skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Current density at failure of twinned silver nanowires
Abstract Silver nanowires have a wide range of potential applications in stretchable and transparent electronics due to their excellent electrical, mechanical, and optical properties. For a successful application in electronic devices, evaluating the electrical reliability of these nanowires is required. We have studied experimentally the behavior of current density at failure for penta-twinned silver nanowires with diameters between 53 and 173 nm, for 93 samples. The current densities at failure are widely scattered, have an average of 9.7 × 10 7 A cm −2 , and a standard deviation of 2.96 × 10 7 A cm −2 . Heat-transfer modeling is employed to explain the results, and Weibull statistics are used to quantify failure probabilities, thus offering guidelines for future designs based on these nanowires. The scatter observed in the measurements is attributed to surface-roughness variations among samples, which lead to local hot spots of high current density. These results quantify the Joule heating electrical reliability of silver nanowires and highlight the importance of heat transfer in increasing it.  more » « less
Award ID(s):
1807686
PAR ID:
10330846
Author(s) / Creator(s):
;
Publisher / Repository:
Elsevier
Date Published:
Journal Name:
Nanotechnology
Volume:
33
Issue:
30
ISSN:
0957-4484
Page Range / eLocation ID:
305706
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; (, figshare)
    We have studied experimentally the behavior of current density at failure for penta-twinned silver nanowires with diameters between 53 nm and 173 nm, for 93 samples. The current densities at failure have an average of 9.7 x 10^7 A/cm2. 
    more » « less
  2. ; ; ; ; ; (, Additive Manufacturing Letters)
    The reliability of additively manufactured flexible electronics or so-called printed electronics is defined as mean time to failure under service conditions, which often involve mechanical loads. It is thus important to understand the mechanical behavior of the printed materials under such conditions to ensure their applicational reliability in, for example, sensors, biomedical devices, battery and storage, and flexible hybrid electronics. In this article, a testing protocol to examine the print quality of additively nanomanufactured electronics is presented. The print quality is assessed by both tensile and electrical resistivity responses during in-situ tension tests. A laser based additive nanomanufacturing method is used to print conductive silver lines on polyimide substrates, which is then tested in-situ under tension inside a scanning electron microscope (SEM). The surface morphology of the printed lines is continuously monitored via the SEM until failure. In addition, the real-time electrical resistance variations of the printed silver lines are measured in-situ with a multimeter during tensile tests conducted outside of the SEM. The protocol is shown to be effective in assessing print quality and aiding process tuning. Finally, it is revealed that samples appearing identical under the SEM can have significant different tendencies to delaminate. 
    more » « less
  3. ; ; ; ; (, Nanophotonics)
    Abstract We have grown arrays of silver nanowires in pores of anodic alumina membranes (metamaterials with hyperbolic dispersion at λ  ≥ 615 nm), spin coated them with the dye-doped polymer (HITC:PMMA), and studied the rates of radiative and nonradiative relaxation as well as the concentration quenching (Förster energy transfer to acceptors). The results were compared to those obtained on top of planar Ag films and glass (control samples). The strong spatial inhomogeneity of emission kinetics recorded in different spots across the sample and strong inhibition of the concentration quenching in arrays of Ag nanowires are among the most significant findings of this study. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; (, ChemNanoMat)
    Abstract We have successfully synthesized ultrathin nanowires of pure Pt, Pt99Ni1, Pt9Ni1, and Pt7Ni3using a modified room‐temperature soft‐template method. Analysis of both methanol oxidation reaction (MOR) and ethanol oxidation reaction (EOR) results found that the Pt7Ni3samples yielded the best performance with specific activities of 0.36 and 0.34 mA/cm2respectively. Additionally, formic acid oxidation reaction (FAOR) tests noted that both Pt and PtNi nanowires oxidize small organic molecules (SOMs) via an indirect pathway. CO oxidation data suggests little measurable performance without any pre‐reduction treatment; however, after annealing in H2, we detected significantly improved CO2formation for both Pt9Ni1and Pt7Ni3motifs. These observations highlight the importance of pre‐treating these nanowires under a reducing atmosphere to enhance their performance for CO oxidation. To explain these findings, we collected extended x‐ray adsorption fine structure (EXAFS) spectroscopy data, consistent with the presence of partial alloying with a tendency for Pt and Ni to segregate, thereby implying the formation of a Pt‐rich shell coupled with a Ni‐rich core. We also observed that the degree of alloying within the nanowires increased after annealing in a reducing atmosphere, a finding deduced through analysis of the coordination numbers and calculations of Cowley's short range order parameters. 
    more » « less
  5. ; (, Extreme Mechanics Letters)
    Penta-twinned nanowires, made of silver, gold, or copper, are envisioned to enable many applications, most notably stretchable and flexible electronics. In several instances of analysis of their behavior for device design, such as heat transfer due to current-induced heating, adhesion to substrates, or adhesion of nanowires to each other in conductive networks, knowledge of variables related to the mechanics of their contact is needed, for example the contact area (or radius). Due to the nanowires’ change in cross section, from circular to rounded- pentagonal as diameter increases, adhesive contact analysis is complex, and up to now has been simplified to assume either circular or perfect pentagonal cross sections. Here, we analyze the adhesive contact of the nanowires, fully considering the complexity of the cross section. We present equations to describe the geometry of the cross-section as it decreases in roundness with increasing diameter, finite element simulations that include elastic anisotropy and Lennard-Jones adhesive interactions, and observations on the adequacy of simplified contact models in describing the behavior. Calculations are presented for contact to typical stiff (silicon) and compliant (PDMS) substrates. The results reveal that, contrary to previous assumptions, the nanowires do not conform to the behavior of a perfect pentagon for the diameters typically encountered experimentally, and the roundness of the cross-section remains a factor that reduces the contact area. This reduction depends on the stiffness of the contact, being greater for stiff substrates.Penta-twinned nanowires, made of silver, gold, or copper, are envisioned to enable many applications, most notably stretchable and flexible electronics. In several instances of analysis of their behavior for device design, such as heat transfer due to current-induced heating, adhesion to substrates, or adhesion of nanowires to each other in conductive networks, knowledge of variables related to the mechanics of their contact is needed, for example the contact area (or radius). Due to the nanowires’ change in cross section, from circular to rounded- pentagonal as diameter increases, adhesive contact analysis is complex, and up to now has been simplified to assume either circular or perfect pentagonal cross sections. Here, we analyze the adhesive contact of the nanowires, fully considering the complexity of the cross section. We present equations to describe the geometry of the cross-section as it decreases in roundness with increasing diameter, finite element simulations that include elastic anisotropy and Lennard-Jones adhesive interactions, and observations on the adequacy of simplified contact models in describing the behavior. Calculations are presented for contact to typical stiff (silicon) and compliant (PDMS) substrates. The results reveal that, contrary to previous assumptions, the nanowires do not conform to the behavior of a perfect pentagon for the diameters typically encountered experimentally, and the roundness of the cross-section remains a factor that reduces the contact area. This reduction depends on the stiffness of the contact, being greater for stiff substrates. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email