Title: Preparation of Bulk TiZrNbMoV and NbTiAlTaV High-Entropy Alloys by Powder Sintering
The refractory HEAs block material was prepared by powder sintering, using an equal atomic proportion of mixed TiZrNbMoV and NbTiAlTaV metal powder raw materials. The phase was analyzed, using an XRD. The microstructure of the specimen was observed, employing a scanning electron microscope, and the compressive strength of the specimen was measured, using an electronic universal testing machine. The results showed that the bulk cubic alloy structure was obtained by sintering at 1300 °C and 30 MPa for 4 h, and a small amount of complex metal compounds were contained. According to the pore distribution, the formed microstructure can be divided into dense and porous zones. At a compression rate of 10−4s−1, the yield strengths of TiZrNbMoV and NbTiAlTaV alloys are 1201 and 700 MPa, respectively.  more » « less
Award ID(s):
1809640
NSF-PAR ID:
10343635
Author(s) / Creator(s):
; ;
Date Published:
Journal Name:
Metals
Volume:
11
Issue:
11
ISSN:
2075-4701
Page Range / eLocation ID:
1748
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    The direct selective laser sintering (SLS) process was successfully demonstrated for additive manufacturing of high-entropy carbide ceramics (HECC), in which a Yb fiber laser was employed for ultrafast (in seconds) reactive sintering of HECC specimens from a powder mixture of constitute monocarbides. A single-phase non-equiatomic HECC was successfully formed in the 4-HECC specimen with a uniform distribution of Zr, Nb, Hf, Ta, and C. In contrast, a three-layer microstructure was formed in the 5-HECC specimen with five metal elements (Zr, Nb, Hf, Ta and Ti), consisting of a TiC-rich top layer, a Zr–Hf–C enriched intermediate layer, and a non-equiatomic Zr–Ta–Nb–Hf–C HECC layer. Vickers hardness of 4- and 5-HECC specimens were 22.2 and 21.8 GPa, respectively, on the surface. These findings have important implications on the fundamental mechanisms governing interactions between laser and monocarbide powders to form a solid solution of HECCs during SLS.

    Graphical abstract

     
    more » « less
  2. Purpose There is recent emphasis on designing new materials and alloys specifically for metal additive manufacturing (AM) processes, in contrast to AM of existing alloys that were developed for other traditional manufacturing methods involving considerably different physics. Process optimization to determine processing recipes for newly developed materials is expensive and time-consuming. The purpose of the current work is to use a systematic printability assessment framework developed by the co-authors to determine windows of processing parameters to print defect-free parts from a binary nickel-niobium alloy (NiNb5) using laser powder bed fusion (LPBF) metal AM. Design/methodology/approach The printability assessment framework integrates analytical thermal modeling, uncertainty quantification and experimental characterization to determine processing windows for NiNb5 in an accelerated fashion. Test coupons and mechanical test samples were fabricated on a ProX 200 commercial LPBF system. A series of density, microstructure and mechanical property characterization was conducted to validate the proposed framework. Findings Near fully-dense parts with more than 99% density were successfully printed using the proposed framework. Furthermore, the mechanical properties of as-printed parts showed low variability, good tensile strength of up to 662 MPa and tensile ductility 51% higher than what has been reported in the literature. Originality/value Although many literature studies investigate process optimization for metal AM, there is a lack of a systematic printability assessment framework to determine manufacturing process parameters for newly designed AM materials in an accelerated fashion. Moreover, the majority of existing process optimization approaches involve either time- and cost-intensive experimental campaigns or require the use of proprietary computational materials codes. Through the use of a readily accessible analytical thermal model coupled with statistical calibration and uncertainty quantification techniques, the proposed framework achieves both efficiency and accessibility to the user. Furthermore, this study demonstrates that following this framework results in printed parts with low degrees of variability in their mechanical properties. 
    more » « less
  3. Adding excessive metal oxide doping to a powder batch is a known way to compensate for the loss of volatile cation species during high temperature sintering. An important case in the piezoelectric ceramics is the bismuth oxide in the lead-free ferroelectric ceramic bismuth sodium titanate (BNT). Building from the earlier knowledge about excessive bismuth oxide's influences on the properties of BNT, we further note that varying the sintering temperature can both control the distribution of excessive Bi3+ and impact the relaxor/normal ferroelectric behaviors and corresponding phase transition. In addition to the nature of polarization, the sintering temperature also significantly manipulates the electrical conductivity. A hypothetical mechanism for the resistive grain boundary is proposed, based on inferences from electrical—microstructure—processing relations in 85% Bi0.5Na0.5TiO3-15% BaTiO3 with batched Bi2O3 excess and acceptor Mg2+ in a co-doped strategy.

     
    more » « less
  4. A boron-rich boron–carbide material (B4+δC) was synthesized by spark plasma sintering of a ball-milled mixture of high-purity boron powder and graphitic carbon at a pressure of 7 MPa and a temperature of 1930 °C. This high-pressure, high-temperature synthesized material was recovered and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, Vickers hardness measurements, and thermal oxidation studies. The X-ray diffraction studies revealed a single-phase rhombohedral structure (space group R-3m) with lattice parameters in hexagonal representation as a = 5.609 ± 0.007 Å and c = 12.082 ± 0.02 Å. The experimental lattice parameters result in a value of δ = 0.55, or the composition of the synthesized compound as B4.55C. The high-resolution scans of boron binding energy reveal the existence of a B-C bond at 188.5 eV. Raman spectroscopy reveals the existence of a 386 cm−1 vibrational mode representative of C-B-B linear chain formation due to excess boron in the lattice. The measured Vickers microhardness at a load of 200 gf shows a high hardness value of 33.8 ± 2.3 GPa. Thermal gravimetric studies on B4.55C were conducted at a temperature of 1300 °C in a compressed dry air environment, and its behavior is compared to other high-temperature ceramic materials such as high-entropy transition metal boride. The high neutron absorption cross section, high melting point, high mechanical strength, and thermal oxidation resistance make this material ideal for applications in extreme environments.

     
    more » « less
  5. Abstract

    This study binder jets a tungsten carbide‐nickel (WC‐Ni) sintered‐agglomerated composite powder, and postprocesses the preforms using an initial sintering step followed by a hot isostatic pressing (HIP) step. The effects of sintering temperatures, sintering durations, and HIP temperatures on notable properties (e.g., porosity, microstructure, hardness, and oxidation behavior) are quantified. The highest average relative density produced in this study was 96.8%, and volumetric shrinkage of these coupons was about 64%. Microstructural characterization shows that the WC grains are homogenously distributed throughout the nickel matrix and grow to an average diameter of 1.6 μm (a 60% increase) during processing. X‐ray diffraction patterns indicate that no unwanted products were formed. Processed coupons achieved a maximum hardness of 54 Rockwell C, limited by their internal porosity. Oxidation tests result in the production of WO3and NiWO4at temperatures above 600°C. Methodologies and results from this study can be leveraged to additively manufacture highly dense, geometrically complex WC‐Ni parts with small carbide grains, low nickel content, desirable microstructure, and suitable functional properties.

     
    more » « less