Using molten‐salt synthetic techniques, NaNbO3(Space group
Titanium dioxide is a photocatalyst, known not only for its ability to oxidize organic contaminants, but also for its antimicrobial properties. In this article, significant enhancement of the antimicrobial activity of TiO2(up to 32 times) was demonstrated after its activation by ball milling. The antimicrobial activity was analyzed for one fungal and 13 bacterial ATCC strains using the microdilution method and recording the minimum inhibitory concentration (MIC) values. In order to further investigate the correlation between the mechanical activation of TiO2and its antimicrobial activity, the structure, morphology and phase composition of the material were studied by means of Electron Microscopy, X‐ray diffraction and nitrogen adsorption‐desorption measurements. UV‐Vis diffuse reflectance spectra were recorded and the Kubelka‐Munk function was applied to convert reflectance into the equivalent band gap energy (
- Award ID(s):
- 1829245
- NSF-PAR ID:
- 10374395
- Publisher / Repository:
- Wiley-Blackwell
- Date Published:
- Journal Name:
- Journal of the American Ceramic Society
- Volume:
- 102
- Issue:
- 12
- ISSN:
- 0002-7820
- Page Range / eLocation ID:
- p. 7735-7745
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract Pbcm ; No. 57) was prepared in high purity at a reaction time of 12 hours and a temperature of 900°C. All NaNbO3products were prepared from stoichiometric ratios of Nb2O5and Na2CO3together with the addition of a salt flux introduced at a 10:1 molar ratio of salt to NaNbO3, that is, using the Na2SO4, NaF, NaCl, and NaBr salts. A solid‐state synthesis was performed in the absence of a molten salt to serve as a control. The reaction products were all found to be phase pure through powder X‐ray diffraction, for example, with refined lattice constants ofa = 5.512(5) Å,b = 5.567(3) Å, andc = 15.516(8) Å from the Na2SO4salt reaction. The products were characterized using UV‐Vis diffuse reflectance spectroscopy to have a bandgap size of ~3.5 eV. The particles sizes were analyzed by scanning electron microscopy (SEM) and found to be dependent upon the flux type used, from ~<1 μm to >10 μm in length, with overall surface areas that could be varied from 0.66 m2/g (for NaF) to 1.55 m2/g (for NaBr). Cubic‐shaped particle morphologies were observed for the metal halide salts with the set of exposed (100)/(010)/(001) crystal facets, while a truncated octahedral morphology formed in the sodium sulfate salt reaction with predominantly the set of (110)/(101)/(011) crystal facets. The products were found to be photocatalytically active for hydrogen production under UV‐Vis irradiation, with the aid of a 1 wt% Pt surface cocatalyst. The platinized NaNbO3particles were suspended in an aqueous 20% methanol solution and irradiated by UV‐Vis light (λ > 230 nm). After 6 hours of irradiation, the average total hydrogen production varied with the particle morphologies and sizes, with 753 µmol for Na2SO4, 334 µmol for NaF, 290 µmol for NaCl, 81 µmol for NaBr, and 249 µmol for the solid‐state synthesized NaNbO3. These trends show a clear relationship to particle sizes, with smaller particles showing higher photocatalytic activity in the order of NaF > NaCl > NaBr. Furthermore, the particle morphologies obtained from the Na2SO4flux showed even higher photocatalytic activity, though having a relatively similar overall surface area, owing to the higher activity of the (110) crystal facets. The apparent quantum yield (100 mW/cm2,λ = 230 to 350 nm, pH = 7) was measured to be 3.7% for NaNbO3prepared using the NaF flux, but this was doubled to 6.8% when prepared using the Na2SO4flux. Thus, these results demonstrate the powerful utility of flux synthetic techniques to control particle sizes and to expose higher‐activity crystal facets to boost their photocatalytic activities for molecular hydrogen production. -
more » « less
