Title: Differences in water and vapor transport through angstrom-scale pores in atomically thin membranes
Abstract The transport of water through nanoscale capillaries/pores plays a prominent role in biology, ionic/molecular separations, water treatment and protective applications. However, the mechanisms of water and vapor transport through nanoscale confinements remain to be fully understood. Angstrom-scale pores (~2.8–6.6 Å) introduced into the atomically thin graphene lattice represent ideal model systems to probe water transport at the molecular-length scale with short pores (aspect ratio ~1–1.9) i.e., pore diameters approach the pore length (~3.4 Å) at the theoretical limit of material thickness. Here, we report on orders of magnitude differences (~80×) between transport of water vapor (~44.2–52.4 g m −2 day −1 Pa −1 ) and liquid water (0.6–2 g m −2 day −1 Pa −1 ) through nanopores (~2.8–6.6 Å in diameter) in monolayer graphene and rationalize this difference via a flow resistance model in which liquid water permeation occurs near the continuum regime whereas water vapor transport occurs in the free molecular flow regime. We demonstrate centimeter-scale atomically thin graphene membranes with up to an order of magnitude higher water vapor transport rate (~5.4–6.1 × 10 4  g m −2 day −1 ) than most commercially available ultra-breathable protective materials while effectively blocking even sub-nanometer (>0.66 nm) model ions/molecules.  more » « less
Award ID(s):
1944134
NSF-PAR ID:
10429601
Author(s) / Creator(s):
; ; ; ; ; ; ;
Date Published:
Journal Name:
Nature Communications
Volume:
13
Issue:
1
ISSN:
2041-1723
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    Direct synthesis of graphene with well‐defined nanoscale pores over large areas can transform the fabrication of nanoporous atomically thin membranes (NATMs) and greatly enhance their potential for practical applications. However, scalable bottom‐up synthesis of continuous sheets of nanoporous graphene that maintain integrity over large areas has not been demonstrated. Here, it is shown that a simple reduction in temperature during chemical vapor deposition (CVD) on Cu induces in‐situ formation of nanoscale defects (≤2–3 nm) in the graphene lattice, enabling direct and scalable synthesis of nanoporous monolayer graphene. By solution‐casting of hierarchically porous polyether sulfone supports on the as‐grown nanoporous CVD graphene, large‐area (>5 cm2) NATMs for dialysis applications are demonstrated. The synthesized NATMs show size‐selective diffusive transport and effective separation of small molecules and salts from a model protein, with ≈2–100× increase in permeance along with selectivity better than or comparable to state‐of‐the‐art commercially available polymeric dialysis membranes. The membranes constitute the largest fully functional NATMs fabricated via bottom‐up nanopore formation, and can be easily scaled up to larger sizes permitted by CVD synthesis. The results highlight synergistic benefits in blending traditional membrane casting with bottom‐up pore creation during graphene CVD for advancing NATMs toward practical applications.

     
    more » « less
  2. Abstract

    Atomically thin membranes comprising nanopores in a 2D material promise to surpass the performance of polymeric membranes in several critical applications, including water purification, chemical and gas separations, and energy harvesting. However, fabrication of membranes with precise pore size distributions that provide exceptionally high selectivity and permeance in a scalable framework remains an outstanding challenge. Circumventing these constraints, here, a platform technology is developed that harnesses the ability of oppositely charged polyelectrolytes to self‐assemble preferentially across larger, relatively leaky atomically thin nanopores by exploiting the lower steric hindrance of such larger pores to molecular interactions across the pores. By selectively tightening the pore size distribution in this manner, self‐assembly of oppositely charged polyelectrolytes simultaneously introduced on opposite sides of nanoporous graphene membranes is demonstrated to discriminate between nanopores to seal non‐selective transport channels, while minimally compromising smaller, water‐selective pores, thereby remarkably attenuating solute leakage. This improved membrane selectivity enables desalination across centimeter‐scale nanoporous graphene with 99.7% and >90% rejection of MgSO4and NaCl, respectively, under forward osmosis. These findings provide a versatile strategy to augment the performance of nanoporous atomically thin membranes and present intriguing possibilities of controlling reactions across 2D materials via exclusive exploitation of pore size‐dependent intermolecular interactions.

