency in Zinc (Zn) metal anodes have limited their practical application. To overcome these issues, this work introduces a single metal‐atom design featuring atomically dispersed single copper (Cu) atoms on 3D nitrogen (N) and oxygen (O) co‐doped porous carbon (CuNOC) as a highly reversible Zn host. The CuNOC structure provides highly active sites for initial Zn nucleation and further promotes uniform Zn deposition. The 3D porous architecture further mitigates the volume changes during the cycle with homogeneous Zn2+flux. Consequently, CuNOC demonstrates exceptional reversibility in Zn plating/stripping processes over 1000 cycles at 2 and 5 mA cm−2with a fixed capacity of 1 mAh cm−2, while achieving stable operation and low voltage hysteresis over 700 h at 5 mA cm−2and 5 mAh cm−2. Furthermore, density functional theory calculations show that co‐doping N and O on porous carbon with atomically dispersed single Cu atoms creates an efficient zincophilic site for stable Zn nucleation. A full cell with the CuNOC host anode and high loading V2O5cathode exhibits outstanding rate‐capability up to 5 A g−1and a stable cycle life over 400 cycles at 0.5 A g−1.

     
    more » « less
  5. ; ; ; ; ; ; ; ; ; ; et al ( , Batteries & Supercaps)
    Abstract

    The cycle life of rechargeable lithium (Li)‐metal batteries is mainly restrained by dendrites growth on the Li‐metal anode and fast depletion of the electrolyte. Here, we report on a stable Li‐metal anode enabled by interconnected two‐dimensional (2D) arrays of niobium nitride (NbN) nanocrystals as the Li host, which exhibits a high Coulombic efficiency (>99 %) after 500 cycles. Combining theoretical and experimental analysis, it is inferred that this performance is due to the intrinsic properties of interconnected 2D arrays of NbN nanocrystals, such as thermodynamic stability against Li‐metal, high Li affinity, fast Li+migration, and Li+transport through the porous 2D nanosheets. Coupled with a lithium nickel–manganese–cobalt oxide cathode, full Li‐metal batteries were built, which showed high cycling stability under practical conditions – high areal cathode loading ≥4 mAh cm−2, low negative/positive (N/P) capacity ratio of 3, and lean electrolyte weight to cathode capacity ratio of 3 g Ah−1. Our results indicate that transition metal nitrides with a rationally designed structure may alleviate the challenges of developing dendrite‐free Li‐metal anodes.

     