The in situ metalorganic chemical vapor deposition (MOCVD) growth of Al 2 O 3 dielectrics on β-Ga 2 O 3 and β-(Al x Ga 1−x ) 2 O 3 films is investigated as a function of crystal orientations and Al compositions of β-(Al x Ga 1−x ) 2 O 3 films. The interface and film qualities of Al 2 O 3 dielectrics are evaluated by high-resolution x-ray diffraction and scanning transmission electron microscopy imaging, which indicate the growth of high-quality amorphous Al 2 O 3 dielectrics with abrupt interfaces on (010), (100), and [Formula: see text] oriented β-(Al x Ga 1−x ) 2 O 3 films. The surface stoichiometries of Al 2 O 3 deposited on all orientations of β-(Al x Ga 1−x ) 2 O 3 are found to be well maintained with a bandgap energy of 6.91 eV as evaluated by high-resolution x-ray photoelectron spectroscopy, which is consistent with the atomic layer deposited (ALD) Al 2 O 3 dielectrics. The evolution of band offsets at both in situ MOCVD and ex situ ALD deposited Al 2 O 3 /β-(Al x Ga 1−x ) 2 O 3 is determined as a function of Al composition, indicating the influence of the deposition method, orientation, and Al composition of β-(Al x Ga 1−x ) 2 O 3 films on resulting band alignments. Type II band alignments are determined at the MOCVD grown Al 2 O 3 /β-(Al x Ga 1−x ) 2 O 3 interfaces for the (010) and (100) orientations, whereas type I band alignments with relatively low conduction band offsets are observed along the [Formula: see text] orientation. The results from this study on MOCVD growth and band offsets of amorphous Al 2 O 3 deposited on differently oriented β-Ga 2 O 3 and β-(Al x Ga 1−x ) 2 O 3 films will potentially contribute to the design and fabrication of future high-performance β-Ga 2 O 3 and β-(Al x Ga 1−x ) 2 O 3 based transistors using MOCVD in situ deposited Al 2 O 3 as a gate dielectric.
more »
« less
In Situ Dielectric Al 2 O 3 /β‐Ga 2 O 3 Interfaces Grown Using Metal–Organic Chemical Vapor Deposition
High quality dielectric‐semiconductor interfaces are critical for reliable high‐performance transistors. This paper reports the in situ metal–organic chemical vapor deposition of Al2O3on β‐Ga2O3as a potentially better alternative to the most commonly used atomic layer deposition (ALD). The growth of Al2O3is performed in the same reactor as Ga2O3using trimethylaluminum and O2as precursors without breaking the vacuum at a growth temperature of 600 °C. The fast and slow near interface traps at the Al2O3/β‐Ga2O3interface are identified and quantified using stressed capacitance–voltage (CV) measurements on metal oxide semiconductor capacitor (MOSCAP) structures. The density of shallow and deep level initially filled traps (Dit) are measured using ultraviolet‐assisted CV technique. The average Ditfor the MOSCAP is determined to be 6.4
- Award ID(s):
- 1931652
- NSF-PAR ID:
- 10360053
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Electronic Materials
- Volume:
- 7
- Issue:
- 11
- ISSN:
- 2199-160X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
In this work, we report a study of the temperature dependent pulsed current voltage and RF characterization of [Formula: see text]-(Al x Ga 1−x ) 2 O 3 /Ga 2 O 3 hetero-structure FETs (HFETs) before and after silicon nitride (Si 3 N 4 ) passivation. Under sub-microsecond pulsing, a moderate DC-RF dispersion (current collapse) is observed before passivation in gate lag measurements, while no current collapse is observed in the drain lag measurements. The dispersion in the gate lag is possibly attributed to interface traps in the gate–drain access region. DC-RF dispersion did not show any strong dependence on the pulse widths. Temperature dependent RF measurements up to 250 °C do not show degradation in the cutoff frequencies. After Si 3 N 4 deposition at 350 °C, a shift of the threshold voltage is observed which changed the DC characteristics. However, the current collapse is eliminated; at 200 ns pulse widths, a 50% higher current is observed compared to the DC at high drain voltages. No current collapse is observed even at higher temperatures. RF performance of the passivated devices does not show degradation. These results show that ex situ deposited Si 3 N 4 is a potential candidate for passivation of [Formula: see text]-(Al x Ga 1−x ) 2 O 3 /Ga 2 O 3 HFETs.more » « less