     
    more » « less
  3. Abstract

    Single‐layer graphene containing molecular‐sized in‐plane pores is regarded as a promising membrane material for high‐performance gas separations due to its atomic thickness and low gas transport resistance. However, typical etching‐based pore generation methods cannot decouple pore nucleation and pore growth, resulting in a trade‐off between high areal pore density and high selectivity. In contrast, intrinsic pores in graphene formed during chemical vapor deposition are not created by etching. Therefore, intrinsically porous graphene can exhibit high pore density while maintaining its gas selectivity. In this work, the density of intrinsic graphene pores is systematically controlled for the first time, while appropriate pore sizes for gas sieving are precisely maintained. As a result, single‐layer graphene membranes with the highest H2/CH4separation performances recorded to date (H2permeance > 4000 GPU and H2/CH4selectivity > 2000) are fabricated by manipulating growth temperature, precursor concentration, and non‐covalent decoration of the graphene surface. Moreover, it is identified that nanoscale molecular fouling of the graphene surface during gas separation where graphene pores are partially blocked by hydrocarbon contaminants under experimental conditions, controls both selectivity and temperature dependent permeance. Overall, the direct synthesis of porous single‐layer graphene exploits its tremendous potential as high‐performance gas‐sieving membranes.

     
    more » « less
  4. Ice nucleation in the atmosphere influences cloud properties, altering precipitation and the radiative balance, ultimately regulating Earth’s climate. An accepted ice nucleation pathway, known as deposition nucleation, assumes a direct transition of water from the vapor to the ice phase, without an intermediate liquid phase. However, studies have shown that nucleation occurs through a liquid phase in porous particles with narrow cracks or surface imperfections where the condensation of liquid below water saturation can occur, questioning the validity of deposition nucleation. We show that deposition nucleation cannot explain the strongly enhanced ice nucleation efficiency of porous compared with nonporous particles at temperatures below −40 °C and the absence of ice nucleation below water saturation at −35 °C. Using classical nucleation theory (CNT) and molecular dynamics simulations (MDS), we show that a network of closely spaced pores is necessary to overcome the barrier for macroscopic ice-crystal growth from narrow cylindrical pores. In the absence of pores, CNT predicts that the nucleation barrier is insurmountable, consistent with the absence of ice formation in MDS. Our results confirm that pore condensation and freezing (PCF), i.e., a mechanism of ice formation that proceeds via liquid water condensation in pores, is a dominant pathway for atmospheric ice nucleation below water saturation. We conclude that the ice nucleation activity of particles in the cirrus regime is determined by the porosity and wettability of pores. PCF represents a mechanism by which porous particles like dust could impact cloud radiative forcing and, thus, the climate via ice cloud formation.

     
    more » « less
  5. Selective proton (H + ) permeation through the atomically thin lattice of graphene and other 2D materials offers new opportunities for energy conversion/storage and novel separations. Practical applications necessitate scalable synthesis via approaches such as chemical vapor deposition (CVD) that inevitably introduce sub-nanometer defects, grain boundaries and wrinkles, and understanding their influence on H + transport and selectivity for large-area membranes is imperative but remains elusive. Using electrically driven transport of H + and potassium ions (K + ) we probe the influence of intrinsic sub-nanometer defects in monolayer CVD graphene across length-scales for the first time. At the micron scale, the areal H + conductance of CVD graphene (∼4.5–6 mS cm −2 ) is comparable to that of mechanically exfoliated graphene indicating similarly high crystalline quality within a domain, albeit with K + transport (∼1.7 mS cm −2 ). However, centimeter-scale Nafion|graphene|Nafion devices with several graphene domains show areal H + conductance of ∼339 mS cm −2 and K + conductance of ∼23.8 mS cm −2 (graphene conductance for H + is ∼1735 mS cm −2 and for K + it is ∼47.6 mS cm −2 ). Using a mathematical-transport-model and Nafion filled polycarbonate track etched supports, we systematically deconstruct the observed orders of magnitude increase in H + conductance for centimeter-scale CVD graphene. The mitigation of defects (>1.6 nm), wrinkles and tears via interfacial polymerization results in a conductance of ∼1848 mS cm −2 for H + and ∼75.3 mS cm −2 for K + (H + /K + selectivity of ∼24.5) via intrinsic sub-nanometer proton selective defects in CVD graphene. We demonstrate atomically thin membranes with significantly higher ionic selectivity than state-of-the-art proton exchange membranes while maintaining comparable H + conductance. Our work provides a new framework to assess H + conductance and selectivity of large-area 2D membranes and highlights the role of intrinsic sub-nanometer proton selective defects for practical applications. 
    more » « less