Abstract The removal of lead from commercialized perovskite‐oxide‐based piezoceramics has been a recent major topic in materials research owing to legislation in many countries. In this regard, Sn(II)‐perovskite oxides have garnered keen interest due to their predicted large spontaneous electric polarizations and isoelectronic nature for substitution of Pb(II) cations. However, they have not been considered synthesizable owing to their high metastability. Herein, the perovskite lead hafnate, i.e., PbHfO3in space groupPbam, is shown to react with SnClF at a low temperature of 300 °C, and resulting in the first complete Sn(II)‐for‐Pb(II) substitution, i.e. SnHfO3. During this topotactic transformation, a high purity and crystallinity is conserved withPbamsymmetry, as confirmed by X‐ray and electron diffraction, elemental analysis, and119Sn Mössbauer spectroscopy. In situ diffraction shows SnHfO3also possesses reversible phase transformations and is potentially polar between ≈130–200 °C. This so‐called ‘de‐leadification’ is thus shown to represent a highly useful strategy to fully remove lead from perovskite‐oxide‐based piezoceramics and opening the door to new explorations of polar and antipolar Sn(II)‐oxide materials.
more »
« less
Circumventing thermodynamics to synthesize highly metastable perovskites: nano eggshells of SnHfO3
Sn(II)-based perovskite oxides, being the subject of longstanding theoretical interest for the past two decades, have been synthesized for the first time in the form of nano eggshell particle morphologies. All past reported synthetic attempts have been unsuccessful owing to their metastable nature, i.e. , by their thermodynamic instability towards decomposition to their constituent oxides. A new approach was discovered that finally provides an effective solution to surmounting this intractable synthetic barrier and which can be the key to unlocking the door to many other predicted metastable oxides. A low-melting KSn2Cl5 salt was utilized to achieve a soft topotactic exchange of Sn(II) cations into a Ba-containing perovskite, i.e., BaHfO3 with particle sizes of ∼350 nm, at a low reaction temperature of 200 °C. The resulting particles exhibit nanoshell-over-nanoshell morphologies, i.e., with SnHfO3 forming as ∼20 nm thick shells over the surfaces of the BaHfO3 eggshell particles. Formation of the metastable SnHfO3 is found to be thermodynamically driven by the co-production of the highly stable BaCl2 and KCl side products. Despite this, total energy calculations show that Sn(II) distorts from the A-site asymmetrically and randomly and the interdiffusion has a negligible impact on the energy of the system (i.e., layered vs. solid solution). Additionally, nano eggshell particle morphologies of BaHfO3 were found to yield highly pure SnHfO3 for the first time, thus circumventing the intrinsic ion-diffusion limits occurring at this low reaction temperature. In summary, these results demonstrate that the metastability of many theoretically predicted Sn(II)-perovskites can be overcome by leveraging the high cohesive energies of the reactants, the exothermic formation of a stable salt side product, and a shortened diffusion pathway for the Sn(II) cations.
more »
« less
- Award ID(s):
- 2004455
- PAR ID:
- 10380182
- Date Published:
- Journal Name:
- Nanoscale Advances
- ISSN:
- 2516-0230
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Recently, many new, complex, functional oxides have been discovered with the surprising use of topotactic ion‐exchange reactions on close‐packed structures, such as found for wurtzite, rutile, perovskite, and other structure types. Despite a lack of apparent cation‐diffusion pathways in these structure types, synthetic low‐temperature transformations are possible with the interdiffusion and exchange of functional cations possessing ns2stereoactive lone pairs (e. g., Sn(II)) or unpaired ndxelectrons (e. g., Co(II)), targeting new and favorable modulations of their electronic, magnetic, or catalytic properties. This enables a synergistic blending of new functionality to an underlying three‐dimensional connectivity, i. e., [‐M−O‐M‐O‐]n, that is maintained during the transformation. In many cases, this tactic represents the only known pathway to prepare thermodynamically unstable solids that otherwise would commonly decompose by phase segregation, such as that recently applied to the discovery of many new small bandgap semiconductors.more » « less
-
