skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Electrical discharge triggers quasicrystal formation in an eolian dune
We report the discovery of a dodecagonal quasicrystal Mn 72.3 Si 15.6 Cr 9.7 Al 1.8 Ni 0.6 —composed of a periodic stacking of atomic planes with quasiperiodic translational order and 12-fold symmetry along the two directions perpendicular to the planes—accidentally formed by an electrical discharge event in an eolian dune in the Sand Hills near Hyannis, Nebraska, United States. The quasicrystal, coexisting with a cubic crystalline phase with composition Mn 68.9 Si 19.9 Ni 7.6 Cr 2.2 Al 1.4 , was found in a fulgurite consisting predominantly of fused and melted sand along with traces of melted conductor metal from a nearby downed power line. The fulgurite may have been created by a lightning strike that combined sand with material from downed power line or from electrical discharges from the downed power line alone. Extreme temperatures of at least 1,710 °C were reached, as indicated by the presence of SiO 2 glass in the sample. The dodecagonal quasicrystal is an example of a quasicrystal of any kind formed by electrical discharge, suggesting other places to search for quasicrystals on Earth or in space and for synthesizing them in the laboratory.  more » « less
Award ID(s):
1725349
PAR ID:
10388022
Author(s) / Creator(s):
; ; ; ; ; ; ;
Date Published:
Journal Name:
Proceedings of the National Academy of Sciences
Volume:
120
Issue:
1
ISSN:
0027-8424
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; (, IUCrJ)
    Icosahedral quasicrystals (i-phases) in the Al–Cu–Fe system are of great interest because of their perfect quasicrystalline structure and natural occurrences in the Khatyrka meteorite. The natural quasicrystal of composition Al 62 Cu 31 Fe 7 , referred to as i-phase II, is unique because it deviates significantly from the stability field of i-phase and has not been synthesized in a laboratory setting to date. Synthetic i-phases formed in shock-recovery experiments present a novel strategy for exploring the stability of new quasicrystal compositions and prove the impact origin of natural quasicrystals. In this study, an Al–Cu–W graded density impactor (GDI, originally manufactured as a ramp-generating impactor but here used as a target) disk was shocked to sample a full range of Al/Cu starting ratios in an Fe-bearing 304 stainless-steel target chamber. In a strongly deformed region of the recovered sample, reactions between the GDI and the steel produced an assemblage of co-existing Al 61.5 Cu 30.3 Fe 6.8 Cr 1.4 i-phase II + stolperite (β, AlCu) + khatyrkite (θ, Al 2 Cu), an exact match to the natural i-phase II assemblage in the meteorite. In a second experiment, the continuous interface between the GDI and steel formed another more Fe-rich quinary i-phase (Al 68.6 Fe 14.5 Cu 11.2 Cr 4 Ni 1.8 ), together with stolperite and hollisterite (λ, Al 13 Fe 4 ), which is the expected assemblage at phase equilibrium. This study is the first laboratory reproduction of i-phase II with its natural assemblage. It suggests that the field of thermodynamically stable icosahedrite (Al 63 Cu 24 Fe 13 ) could separate into two disconnected fields under shock pressure above 20 GPa, leading to the co-existence of Fe-rich and Fe-poor i-phases like the case in Khatyrka. In light of this, shock-recovery experiments do indeed offer an efficient method of constraining the impact conditions recorded by quasicrystal-bearing meteorite, and exploring formation conditions and mechanisms leading to quasicrystals. 
    more » « less
  2. ; ; ; ; ; (, Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms)
    Bogdanović; Iva; Lorenz, Katharina (Ed.)
