Resonant tunneling diodes (RTDs) have come full-circle in the past 10 years after their demonstration in the early 1990s
as the fastest room-temperature semiconductor oscillator, displaying experimental results up to 712 GHz and fmax values
exceeding 1.0 THz [1]. Now the RTD is once again the preeminent electronic oscillator above 1.0 THz and is being
implemented as a coherent source [2] and a self-oscillating mixer [3], amongst other applications. This paper concerns
RTD electroluminescence – an effect that has been studied very little in the past 30+ years of RTD development, and not
at room temperature. We present experiments and modeling of an n-type In0.53Ga0.47As/AlAs double-barrier RTD
operating as a cross-gap light emitter at ~300K. The MBE-growth stack is shown in Fig. 1(a). A 15-μm-diam-mesa
device was defined by standard planar processing including a top annular ohmic contact with a 5-μm-diam pinhole in the
center to couple out enough of the internal emission for accurate free-space power measurements [4]. The emission spectra
have the behavior displayed in Fig. 1(b), parameterized by bias voltage (VB). The long wavelength emission edge is at
= 1684 nm - close to the In0.53Ga0.47As bandgap energy of Ug ≈ 0.75 eV at 300 K. The spectral peaks for VB = 2.8 and
3.0 V both occur around = 1550 nm (h = 0.75 eV), so blue-shifted relative to the peak of the “ideal”, bulk InGaAs
emission spectrum shown in Fig. 1(b) [5]. These results are consistent with the model displayed in Fig. 1(c), whereby
the broad emission peak is attributed to the radiative recombination between electrons accumulated on the emitter side,
and holes generated on the emitter side by interband tunneling with current density Jinter. The blue-shifted main peak is
attributed to the quantum-size effect on the emitter side, which creates a radiative recombination rate RN,2 comparable to
the band-edge cross-gap rate RN,1. Further support for this model is provided by the shorter wavelength and weaker
emission peak shown in Fig. 1(b) around = 1148 nm. Our quantum mechanical calculations attribute this to radiative
recombination RR,3 in the RTD quantum well between the electron ground-state level E1,e, and the hole level E1,h.
To further test the model and estimate quantum efficiencies, we conducted optical power measurements using a
large-area Ge photodiode located ≈3 mm away from the RTD pinhole, and having spectral response between 800 and
1800 nm with a peak responsivity of ≈0.85 A/W at =1550 nm. Simultaneous I-V and L-V plots were obtained and
are plotted in Fig. 2(a) with positive bias on the top contact (emitter on the bottom). The I-V curve displays a pronounced
NDR region having a current peak-to-valley current ratio of 10.7 (typical for In0.53Ga0.47As RTDs). The external quantum
efficiency (EQE) was calculated from EQE = e∙IP/(∙IE∙h) where IP is the photodiode dc current and IE the RTD current.
The plot of EQE is shown in Fig. 2(b) where we see a very rapid rise with VB, but a maximum value (at VB= 3.0 V) of
only ≈2×10-5. To extract the internal quantum efficiency (IQE), we use the expression EQE= c ∙i ∙r ≡ c∙IQE where
ci, and r are the optical-coupling, electrical-injection, and radiative recombination efficiencies, respectively [6]. Our
separate optical calculations yield c≈3.4×10-4 (limited primarily by the small pinhole) from which we obtain the curve
of IQE plotted in Fig. 2(b) (right-hand scale). The maximum value of IQE (again at VB = 3.0 V) is 6.0%. From the implicit
definition of IQE in terms of i and r given above, and the fact that the recombination efficiency in In0.53Ga0.47As is
likely limited by Auger scattering, this result for IQE suggests that i might be significantly high.
To estimate i, we have used the experimental total current of Fig. 2(a), the Kane two-band model of interband
tunneling [7] computed in conjunction with a solution to Poisson’s equation across the entire structure, and a rate-equation
model of Auger recombination on the emitter side [6] assuming a free-electron density of 2×1018 cm3. We focus on the
high-bias regime above VB = 2.5 V of Fig. 2(a) where most of the interband tunneling should occur in the depletion region
on the collector side [Jinter,2 in Fig. 1(c)]. And because of the high-quality of the InGaAs/AlAs heterostructure (very few
traps or deep levels), most of the holes should reach the emitter side by some combination of drift, diffusion, and tunneling
through the valence-band double barriers (Type-I offset) between InGaAs and AlAs. The computed interband current
density Jinter is shown in Fig. 3(a) along with the total current density Jtot. At the maximum Jinter (at VB=3.0 V) of 7.4×102
A/cm2, we get i = Jinter/Jtot = 0.18, which is surprisingly high considering there is no p-type doping in the device. When
combined with the Auger-limited r of 0.41 and c ≈ 3.4×10-4, we find a model value of IQE = 7.4% in good agreement
with experiment. This leads to the model values for EQE plotted in Fig. 2(b) - also in good agreement with experiment.