Traditional synthetic efforts to prepare Eu(II)-containing oxides have principally involved the use of high temperature reactions starting from EuO or a controlled, highly-reducing, atmosphere. Conversely, chimie douce approaches that are more amenable to the targeted syntheses of new, and potentially metastable, Eu(II)-oxides have yet to be explored. Herein, a cation-exchange route to new Eu(II)-containing oxides, e.g., EuTa4-xO11 (x = 0.04), has been discovered and its structure determined by powder X-ray diffraction (Space group P6322 (#182), a = 6.2539(2) Å; c = 12.3417(2) Å). The compound derives from the cation exchange of Na2Ta4O11, via a reaction with EuBr2 at 1173 K, and replacement by half the number of divalent Eu cations. Rietveld refinements show preferential ordering of the Eu cations over one of the two possible cation sites, i.e., Wyckoff site 2d (~94%; Eu1) versus 2b (~6%; Eu2). Total energy calculations confirm an energetic preference of the Eu cation in the 2d site. Tantalum vacancies of ~1% occur within the layer of Eu cations and TaO6 octahedra, and ~20% partial oxidation of Eu(II) to Eu(III) cations from charge balance considerations. 151Eu M¨ossbauer spectroscopy measured at 78 K found a Eu(II):Eu(III) ratio of 69:31, with a relatively broad line width of the former signal of Γ = 7.6(2) mm s–1. Also, the temperature-dependent magnetic susceptibility could be fitted to a Curie Weiss expression, giving a μeff = 6.2 μB and θCW = 10 K and confirming a mixture of Eu(II)/Eu(III) cations. The optical bandgap of EuTa4-xO11 was found to be ~1.5 eV (indirect), significantly redshifted as compared to ~4.1 eV for Na2Ta4O11. Spin-polarized electronic structure calculations show that this redshift stems from the addition of Eu 4f7 states as a higher-energy valence band. Thus, these results demonstrate a new cation-exchange approach that represents a useful synthetic pathway to new Eu(II)-containing ox- ides for tunable magnetic and optical properties.more » « less
-
Metastable phases of the photoswitchable molecular magnet K0.3Co[Fe(CN)6]0.77 ⋅ nH2O in sub-micrometer particles have been structurally investigated by synchrotron powder x-ray diffraction (PXRD) measurements. The K0.3Co[Fe(CN)6]0.77 ⋅ nH2O bulk compound (studied here with a sample having average particle size of 500 nm) undergoes a charge transfer coupled spin transition (CTCST), where spin configurations change between a paramagnetic CoII( S = 3/2) –FeIII( S = 1/2) high-temperature (HT) state and a diamagnetic CoIII( S = 0) –FeII( S = 0) low-temperature (LT) state. The bulk compound exhibits a unique intermediate (IM) phase, which corresponds to a mixture of HT and LT spin states that depend on the cooling rate. Several hidden metastable HT states emerge as a function of thermal and photo stimuli, namely: (1) a quench (Q) state generated from the HT state by flash cooling, (2) a LTPX state obtained by photoexcitation from the LT state derived by thermal relaxation from the Q state, and (3) an IMPX state accessed by photo-irradiation from the IM state. A sample with a smaller particle size, 135 nm, is investigated for which the particles are on the scale of the coherent LT domains in the IM phase within the larger 500 nm sample. PXRD studies under controlled thermal and/or optical excitations have clarified that the reduction of the particle size profoundly affects the structural changes associated with the CTCST. The unusual IM state is also observed as segregated domains in the 135 nm particle, but the collective structural transformations are more hindered in small particles. The volume change decreases to 2%–3%, almost half the value found for 500 nm particles (5%–8%), even though the linear thermal expansion coefficients are larger for the smaller particles. Furthermore, photoexcitation from the IM and LT states does not turn into single phases in the smaller particles, presumably because of the multiple interfaces and/or internal stress generated by the coexistence of small CoII–FeIIIand CoIII–FeIIdomains in the lattice. Since the reduced particle size limits cooperativity and domain growth in the lattice, CTCST in the small particle sample becomes less sensitive to external stimuli.more » « less
-
Sn‐based perovskites are promising Pb‐free photovoltaic materials with an ideal 1.3 eV bandgap. However, to date, Sn‐based thin film perovskite solar cells have yielded relatively low power conversion efficiencies (PCEs). This is traced to their poor photophysical properties (i.e., short diffusion lengths (<30 nm) and two orders of magnitude higher defect densities) than Pb‐based systems. Herein, it is revealed that melt‐synthesized cesium tin iodide (CsSnI3) ingots containing high‐quality large single crystal (SC) grains transcend these fundamental limitations. Through detailed optical spectroscopy, their inherently superior properties are uncovered, with bulk carrier lifetimes reaching 6.6 ns, doping concentrations of around 4.5 × 1017cm−3, and minority‐carrier diffusion lengths approaching 1 µm, as compared to their polycrystalline counterparts having ≈54 ps, ≈9.2 × 1018cm−3, and ≈16 nm, respectively. CsSnI3SCs also exhibit very low surface recombination velocity of ≈2 × 103cm s−1, similar to Pb‐based perovskites. Importantly, these key parameters are comparable to high‐performance p‐type photovoltaic materials (e.g., InP crystals). The findings predict a PCE of ≈23% for optimized CsSnI3SCs solar cells, highlighting their great potential.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/D2NA00603K