Abstract Block copolymers (BCPs) have received significant attention as promising candidates for sequestering nanoparticles and fabrication of aligned nanostructures with optimal optical or electrical properties. We investigate the influence of static and dynamic thermal field on the alignment of polystyrene‐
block ‐poly(methyl methacrylate) (PS‐b ‐PMMA) BCP morphology with the loading of novel poly(methyl methacrylate‐block ‐Polystyrene) (PMMA‐b ‐PS)‐grafted‐TiO2nanoparticles (BCP‐g‐TiO2). Observation of characteristics IR peaks for PMMA and PS in BCP‐g‐TiO2nanoparticles and Transmission Electron Microscopy (TEM) results of the outer coating of core nanoparticle, validate the grafting to approach in synthesizing BCP‐g‐TiO2. Here we report that under the sharp dynamic thermal field, at low loading of BCP‐g‐TiO2, there is good dispersion of nanoparticles in unidirectionally aligned BCP matrix in film interior probed by GISAXS, while, at high nanoparticle loading (~10 wt%), there is local frustration in the unidirectional alignment of the BCP matrix due to aggregation of BCP‐g‐TiO2nanoparticles. However, Grazing incidence small angle X‐ray scattering (GISAXS) shows clearly that the BCP films remain largely locally ordered at the domain scale, despite these large perturbations to long‐range ordering even at high loading level, while bringing in new TiO2functionality to the BCP films, such as UVO absorptivity or biofouling prevention, important to potential new applications of such membranes. -
more » « less
Abstract Large separation of magnetic levels and slow relaxation in metal complexes are desirable properties of single‐molecule magnets (SMMs). Spin‐phonon coupling (interactions of magnetic levels with phonons) is ubiquitous, leading to magnetic relaxation and loss of memory in SMMs and quantum coherence in qubits. Direct observation of magnetic transitions and spin‐phonon coupling in molecules is challenging. We have found that far‐IR magnetic spectra (FIRMS) of Co(PPh3)2X2(
Co‐X ; X=Cl, Br, I) reveal rarely observed spin‐phonon coupling as avoided crossings between magnetic andu ‐symmetry phonon transitions. Inelastic neutron scattering (INS) gives phonon spectra. Calculations using VASP and phonopy programs gave phonon symmetries and movies. Magnetic transitions among zero‐field split (ZFS) levels of theS =3/2 electronic ground state were probed by INS, high‐frequency and ‐field EPR (HFEPR), FIRMS, and frequency‐domain FT terahertz EPR (FD‐FT THz‐EPR), giving magnetic excitation spectra and determining ZFS parameters (D, E ) andg values. Ligand‐field theory (LFT) was used to analyze earlier electronic absorption spectra and give calculated ZFS parameters matching those from the experiments. DFT calculations also gave spin densities inCo‐X , showing that the larger Co(II) spin density in a molecule, the larger its ZFS magnitude. The current work reveals dynamics of magnetic and phonon excitations in SMMs. Studies of such couplings in the future would help to understand how spin‐phonon coupling may lead to magnetic relaxation and develop guidance to control such coupling. -
more » « less
Abstract Almahata Sitta (AhS), an anomalous polymict ureilite, is the first meteorite observed to originate from a spectrally classified asteroid (2008
TC 3). However, correlating properties of the meteorite with those of the asteroid is not straightforward because the AhS stones are diverse types. Of those studied prior to this work, 70–80% are ureilites (achondrites) and 20–30% are various types of chondrites. Asteroid 2008TC 3was a heterogeneous breccia that disintegrated in the atmosphere, with its clasts landing on Earth as individual stones and most of its mass lost. We describe AhS 91A and AhS 671, which are the first AhS stones to show contacts between ureilitic and chondritic materials and provide direct information about the structure and composition of asteroid 2008TC 3. AhS 91A and AhS 671 are friable breccias, consisting of a C1 lithology that encloses rounded to angular clasts (<10 μm to 3 mm) of olivine, pyroxenes, plagioclase, graphite, and metal‐sulfide, as well as chondrules (~130–600 μm) and chondrule