A versatile system for the fabrication of surface microstructures is demonstrated by combining the photomechanical response of supramolecular azopolymers with structured polarized illumination from a high resolution spatial light modulator. Surface relief structures with periods 900 nm - 16.5 µm and amplitudes up to 1.0 µm can be fabricated with a single 5 sec exposure at 488 nm. Sinusoidal, circular, and chirped surface profiles can be fabricated via direct programming of the spatial light modulator, with no optomechanical realignment required. Surface microstructures can be combined into macroscopic areas by mechanical translation followed by exposure. The surface structures grow immediately in response to illumination, can be visually observed in real time, and require no post-exposure processing.
Thin film supramolecular azopolymers support the all‐optical generation of dynamic surface microstructures. Using a spatial light modulator (SLM) illuminated at 488 nm, structured polarized light drives surface waves of sinusoidal profile with periods 700 nm–5 µm at speeds up to 1 µm s−1. Multiple regions on the film surface within the SLM focal plane can be independently set into motion, each with unique period, speed, amplitude, and propagation direction. The underlying mechanism is the photomechanical response of the azopolymer, which is more commonly exploited for the fabrication of static surface microstructures. Hydrogen‐bonded systems such as the supramolecular system described here are particularly advantageous due to their facile fabrication from commercially available components. In addition to applications in dynamic diffractive optics, this programmable system for optical surface waves is well‐suited for studies in nanoparticle manipulation, as well as in bioengineering as a reconfigurable surface template for directed cell growth.
more » « less- NSF-PAR ID:
- 10400933
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Optical Materials
- Volume:
- 11
- Issue:
- 8
- ISSN:
- 2195-1071
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
more » « less
Summary We combined optical and atomic force microscopy to observe morphology and kinetics of microstructures (typically referred to as bees) that formed at free surfaces of unmodified Performance Graded (PG) 64‐22 asphalt binders upon cooling from 150°C to room temperature (RT) at 5°C min–1, and changes in these microstructures when the surface was terminated with a transparent solid (glass) or liquid (glycerol) overlayer. The main findings are: (1) at free binder surfaces, wrinkled microstructures started to form near the crystallization temperature (∼45°C) of saturates such as wax observed by differential scanning calorimetry, then grew to ∼5 µm diameter, ∼25 nm wrinkle amplitude and 10–30% surface area coverage upon cooling to RT, where they persisted indefinitely without observable change in shape or density. (2) Glycerol coverage of the binder surface during cooling reduced wrinkled area and wrinkle amplitude three‐fold compared to free binder surfaces upon initial cooling to RT; continued glycerol coverage at RT eliminated most surface microstructures within ∼4 h. (3) No surface microstructures were observed to form at binder surfaces covered with glass. (4) Submicron bulk microstructures were observed by near‐infrared microscopy beneath the surfaces of all binder samples, with size, shape and density independent of surface coverage. No tendency of such structures to float to the top or sink to the bottom of mm‐thick samples was observed. (5) We attribute the dependence of surface wrinkling on surface coverage to variation in interface tension, based on a thin‐film continuum mechanics model.
Lay Description Asphalt binder, or bitumen, is the glue that holds aggregate particles together to form a road surface. It is derived from the heavy residue that remains after distilling gasoline, diesel and other lighter products out of crude oil. Nevertheless, bitumen varies widely in composition and mechanical properties. To avoid expensive road failures, bitumen must be processed after distillation so that its mechanical properties satisfy diverse climate and load requirements. International standards now guide these mechanical properties, but yield varying long‐term performance as local source composition and preparation methods vary.