Finally, we address the high Jinter and consider a possible universal nature of the light-emission mechanism. Fig.
3(b) shows the tunneling probability T according to the Kane two-band model in the three materials, In0.53Ga0.47As, GaAs,
and GaN, following our observation of a similar electroluminescence mechanism in GaN/AlN RTDs (due to strong
polarization field of wurtzite structures) [8]. The expression is Tinter = (2/9)∙exp[(-2 ∙Ug
2 ∙me)/(2h∙P∙E)], where Ug is the
bandgap energy, P is the valence-to-conduction-band momentum matrix element, and E is the electric field. Values for
the highest calculated internal E fields for the InGaAs and GaN are also shown, indicating that Tinter in those structures
approaches values of ~10-5. As shown, a GaAs RTD would require an internal field of ~6×105 V/cm, which is rarely
realized in standard GaAs RTDs, perhaps explaining why there have been few if any reports of room-temperature
electroluminescence in the GaAs devices.
[1] E.R. Brown,et al., Appl. Phys. Lett., vol. 58, 2291, 1991. [5] S. Sze, Physics of Semiconductor Devices, 2nd Ed. 12.2.1 (Wiley, 1981).
[2] M. Feiginov et al., Appl. Phys. Lett., 99, 233506, 2011. [6] L. Coldren, Diode Lasers and Photonic Integrated Circuits, (Wiley, 1995).
[3] Y. Nishida et al., Nature Sci. Reports, 9, 18125, 2019. [7] E.O. Kane, J. of Appl. Phy 32, 83 (1961).
[4] P. Fakhimi, et al., 2019 DRC Conference Digest. [8] T. Growden, et al., Nature Light: Science & Applications 7, 17150 (2018).
[5] S. Sze, Physics of Semiconductor Devices, 2nd Ed. 12.2.1 (Wiley, 1981).
[6] L. Coldren, Diode Lasers and Photonic Integrated Circuits, (Wiley, 1995).
[7] E.O. Kane, J. of Appl. Phy 32, 83 (1961).
[8] T. Growden, et al., Nature Light: Science & Applications 7, 17150 (2018).
more »
« less
Resonant Tunneling and Negative Differential Resistance in Black Phosphorus Vertical Heterostructures
Resonant tunneling diodes with negative differential resistance (NDR) have attracted significant attention due to their unique quantum resonant tunneling phenomena and potential applications in terahertz emission/detection and high‐density logic/memory. In this paper, resonant tunneling devices, where the carriers tunnel through a hexagonal boron nitride (hBN) barrier sandwiched by two black phosphorus (BP) layers, are explored. The resonance occurs when the energy bands of the two black phosphorus layers are aligned. The conductive atomic force microscopy (CAFM) measurements reveal prominent NDR peaks with large peak‐to‐valley ratios at room temperature. It is found that the positions of the NDR peaks are very sensitive to the amplitude and the shape of the voltage waveform used in CAFM, which can be explained by the charge trapping effect. Furthermore, resonant tunneling transistors are demonstrated based on BP/hBN/BP stacks in which the locations of the NDR peaks are tunable by the electrostatic gating. As compared to the traditional tunneling diodes based on bulk materials, the tunneling devices based on thin boron nitride tunneling barrier and high mobility black phosphorus offer ultra‐high‐speed response. This feature, together with the NDR characteristics, provides the potential for applications in THz oscillators and multi‐value logic devices.
