We report on inorganic CsPbBr 3 solar cells with very high open circuit voltages and excellent environmental stability. The cells were fabricated using vapor deposition. We show that by using an interfacial n-doped CdS (CdS:In) layer between the cell TiO2, we can obtain voltages of ∼1.68 V, the highest ever reported in vapor deposited CsPbBr3 material. A surprising phenomenon was that the crystal structure of the material, and the apparent bandgap, changed when a thicker CdS:In layer was used as the n layer. We also show that there is little environmental degradation in performance for a cell kept for 600 hours in room air, and even for a cell kept at 200 °C for 24 hours in air. The cells were deposited using sequential deposition in vacuum followed by anneals at 450 °C. We study both organic p layers (P3HT) and inorganic p layers (paste coated C).
more »
« less
Inorganic perovskite solar cells with high voltage and excellent stability against thermal and environmental degradation
We report on the properties and stability of inorganic perovskite CsPbBr3 fabricated using vapor deposition. We have obtained the highest voltage ever recorded, exceeding 1.6V, in this material. The material was deposited using vapor deposition process, followed by post-deposition anneal at 450 C. Both layer by layer, and sequential anneal processes were sued for growing the material. After growth and anneals, the material was tested for thermal stability at temperatures of 300 C, and the x-ray data showed that there was no degradation of the material even at this high temperature. n-i-p superstrate devices were fabricated on FTO substrates coated with either TiO2 or n-CdS. The p layer was P3HT or PTAA. The devices showed an open-circuit voltage of 1.62V, the highest ever reported in this material. The devices were exposed to humid room air for 25 days, and showed no degradation at all in its performance. Detailed material measurements such as subgap quantum efficiency and deep defects were measured. The Urbach energy for valence band tails is found to be 22 meV and mid-gap defect density in the range of few 1015/cm3.
more »
« less
- Award ID(s):
- 2035240
- PAR ID:
- 10343800
- Date Published:
- Journal Name:
- 2021 IEEE 48th Photovoltaic Specialists Conference (PVSC)
- Page Range / eLocation ID:
- 0425 to 0428
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract The structural properties of co-deposited ultrathin PtSe 2 films grown at low temperatures by molecular beam epitaxy on c-plane Al 2 O 3 are studied. By simultaneously supplying a Se flux from a Knudsen cell and Pt atoms from an electron-beam evaporator, crystalline (001)-oriented PtSe 2 films were formed between 200 °C and 300 °C. The long separation between substrate and electron beam evaporator of about 60 cm ensured minimal thermal load. At optimum deposition temperatures, a ten times or even higher supply rate of Se compared to Pt ensured that the pronounced volatility of the Se was compensated and the PtSe 2 phase was formed and stabilized at the growth front. Postgrowth anneals under a Se flux was found to dramatically improve the crystalline quality of the films. Even before the postgrowth anneal in Se, the crystallinity of PtSe 2 films grown with the co-deposition method was superior to films realized by thermal assisted conversion. Postgrowth annealed films showed Raman modes with narrower peaks and more than twice the intensity. Transmission electron microscopy investigations revealed that the deposited material transitioned to a two-dimensional layered structure only after the postgrowth anneal. PtSe 2 growth was found to start as single layer islands that preferentially nucleated at atomic steps of the substrate and progressed in a layer-by-layer like fashion. A close to ideal wetting behavior resulted in coalesced PtSe 2 films after depositing about 1.5 PtSe 2 layers. Detailed Raman investigation of the observed PtSe 2 layer breathing modes of films grown under optimized co-deposition conditions revealed an interlayer coupling force constant of 5.0–5.6 × 10 19 N m −3 .more » « less
-
