Here we present the synthesis and characterization of a hybrid vanadium-organic coordination polymer with robust magnetic order, a Curie temperature T C of ∼110 K, a coercive field of ∼5 Oe at 5 K, and a maximum mass magnetization of about half that of the benchmark ferrimagnetic vanadium(tetracyanoethylene) ∼2 (V·(TCNE) ∼2 ). This material was prepared using a new tetracyano-substituted quinoidal organic small molecule 7 based on a tricyclic heterocycle 4-hexyl-4 H -pyrrolo[2,3- d :5,4- d ′]bis(thiazole) ( C6-PBTz ). Single crystal X-ray diffraction of the 2,6-diiodo derivative of the parent C6-PBTz , showed a disordered hexyl chain and a nearly linear arrangement of the substituents in positions 2 and 6 of the tricyclic core. Density functional theory (DFT) calculations indicate that C6-PBTz -based ligand 7 is a strong acceptor with an electron affinity larger than that of TCNE and several other ligands previously used in molecular magnets. This effect is due in part to the electron-deficient thiazole rings and extended delocalization of the frontier molecular orbitals. The ligand detailed in this study, a representative example of fused heterocycle aromatic cores with extended π conjugation, introduces new opportunities for structure–magnetic-property correlation studies where the chemistry of the tricyclic heterocycles can modulate the electronic properties and the substituent at the central N -position can vary the spatial characteristics of the magnetic polymer.
more »
« less
Probing the structure of vanadium tetracyanoethylene using electron energy-loss spectroscopy
The molecule-based ferrimagnetic semiconductor vanadium tetracyanoethylene (V[TCNE] x , x [Formula: see text] 2) has garnered interest from the quantum information community due to its excellent coherent magnonic properties and ease of on-chip integration. Despite these attractive properties, a detailed understanding of the electronic structure and mechanism for long-range magnetic ordering have remained elusive due to a lack of detailed atomic and electronic structural information. Previous studies via x-ray absorption near edge spectroscopy and the extended x-ray absorption fine structure have led to various proposed structures, and in general, V[TCNE] x is believed to be a three-dimensional network of octahedrally coordinated V 2+ , each bonded to six TCNE molecules. Here, we elucidate the electronic structure, structural ordering, and degradation pathways of V[TCNE] x films by correlating calculations of density functional theory (DFT) with scanning transmission electron microscopy and electron energy-loss spectroscopy (EELS) of V[TCNE] x films. Low-loss EELS measurements reveal a bandgap and an excited state structure that agree quantitatively with DFT modeling, including an energy splitting between apical and equatorial TCNE ligands within the structure, providing experimental results directly backed by theoretical descriptions of the electronic structure driving the robust magnetic ordering in these films. Core-loss EELS confirms the presence of octahedrally coordinated V +2 atoms. Upon oxidation, changes in the C1s- π* peak indicate that C=C of TCNE is preferentially attacked. Furthermore, we identify a relaxation of the structural ordering as the films age. These results lay the foundation for a more comprehensive and fundamental understanding of magnetic ordering and dynamics in these classes of metal–ligand compounds.