    PIXE analysis was conducted on p8 fisher brand filter paper samples soaked in elemental standard solutions to determine the minimum detectable levels of Al, Si, P, S, Cl, K, Ca, Cr, Fe, Ni, Cu, and Se. All samples were analyzed with beam parameters of 2 µC incident charge, and beam current of less than 2 nA at 2 MeV beam energy. Minimum detectable levels were obtained by analyzing the x-ray spectrum in the GeoPIXE analysis package, and the data for each element would be averaged over all collected spectra. The minimum detectable level in parts per million was found to be on average 9.59 for Al, 4.6 for Si, 3.23 for P, 2.27 for S, 1.82 for Cl, 1.15 for K, 0.88 for Ca, 0.51 for Cr, 0.07 for Mn, 0.54 for Fe, 1.59 for Ni, 2.0 for Zn, 1.55 for Cu, and 6.5 for Se. Minimal deviation from the averaged values was observed, except in cases where samples contained high concentrations of elements with overlapping X-ray energies. 
    more » « less
  3. ; ; ; ; ; (, Proceedings of the National Academy of Sciences)
    The first test explosion of a nuclear bomb, the Trinity test of 16 July 1945, resulted in the fusion of surrounding sand, the test tower, and copper transmission lines into a glassy material known as “trinitite.” Here, we report the discovery, in a sample of red trinitite, of a hitherto unknown composition of icosahedral quasicrystal, Si61Cu30Ca7Fe2. It represents the oldest extant anthropogenic quasicrystal currently known, with the distinctive property that its precise time of creation is indelibly etched in history. Like the naturally formed quasicrystals found in the Khatyrka meteorite and experimental shock syntheses of quasicrystals, the anthropogenic quasicrystals in red trinitite demonstrate that transient extreme pressure–temperature conditions are suitable for the synthesis of quasicrystals and for the discovery of new quasicrystal-forming systems. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al (, arXivorg)
    Quasicrystals are characterized by atomic arrangements possessing long-range order without periodicity. Van der Waals (vdW) bilayers provide a unique opportunity to controllably vary atomic alignment between two layers from a periodic moir´e crystal to an aperiodic quasicrystal. Here, we reveal a remarkable consequence of the unique atomic arrangement in a dodecagonal WSe2 quasicrystal: the K and Q valleys in separate layers are brought arbitrarily close in momentum space via higher-order Umklapp scatterings. A modest perpendicular electric field is sufficient to induce strong interlayer K − Q hybridization, manifested as a new hybrid excitonic doublet. Concurrently, we observe the disappearance of the trion resonance and attribute it to quasicrystal potential driven localization. Our findings highlight the remarkable attribute of incommensurate systems to bring any pair of momenta into close proximity, thereby introducing a novel aspect to valley engineering. 
    more » « less
  5. ; ; (, Shape Memory and Superelasticity)
    Abstract This study investigates the fabrication of Fe–Mn–Al–Ni iron-based shape memory alloys (SMAs) using laser powder bed fusion (LPBF) across a range of laser powers. The influence of energy input on material properties was assessed by evaluating the resulting volumetric energy density. Samples were produced under both as-built conditions and subjected to in situ and ex situ treatments to enhance performance. Mechanical properties were characterized through macro-indentation, Profilometry-based Indentation Plastometry (PIP), and nanoindentation techniques, while room-temperature compression testing was conducted to assess superelastic behavior. Microstructural and phase variations were analyzed using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that increasing the fabrication power improved the mechanical properties of the as-built SMAs, with the optimal performance achieved at 175 W. In situ/ex situ treatments led to a significant reduction in strength but enhanced ductility by up to 39%, along with a 52% reduction in microhardness for samples fabricated at 175 W. Overall, the LPBF-produced Fe–Mn–Al–Ni SMAs exhibited good strain recovery and stability, comparable to those produced by conventional methods. This work demonstrates the potential of LPBF in developing Fe–Mn–Al–Ni SMAs with properties matching traditionally manufactured counterparts. Graphical Abstract Mechanical behavior and microstructural features of LPBF-fabricated Fe–Mn–Al–Ni SMA under the effects of in situ and ex situ treatments 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email