We report the facile synthesis and 3D printing of a series of triblock copolymers consisting of soft and hard blocks and demonstrate that alkene pendant groups of the hard block can be covalently modified. The polymers are prepared using a salenCo(III)TFA/PPNTFA binary catalyst system and 1,2‐propanediol as a chain transfer agent, providing an efficient one‐pot, two‐step strategy to tailor polymer thermal and mechanical properties. Thixotropic inks suitable for direct ink write printing were formulated by dissolving the block copolymers in organic solvent and dispersing NaCl particles. After printing, porous structures were produced by removing solvent and NaCl with water to give printed structures with surfaces that could be modified via UV‐initiated thiol‐ene click reactions. Alternatively, a tetra‐thiol could be incorporated into the ink and used for cross‐linking to give objects with high solvent resistance and selective degradability.
We report the facile synthesis and 3D printing of a series of triblock copolymers consisting of soft and hard blocks and demonstrate that alkene pendant groups of the hard block can be covalently modified. The polymers are prepared using a salenCo(III)TFA/PPNTFA binary catalyst system and 1,2‐propanediol as a chain transfer agent, providing an efficient one‐pot, two‐step strategy to tailor polymer thermal and mechanical properties. Thixotropic inks suitable for direct ink write printing were formulated by dissolving the block copolymers in organic solvent and dispersing NaCl particles. After printing, porous structures were produced by removing solvent and NaCl with water to give printed structures with surfaces that could be modified via UV‐initiated thiol‐ene click reactions. Alternatively, a tetra‐thiol could be incorporated into the ink and used for cross‐linking to give objects with high solvent resistance and selective degradability.
more » « less- NSF-PAR ID:
- 10370815
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Angewandte Chemie
- Volume:
- 134
- Issue:
- 37
- ISSN:
- 0044-8249
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract Hydrogels hold much promise for 3D printing of functional living materials; however, challenges remain in tailoring mechanical robustness as well as biological performance. In addressing this challenge, the modular synthesis of functional hydrogels from 3‐arm diblock copolypeptide stars composed of an inner poly(
l ‐glutamate) domain and outer poly(l ‐tyrosine) or poly(l ‐valine) blocks is described. Physical crosslinking due to ß‐sheet assembly of these star block copolymers gives mechanical stability during extrusion printing and the selective incorporation of methacrylate units allows for subsequent photocrosslinking to occur under biocompatible conditions. This permits direct ink writing (DIW) printing of bacteria‐based mixtures leading to 3D objects with high fidelity and excellent bacterial viability. The tunable stiffness of different copolypeptide networks enables control over proliferation and colony formation for embeddedEscherichia coli bacteria as demonstrated via isopropyl ß‐d ‐1‐thiogalactopyranoside (IPTG) induction of green fluorescent protein (GFP) expression. This translation of molecular structure to network properties highlights the versatility of these polypeptide hydrogel systems with the combination of writable structures and biological activity illustrating the future potential of these 3D‐printed biocomposites. -
A modular platform for 3D printing fluid-containing structures is reported. Pickering emulsion-templated fluid-filled polymeric capsules were synthesized and incorporated into viscous liquids to produce inks for direct ink writing. Printed objects could be cured by solvent removal or irradiation with ultraviolet light to give monolithic structures containing capsules of fluid, with porosity dependent upon the curing method.more » « less
-
more » « less
Abstract The fabrication of three‐dimensional (3D) scaffolds is indispensable to tissue engineering and 3D printing is emerging as an important approach towards this. Hydrogels are often used as inks in extrusion‐based 3D printing, including with encapsulated cells; however, numerous challenging requirements exist, including appropriate viscosity, the ability to stabilize after extrusion, and cytocompatibility. Here, we present a shear‐thinning and self‐healing hydrogel crosslinked through dynamic covalent chemistry for 3D bioprinting. Specifically, hyaluronic acid was modified with either hydrazide or aldehyde groups and mixed to form hydrogels containing a dynamic hydrazone bond. Due to their shear‐thinning and self‐healing properties, the hydrogels could be extruded for 3D printing of structures with high shape fidelity, stability to relaxation, and cytocompatibility with encapsulated fibroblasts (>80% viability). Forces for extrusion and filament sizes were dependent on parameters such as material concentration and needle gauge. To increase scaffold functionality, a second photocrosslinkable interpenetrating network was included that was used for orthogonal photostiffening and photopatterning through a thiol‐ene reaction. Photostiffening increased the scaffold's modulus (∼300%) while significantly decreasing erosion (∼70%), whereas photopatterning allowed for spatial modification of scaffolds with dyes. Overall, this work introduces a simple approach to both fabricate and modify 3D printed scaffolds. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 865–875, 2018.
-
Facile and large-scale synthesis of well-defined, thermally stable silver nanoparticles protected by polymer brushes for use in practical applications is still a challenge. Recent work has reported a nanoreactor approach that can be used to synthesize these silver nanoparticles. This approach uses amphiphilic star-block copolymers, which have a hydrophilic core surrounded by a hydrophobic exterior. These polymers thus can serve as the nanoreactors. In this study, we hypothesize that the local high concentration of silver ions in the inner hydrophilic cores of these star-block copolymers facilitates the nucleation and subsequent growth of silver nanoparticles. When all silver nanoparticles nucleate from the cores of the star-block copolymers in solution, the particle size can be controlled by the core size of the polymer. To test this hypothesis, a polyisoprene-b-poly(p-tert-butylstyrene) (PI-b-PtBS) star-block copolymer was functionalized with carboxylic acid groups using a high-efficiency, photo-initiated thiol-ene click reaction. We characterized this modified polymer using proton nuclear magnetic resonance spectroscopy, and the results indicated that ~60% of the double bonds in the polyisoprene block were successfully functionalized with carboxylic acid groups. When silver ions were added to a solution of these functionalized star-block copolymers, the negatively charged carboxylic acid groups would attract the positively charged silver ions. Subsequent reduction of these Ag+ by a tert-butylamine-borane complex at room temperature produced nanosized silver particles. However, transmission electron microscopy images showed that a significant amount of relatively large silver nanoparticles grew outside the star-block copolymer nanoreactors.more » « less