more »
« less
- PAR ID:
- 10350058
- Date Published:
- Journal Name:
- APL Materials
- Volume:
- 10
- Issue:
- 8
- ISSN:
- 2166-532X
- Page Range / eLocation ID:
- 081102
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Transition metal spinel oxides comprised of earth-abundant Mn and Co have long been explored for their use in catalytic reactions and energy storage. However, understanding functional properties can be challenging due to differences in sample preparation and the ultimate structural properties of the materials. Epitaxial thin film synthesis provides a novel means of producing precisely controlled materials to explore the variations reported in the literature. In this work, MnxCo3−xO4 samples from x = 0 to x = 1.28 were synthesized through molecular beam epitaxy and characterized to develop a material properties map as a function of stoichiometry. Films were characterized via in situ x-ray photoelectron spectroscopy, x-ray diffraction, scanning transmission electron microscopy, and polarized K-edge x-ray absorption spectroscopy. Mn cations within this range were found to be octahedrally coordinated, in line with an inverse spinel structure. Samples largely show mixed Mn3+ and Mn4+ character with evidence of phase segregation tendencies with the increasing Mn content and increasing Mn3+ formal charge. Phase segregation may occur due to structural incompatibility between cubic and tetragonal crystal structures associated with Mn4+ and Jahn–Teller active Mn3+ octahedra, respectively. Our results help in explaining the reported differences across samples in these promising materials for renewable energy technologies.more » « less
-
For some intermetallic compounds containing lanthanides, structural transitions can result in intermediate electronic states between trivalency and tetravalency; however, this is rarely observed for praseodymium compounds. The dominant trivalency of praseodymium limits potential discoveries of emergent quantum states in itinerant 4f1systems accessible using Pr4+-based compounds. Here, we use in situ powder x-ray diffraction and in situ electron energy-loss spectroscopy (EELS) to identify an intermetallic example of a dominantly Pr4+state in the polymorphic system Pr2Co3Ge5. The structure-valence transition from a nearly full Pr4+electronic state to a typical Pr3+state shows the potential of Pr-based intermetallic compounds to host valence-unstable states and provides an opportunity to discover previously unknown quantum phenomena. In addition, this work emphasizes the need for complementary techniques like EELS when evaluating the magnetic and electronic properties of Pr intermetallic systems to reveal details easily overlooked when relying on bulk magnetic measurements alone.more » « less
-
W e present a scalable solution-processing method for fabricating high-quality graphene and graphene/1T-MoS 2 heterostructure films. The process begins with the synthesis of potassium-intercalated graphite (KC 8 ), which is exfoliated in tetrahydrofuran (THF) to produce stable dispersions of negatively charged (electron rich) graphene sheets. The graphene is subsequently transferred to water, forming a surfactant-free aqueous dispersion suitable for creating homogenous graphene films via vacuum filtration and stamping. Additionally, graphene is combined with 1T-MoS 2 nanosheets to fabricate graphene/1T-MoS 2 bulk heterostructure films. Comprehensive characterization, including X-ray diffraction (XRD), absorption spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy ( TEM), Raman spectroscopy, and X-ray photon emission spectroscopy (XPS), reveals that the heterostructure films exhibit enhanced optical and electronic properties, including improved light absorption, which could lead to novel photo-responsive devices. Raman spectroscopy shows significant changes in the graphene’s structural a nd electronic properties upon interaction with MoS 2 , indicating strong interlayer coupling and potential charge transfer between the layered components. The g raphene films demonstrate highly sensitive detection of dopamine (DA), while the graphene/1T-MoS 2 b ulk heterostructure films exhibit capacitance values up to 3 8.3 Fg − 1 at 5 mV/s in non-aqueous electrolytes. These results highlight the potential of these films for advanced applications in molecular sensing and energy storage.more » « less
-
Abstract High pressure is an effective tool to induce exotic quantum phenomena in magnetic topological insulators by controlling the interplay of magnetic order and topological state. This work presents a comprehensive high-pressure study of the crystal structure and magnetic ground state up to 62 GPa in an intrinsic topological magnet EuSn 2 P 2 . With a combination of high resolution X-ray diffraction, 151 Eu synchrotron Mössbauer spectroscopy, X-ray absorption spectroscopy, molecular orbital calculations, and electronic band structure calculations, it has been revealed that pressure drives EuSn 2 P 2 from a rhombohedral crystal to an amorphous phase at 36 GPa accompanied by a fourfold enhancement of magnetic ordering temperature. In the pressure-induced amorphous phase, Eu ions take an intermediate valence state. The drastic enhancement of magnetic ordering temperature from 30 K at ambient pressure to 130 K at 41.2 GPa resulting from Ruderman–Kittel–Kasuya–Yosida (RKKY) interactions likely attributes to the stronger Eu–Sn interaction at high pressure. These rich results demonstrate that EuSn 2 P 2 is an ideal platform to study the correlation of the enhanced RKKY interactions, disordered lattice, intermediate valence, and topological state.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1063/5.0087997