This work demonstrates quasi-vertical β-Ga2O3 Schottky barrier diodes (SBDs) fabricated on c-plane sapphire substrates using an all-low-pressure chemical vapor deposition (LPCVD)-based, plasma-free process flow that integrates both epitaxial growth of a high-quality β-Ga2O3 heteroepitaxial film with in situ Ga-assisted β-Ga2O3 etching. A 6.3 μm thick (2̄01) oriented β-Ga2O3 epitaxial layer structure was grown on c-plane sapphire with 6° miscut, comprising a moderately Si-doped (2.1 × 1017 cm−3) 3.15 μm thick drift layer and a heavily doped (1 × 1019 cm−3) contact layer on an unintentionally doped buffer layer. Mesa isolation was achieved via Ga-assisted plasma-free LPCVD etching, producing ∼60° inclined mesa sidewalls with an etch depth of 3.6 μm. The fabricated SBDs exhibited excellent forward current–voltage characteristics, including a turn-on voltage of 1.22 V, an ideality factor of 1.29, and a Schottky barrier height of 0.83 eV. The minimum differential specific on-resistance was measured to be 8.6 mΩ cm2, and the devices demonstrated high current density capability (252 A/cm2 at 5 V). Capacitance–voltage analysis revealed a net carrier concentration of 2.1 × 1017 cm−3, uniformly distributed across the β-Ga2O3 drift layer. Temperature-dependent J–V–T measurements, conducted from 25 to 250 °C, revealed thermionic emission-dominated transport with strong thermal stability. The Schottky barrier height increased from 0.80 to 1.16 eV, and the ideality factor rose modestly from 1.31 to 1.42 over this temperature range. Reverse leakage current remained low, increasing from ∼5 × 10−6 A/cm2 at 25 °C to ∼1 × 10−4 A/cm2 at 250 °C, with the Ion/Ioff ratio decreasing from ∼1 × 107 to 5 × 105. The devices achieved breakdown voltages ranging from 73 to 100 V, corresponding to parallel-plate electric field strengths of 1.66–1.94 MV/cm. These results highlight the potential of LPCVD-grown and etched β-Ga2O3 devices for high-performance, thermally resilient power electronics applications.more » « less
-
We report the electrical properties of Al0.3Ga0.7N/GaN heterojunction field effect transistor (HFET) structures with a Ga2O3 passivation layer grown by metal–organic chemical vapor deposition (MOCVD). In this study, three different thicknesses of β-Ga2O3 dielectric layers were grown on Al0.3Ga0.7N/GaN structures leading to metal-oxide-semiconductor-HFET or MOSHFET structures. X-ray diffraction (XRD) showed the (2¯01) orientation peaks of β-Ga2O3 in the device structure. The van der Pauw and Hall measurements yield the electron density of ~ 4 × 1018 cm−3 and mobility of ~770 cm2V−1s−1 in the 2-dimensional electron gas (2DEG) channel at room temperature. Capacitance–voltage (C-V) measurement for the on-state 2DEG density for the MOSHFET structure was found to be of the order of ~1.5 × 1013 cm−2. The thickness of the Ga2O3 layer was inversely related to the threshold voltage and the on-state capacitance. The interface charge density between the oxide and Al0.3Ga0.7N barrier layer was found to be of the order of ~1012 cm2eV−1. A significant reduction in leakage current from ~10−4 A/cm2 for HFET to ~10−6 A/cm2 for MOSHFET was observed well beyond pinch-off in the off-stage at -20 V applied gate voltage. The annealing at 900° C of the MOSHFET structures revealed that the Ga2O3 layer was thermally stable at high temperatures resulting in insignificant threshold voltage shifts for annealed samples with respect to as-deposited (unannealed) structures. Our results show that the MOCVD-gown Ga2O3 dielectric layers can be a strong candidate for stable high-power devices.more » « less
-
The thermal stability of n/n + β -Ga 2 O 3 epitaxial layer/substrate structures with sputtered ITO on both sides to act as rectifying contacts on the lightly doped layer and Ohmic on the heavily doped substrate is reported. The resistivity of the ITO deposited separately on Si decreased from 1.83 × 10 −3 Ω.cm as-deposited to 3.6 × 10 −4 Ω.cm after 300 °C anneal, with only minor reductions at higher temperatures (2.8 × 10 −4 Ω.cm after 600 °C anneals). The Schottky barrier height also decreased with annealing, from 0.98 eV in the as-deposited samples to 0.85 eV after 500 °C annealing. The reverse breakdown voltage exhibited a negative temperature coefficient of −0.46 V.C −1 up to an annealing temperature of 400 °C and degraded faster at higher temperatures. Transmission Electron Microscopy showed significant reaction at the ITO and Ga 2 O 3 interface above 300 °C, with a very degraded contact stack after annealing at 500 °C.more » « less
An official website of the United States government