skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Ultralight and Flexible Monolithic Polymer Aerogel with Extraordinary Thermal Insulation by A Facile Ambient Process
Abstract High performance thermal insulation materials are desired for a wide range of applications in space, buildings, energy, and environments. Here, a facile ambient processing approach is reported to synthesize a highly insulating and flexible monolithic poly(vinyl chloride) aerogel. The thermal conductivity is measured respectively as 28 mW (m K)−1at atmosphere approaching the air conductivity and 7.7 mW (m K)−1under mild evacuation condition. Thermal modeling is performed to understand the thermal conductivity contributions from different heat transport pathways in air and solid. The analysis based on the Knudsen effect and scattering mean free paths shows that the thermal insulation performance can be further improved through the optimization of porous structures to confine the movement of air molecules. Additionally, the prepared aerogels show superhydrophobicity due to the highly porous structures, which enables new opportunities for surface engineering. Together, the study demonstrates an energy‐saving and scalable ambient‐processing pathway to achieve ultralight, flexible, and superhydrophobic poly(vinyl chloride) aerogel for thermal insulation applications.  more » « less
Award ID(s):
1753393
PAR ID:
10371998
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Materials Interfaces
Volume:
6
Issue:
13
ISSN:
2196-7350
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; (, Journal of Manufacturing Science and Engineering)
    null (Ed.)
    Abstract The conventional manufacturing processes of aerogel insulation material is largely relying on the supercritical drying, which suffers from issues of massive energy consumption, high-cost equipment, and prolonged processing time. With the consideration of large market demand of the aerogel insulation material in the next decade, a low-cost and scalable fabrication technique is highly desired. In this paper, a direct ink writing (DIW) method is used to three-dimensionally fabricate the silica aerogel insulation material, followed by room-temperature and ambient pressure drying. Compared to the supercritical drying and freeze-drying, the reported method significantly reduces the fabrication time and costs. The cost-effective DIW technique offers the capability to print complex hollow internal structures, coupled with the porous structure, is found to be beneficial to the thermal insulation property. The addition of fiber to the ink assures the durability of the fabricated product, without sacrificing the thermal insulation performance. The foam ink preparation methods and the printability are demonstrated in this paper, along with the printing of complex three-dimensional geometries. The thermal insulation performance of the printed objects is characterized, and the mechanical properties are also examined. The proposed approach is found to have 56% reduction in the processing time. The printed silica aerogels exhibit a low thermal conductivity of 0.053 W m−1 K−1. 
    more » « less
  2. ; ; ; ; ; (, RSC Advances)
    Achieving a mesoporous structure in superinsulation materials is pivotal for guaranteeing a harmonious relationship between low thermal conductivity, high porosity, and low density. Herein, we report silica-based cryogel and aerogel materials by implementing freeze-drying and ambient-pressure-drying processes respectively. The obtained freeze-dried cryogels yield thermal conductivity of 23 mW m −1 K −1 , with specific surface area of 369.4 m 2 g −1 , and porosity of 96.7%, whereas ambient-pressure-dried aerogels exhibit thermal conductivity of 23.6 mW m −1 K −1 , specific surface area of 473.8 m 2 g −1 , and porosity of 97.4%. In addition, the fiber-reinforced nanocomposites obtained via freeze-drying feature a low thermal conductivity (28.0 mW m −1 K −1 ) and high mechanical properties (∼620 kPa maximum compressive stress and Young's modulus of 715 kPa), coupled with advanced flame-retardant capabilities, while the composite materials from the ambient pressure drying process have thermal conductivity of 28.8 mW m −1 K −1 , ∼200 kPa maximum compressive stress and Young's modulus of 612 kPa respectively. The aforementioned results highlight the capabilities of both drying processes for the development of thermal insulation materials for energy-efficient applications. 
    more » « less
  3. ; ; ; ; (, Materials advances)
    Flexible thermal insulating membranes are ubiquitous in thermal management. Nevertheless, difficulties arise for composite membranes to combine a resilient, robust structural framework with uniform percolation networks purposefully conceived for thermal insulation. Herein, by controlling the microstructure homogeneity, we report flexible, hydrophobic thermal insulating membranes consisting of ceramic fiber and porous silica materials. The resulting nanofibrous membrane composites exhibit a low thermal insulation of 11.4 mW m−1 K−1, a low density of 0.245 g cm−3, mechanical flexibility with a bending rigidity of 1.25 cN mm−1, and hydrophobicity with a water contact angle of 144°. These nanofibrous-reinforced, silica-aerogel-based nanocomposite membranes are potential candidates for advanced thermal management applications. 
    more » « less
  4. ; ; ; ; ; (, ASME 2020 15th International Manufacturing Science and Engineering Conference)
    null (Ed.)
    Abstract The conventional manufacturing process of aerogel insulation material relies largely on the supercritical drying, which suffers from issues of massive energy consumption, high-cost equipment and prolonged processing time. With the consideration of large market demand of the aerogel insulation material in the next decade, a low-cost and scalable fabrication technique is highly desired. In this paper, a direct ink writing (DIW) method is used to three-dimensionally fabricate the silica aerogel insulation material, followed by room-temperature and ambient pressure drying. Compared to the supercritical drying and freeze-drying, the reported method significantly reduces the fabrication time and costs. The cost-effective DIW technique offers the capability to print complex hollow internal structures, coupled with the porous structure, is found to be beneficial to the thermal insulation property. The addition of fiber to the ink assures the durability of the fabricated product. The foam ink preparation methods and the printability are demonstrated in this paper, along with the printed samples for characterizing thermal insulation performance and mechanical properties. 
    more » « less
  5. ; ; ; ; ; ; ; ; ; ; et al (, Advanced Materials)
    Abstract The realization of low thermal conductivity at high temperatures (0.11 W m−1K−1800 °C) in ambient air in a porous solid thermal insulation material, using stable packed nanoparticles of high‐entropy spinel oxide with 8 cations (HESO‐8 NPs) with a relatively high packing density of ≈50%, is reported. The high‐density HESO‐8 NP pellets possess around 1000‐fold lower thermal diffusivity than that of air, resulting in much slower heat propagation when subjected to a transient heat flux. The low thermal conductivity and diffusivity are realized by suppressing all three modes of heat transfer, namely solid conduction, gas conduction, and thermal radiation, via stable nanoconstriction and infrared‐absorbing nature of the HESO‐8 NPs, which are enabled by remarkable microstructural stability against coarsening at high temperatures due to the high entropy. This work can elucidate the design of the next‐generation high‐temperature thermal insulation materials using high‐entropy ceramic nanostructures. 