In situ diagnostic methods that can predict bitumen performance independently of processing history are therefore needed. The present work focuses on one promising diagnostic candidate: microscopic observation of internal bitumen structure. Past bitumen microscopy has revealed microstructures of widely varying composition, size, shape and density. A challenge is distinguishing bulk microstructures, which directly influence a binder's mechanical properties, from surface microstructures, which often dominate optical microscopy because of bitumen's opacity and scanning‐probe microscopy because of its inherent surface specificity. In previously published work, we used infrared microscopy to enhance visibility of bulk microstructure. Here, as a foil to this work, we use visible‐wavelength microscopy together with atomic‐force microscopy (AFM) specifically to isolatesurface microstructure, to understand its distinct origin and morphology, and to demonstrate its unique sensitivity to surface alterations. To this end, optical microscopy complements AFM by enabling us to observe surface microstructures form at temperatures (50°C–70°C) at which bitumen's fluidity prevents AFM, and to observe surface microstructure beneath transparent, but chemically inert, liquid (glycerol) and solid (glass) overlayers, which alter surface tension compared to free surfaces. From this study, we learned, first, that, as bitumen cools, distinctly wrinkled surface microstructures form at the same temperature at which independent calorimetric studies showed crystallization in bitumen, causing it to release latent heat of crystallization. This shows that surface microstructures are likely precipitates of the crystallizable component(s). Second, a glycerol overlayer on the cooling bitumen results in smaller, less wrinkled, sparser microstructures, whereas a glass overlayer suppresses them altogether. In contrast, underlying smaller bulk microstructures are unaffected. This shows that surface tension is the driving force behind formation and wrinkling of surface precipitates. Taken together, the work advances our ability to diagnose bitumen samples noninvasively by clearly distinguishing surface from bulk microstructure. -
more » « less
Abstract Synergizing grayscale photopolymerization and meniscus coating processes, rapid 3D printing of optical lenses is reported previously using projection microstereolithography (PµSL) process. Despite its 14 000‐fold‐improved printing speed over the femtosecond 3D printing process, PµSL still consumes significant amount of the fabrication time for precise recoating 5 µm thick fresh resin layers. At the reported speed of 24.54 mm3h−1, 3D printing of the millimeter‐size lenses still takes hours. To further improve the printing speed, the microcontinuous liquid interface production process is implemented to eliminate the time‐consuming resin recoating step. However, the micrometer‐size pores in the Teflon membrane needed for oxygen transportation are found to completely spoil the surface smoothness. The use of polydimethylsiloxane thin film possessing much refined nanoscopic porosities as the functional substitute of Teflon membrane is reported to significantly reduce the surface roughness to 13.7 nm. 3D printing of 3 mm high aspherical lens in ≈2 min at a 200‐fold‐improved speed at 4.85 × 103mm3h−1is demonstrated. The 3D printed aspherical lens has the demonstrated imaging resolution of 3.10 µm. This work represents a significant step in tackling the speed‐accuracy trade‐off of 3D printing process and thus enables rapid fabrication of customized optical components.
-
more » « less
Abstract Optical lenses require feature resolution and surface roughness that are beyond most (3D) printing methods. A new continuous projection‐based vat photopolymerization process is reported that can directly shape polymer materials into optical lenses with microscale dimensional accuracy (< 14.7 µm) and nanoscale surface roughness (< 20 nm) without post‐processing. The main idea is to utilize frustum layer stacking, instead of the conventional 2.5D layer stacking, to eliminate staircase aliasing. A continuous change of mask images is achieved using a zooming‐focused projection system to generate the desired frustum layer stacking with controlled slant angles. The dynamic control of image size, objective and imaging distances, and light intensity involved in the zooming‐focused continuous vat photopolymerization are systematically investigated. The experimental results reveal the effectiveness of the proposed process. The 3D‐printed optical lenses with various designs, including parabolic lenses, fisheye lenses, and a laser beam expander, are fabricated with a surface roughness of 3.4 nm without post‐processing. The dimensional accuracy and optical performance of the 3D‐printed compound parabolic concentrators and fisheye lenses within a few millimeters are investiagted. These results highlight the rapid and precise nature of this novel manufacturing process, demonstrating a promising avenue for future optical component and device fabrication.
-
Sodium naphthenates (NaNs), found in crude oils and oil sands process-affected water (OSPW), can act as surfactants and stabilize undesirable foams and emulsions. Despite the critical impact of soap-like NaNs on the formation, properties, and stability of petroleum and OSPW foams, there is a significant lack of studies that characterize foam film drainage, motivating this study. Here, we contrast the drainage of aqueous foam films formulated with NaN with foams containing sodium dodecyl sulfate (SDS), a well-studied surfactant system, in the relatively low concentration regime ( c /CMC < 12.5). The foam films exhibit drainage via stratification, displaying step-wise thinning and coexisting thick–thin regions manifested as distinct shades of gray in reflected light microscopy due to thickness-dependent interference intensity. Using IDIOM (interferometry digital imaging optical microscopy) protocols that we developed, we analyze pixel-wise intensity to obtain thickness maps with high spatiotemporal resolution (thickness <1 nm, lateral ∼500 nm, time ∼10 ms). The analysis of interference intensity variations over time reveals that the aqueous foam films of both SDS and NaN possess an evolving, dynamic, and rich nanoscopic topography. The nanoscopic thickness transitions for stratifying SDS foam films are attributed to the role played by damped supramolecular oscillatory structural disjoining pressure contributed by the confinement-induced layering of spherical micelles. In comparison with SDS, we find smaller concentration-dependent step size and terminal film thickness values for NaN, implying weaker intermicellar interactions and oscillatory structural disjoining pressure with shorter decay length and periodicity.more » « less