-
more » « less
α-Ga2O3has the corundum structure analogous to that of α-Al2O3. The bandgap energy of α-Ga2O3is 5.3 eV and is greater than that of β-Ga2O3, making the α-phase attractive for devices that benefit from its wider bandgap. The O–H and O–D centers produced by the implantation of H+and D+into α-Ga2O3have been studied by infrared spectroscopy and complementary theory. An O–H line at 3269 cm−1is assigned to H complexed with a Ga vacancy (VGa), similar to the case of H trapped by an Al vacancy (VAl) in α-Al2O3. The isolated VGaand VAldefects in α-Ga2O3and α-Al2O3are found by theory to have a “shifted” vacancy-interstitial-vacancy equilibrium configuration, similar to VGain β-Ga2O3, which also has shifted structures. However, the addition of H causes the complex with H trapped at an unshifted vacancy to have the lowest energy in both α-Ga2O3and α-Al2O3.
-
more » « less
We report on growth and electrical properties of α-Ga2O3films prepared by halide vapor phase epitaxy (HVPE) at 500 °C on α-Cr2O3buffers predeposited on sapphire by magnetron sputtering. The α-Cr2O3buffers showed a wide microcathodoluminescence (MCL) peak near 350 nm corresponding to the α-Cr2O3bandgap and a sharp MCL line near 700 nm due to the Cr+intracenter transition. Ohmic contacts to Cr2O3were made with both Ti/Au or Ni, producing linear current–voltage ( I– V) characteristics over a wide temperature range with an activation energy of conductivity of ∼75 meV. The sign of thermoelectric power indicated p-type conductivity of the buffers. Sn-doped, 2- μm-thick α-Ga2O3films prepared on this buffer by HVPE showed donor ionization energies of 0.2–0.25 eV, while undoped films were resistive with the Fermi level pinned at ECof 0.3 eV. The I– V and capacitance–voltage ( C– V) characteristics of Ni Schottky diodes on Sn-doped samples using a Cr2O3buffer indicated the presence of two face-to-face junctions, one between n-Ga2O3and p-Cr2O3, the other due to the Ni Schottky diode with n-Ga2O3. The spectral dependence of the photocurrent measured on the structure showed the presence of three major deep traps with optical ionization thresholds near 1.3, 2, and 2.8 eV. Photoinduced current transient spectroscopy spectra of the structures were dominated by deep traps with an ionization energy of 0.95 eV. These experiments suggest another pathway to obtain p–n heterojunctions in the α-Ga2O3system.
-
more » « less
Abstract Reactive ion etching (RIE) used to fabricate high‐aspect‐ratio (HAR) nano/microstructures is known to damage semiconductor surfaces which enhances surface recombination and limits the conversion efficiency of nanostructured solar cells. Here, defect passivation of ultrathin Al2O3‐coated Si micropillars (MPs) using different surface pretreatment steps is reported. Effects on interface state density are quantified by means of electrochemical impedance spectroscopy which is used to extract quantitative capacitance–voltage and conductance–voltage characteristics from HAR dielectric–semiconductor structures which would otherwise suffer from high gate leakage currents if tested using solid‐state metal–insulator–semiconductor structures. High‐temperature thermal oxidation to form a sacrificial oxide on RIE‐fabricated Si MPs, followed by atomic layer deposition of 4 nm thick Al2O3after removal of the sacrificial layer produces an interface trap density (
D it) as low as 1.5 × 1011cm−2eV−1at the mid‐gap energy of silicon. However, a greatly reduced mid‐gapD it(2 × 1011cm−2eV−1) is possible even with a simple air annealing procedure having a maximum temperature of 400 °C.