fragments. The C1 material consists of fine‐grained phyllosilicates (serpentine and saponite) and amorphous material, magnetite, breunnerite, dolomite, fayalitic olivine (Fo 28‐42), an unidentified Ca‐rich silicate phase, Fe,Ni sulfides, and minor Ca‐phosphate and ilmenite. It has similarities toCI 1 but shows evidence of heterogeneous thermal metamorphism. Its bulk oxygen isotope composition (δ18O = 13.53‰, δ17O = 8.93‰) is unlike that of any known chondrite, but similar to compositions of severalCC ‐like clasts in typical polymict ureilites. Its Cr isotope composition is unlike that of any known meteorite. The enclosed clasts and chondrules do not belong to the C1 lithology. The olivine (Fo 75‐88), pyroxenes (pigeonite of Wo ~10 and orthopyroxene of Wo ~4.6), plagioclase, graphite, and some metal‐sulfide are ureilitic, based on mineral compositions, textures, and oxygen isotope compositions, and represent at least six distinct ureilitic lithologies. The chondrules are probably derived from type 3OC and/orCC , based on mineral and oxygen isotope compositions. Some of the metal‐sulfide clasts are derived fromEC . AhS 91A and AhS 671 are plausible representatives of the bulk of the asteroid that was lost. Reflectance spectra of AhS 91A are dark (reflectance ~0.04–0.05) and relatively featureless inVNIR , and have an ~2.7 μm absorption band due toOH −in phyllosilicates. Spectral modeling, using mixtures of laboratoryVNIR reflectance spectra of AhS stones to fit the F‐type spectrum of the asteroid, suggests that 2008TC 3consisted mainly of ureilitic and AhS 91A‐like materials, with as much as 40–70% of the latter, and <10% ofOC ,EC , and other meteorite types. The bulk density of AhS 91A (2.35 ± 0.05 g cm−3) is lower than bulk densities of other AhS stones, and closer to estimates for the asteroid (~1.7–2.2 g cm−3). Its porosity (36%) is near the low end of estimates for the asteroid (33–50%), suggesting significant macroporosity. The textures of AhS 91A and AhS 671 (finely comminuted clasts of disparate materials intimately mixed) support formation of 2008TC 3in a regolith environment. AhS 91A and AhS 671 could represent a volume of regolith formed when aCC ‐like body impacted into already well‐gardened ureilitic + impactor‐derived debris. AhS 91A bulk samples do not show a solar wind component, so they represent subsurface layers. AhS 91A has a lower cosmic ray exposure (CRE ) age (~5–9 Ma) than previously studied AhS stones (11–22 Ma). The spread inCRE ages argues for irradiation in a regolith environment. AhS 91A and AhS 671 show that ureilitic asteroids could have detectable ~2.7 μm absorption bands. -
more » « less
Abstract Titanium dioxide (TiO2) is a promising electrode material for reversible lithium storage. However, the poor electronic conductivity, sluggish diffusivity, and intrinsic kinetics limit hinder its fast lithium storage capability. Here we present that the oxygen‐deficient TiO2hierarchical spheres can address the issues for high capacity, long‐term lithium‐ion battery anode. First‐principles calculations show that introducing oxygen vacancies to anatase TiO2can reduce the bandgap, thus improving the electronic conductivity and further the lithium storage properties of TiO2. By annealing TiO2/H2Ti5O11⋅3H2O hierarchical spheres precursor in nitrogen, accompanying with the phase transfer process, the growth of TiO2crystallites is restricted due to the generation of residual carbon species, resulting in a well maintained hierarchical spherical structure. Rich oxygen vacancies are generated in the oxygen‐deficient environment and evidenced by EPR, XPS, and UV‐Vis spectra, which enable the TiO2hierarchical spheres reduced bandgap. The oxygen vacancies in the as‐obtained TiO2hierarchical spheres together with the high structural integrity of the hierarchical spheres gives rise to superior lithium storage properties including a high specific capacity of 282 mAh g−1at 200 mA g−1, and long‐term cycling stability with a capacity retention of 85.2 % at 4 A g−1over 10000 cycles.