more » « less- Award ID(s):
- 1653241
- NSF-PAR ID:
- 10378501
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Electronic Materials
- Volume:
- 6
- Issue:
- 8
- ISSN:
- 2199-160X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
more » « less
Abstract Black phosphorus (BP) has recently attracted significant attention due to its exceptional physical properties. Currently, high‐quality few‐layer and thin‐film BP are produced primarily by mechanical exfoliation, limiting their potential in future applications. Here, the synthesis of highly crystalline thin‐film BP on 5 mm sapphire substrates by conversion from red to black phosphorus at 700 °C and 1.5 GPa is demonstrated. The synthesized ≈50 nm thick BP thin films are polycrystalline with a crystal domain size ranging from 40 to 70 µm long, as indicated by Raman mapping and infrared extinction spectroscopy. At room temperature, field‐effect mobility of the synthesized BP thin film is found to be around 160 cm2V−1s−1along armchair direction and reaches up to about 200 cm2V−1s−1at around 90 K. Moreover, red phosphorus (RP) covered by exfoliated hexagonal boron nitride (hBN) before conversion shows atomically sharp hBN/BP interface and perfectly layered BP after the conversion. This demonstration represents a critical step toward the future realization of large scale, high‐quality BP devices and circuits.
-
IEEE (Ed.)In this project, Hall bar devices with black phosphorus (BP) as the semiconductor layer were fabricated to measure the Hall mobility and carrier density of exfoliated BP flakes obtained from bulk crystals acquired from various commercial sources. Black phosphorus is proposed as an alternative material for terahertz photoconductive antennas (PCAs) from the standard GaAs or InGaAs PCAs that are currently available commercially. Black phosphorus is an anisotropic material with a reported Hall mobility over three times greater than GaAs, but our preliminary testing of BP PCAs has shown dramatic differences of electrical properties between black phosphorus sourced from three different vendors. To determine the best quality black phosphorus source, Hall bar devices containing 40 nm BP flakes were used to measure the carrier mobility of the semiconductor. A Hall bar device is created by layering a 40nm BP flake underneath a hexagonal boron-nitride (hBN) flake, all on top of gold contacts in a Hall bar arrangement fabricated on a high-resistivity silicon substrate. The hBN acts as a passivation layer for the BP so that it may be safely removed from the glove box without damage. The Hall mobility of the material from different sources ranges from around 100 cm2/Vs to 1600 cm2/Vs, with only one source showing promising, high mobility results. This study allows BP with optimized electrical properties to be incorporated into THz PCAs for characterization via THz time domain spectroscopy.more » « less
-
more » « less
Abstract Recently, 2D electron gases have been observed in atomically thin semiconducting crystals, enabling the observation of rich physical phenomena at the quantum level within the ultimate thickness limit. However, the observation of 2D electron gases and subsequent quantum Hall effect require exceptionally high crystalline quality, rendering mechanical exfoliation as the only method to produce high‐quality 2D semiconductors of black phosphorus and indium selenide (InSe), which hinder large‐scale device applications. Here, the controlled one‐step synthesis of high‐quality 2D InSe thin films via chemical vapor transport method is reported. The carrier Hall mobility of hexagonal boron nitride (hBN) encapsulated InSe flakes can be up to 5000 cm2V−1s−1at 1.5 K, enabling to observe the quantum Hall effect in a synthesized van der Waals semiconductor. The existence of the quantum Hall effect in directly synthesized 2D semiconductors indicates a high quality of the chemically synthesized 2D semiconductors, which hold promise in quantum devices and applications with high mobility.
-
more » « less
Abstract While hexagonal boron nitride (hBN) has been widely used as a buffer or encapsulation layer for emerging electronic devices, interest in utilizing it for large‐area chemical barrier coating has somewhat faded. A chemical vapor deposition process is reported here for the conformal growth of hBN on large surfaces of various alloys and steels, regardless of their complex shapes. In contrast to the previously reported very limited protection by hBN against corrosion and oxidation, protection of steels against 10% HCl and oxidation resistance at 850 °C in air is demonstrated. Furthermore, an order of magnitude reduction in the friction coefficient of the hBN coated steels is shown. The growth mechanism is revealed in experiments on thin metal films, where the tunable growth of single‐crystal hBN with a selected number of layers is demonstrated. The key distinction of the process is the use of N2gas, which gets activated exclusively on the catalyst's surface and eliminates adverse gas‐phase reactions. This rate‐limiting step allowed independent control of activated nitrogen along with boron coming from a solid source (like elemental boron). Using abundant and benign precursors, this approach can be readily adopted for large‐scale hBN synthesis in applications where cost, production volume, and process safety are essential.