A 2D plane strain extended finite element method (XFEM) model was developed to simulate three-point bending fracture toughness tests for human bone conducted in hydrated and dehydrated conditions. Bone microstructures and crack paths observed by micro-CT imaging were simulated using an XFEM damage model. Critical damage strains for the osteons, matrix, and cement lines were deduced for both hydrated and dehydrated conditions and it was found that dehydration decreases the critical damage strains by about 50%. Subsequent parametric studies using the various microstructural models were performed to understand the impact of individual critical damage strain variations on the fracture behavior. The study revealed the significant impact of the cement line critical damage strains on the crack paths and fracture toughness during the early stages of crack growth. Furthermore, a significant sensitivity of crack growth resistance and crack paths on critical strain values of the cement lines was found to exist for the hydrated environments where a small change in critical strain values of the cement lines can alter the crack path to give a significant reduction in fracture resistance. In contrast, in the dehydrated state where toughness is low, the sensitivity to changes in critical strain values of the cement lines is low. Overall, our XFEM model was able to provide new insights into how dehydration affects the micromechanisms of fracture in bone and this approach could be further extended to study the effects of aging, disease, and medical therapies on bone fracture.
more »
« less
Dataset for Fracture and Impact Toughness of High-Entropy Alloys
Abstract Fracture dictates the service limits of metallic structures. Damage tolerance of materials may be characterized by fracture toughness rigorously developed from fracture mechanics, or less rigorous yet more easily obtained impact toughness (or impact energy as a variant). Given the promise of high-entropy alloys (HEAs) in structural and damage-tolerance applications, we compiled a dataset of fracture toughness and impact toughness/energy from the literature till the end of the 2022 calendar year. The dataset is subdivided into three categories, i.e., fracture toughness, impact toughness, and impact energy, which contain 153, 14, and 78 distinct data records, respectively. On top of the alloy chemistry and measured fracture quantities, each data record also documents the factors influential to fracture. Examples are material-processing history, phase structures, grain sizes, uniaxial tensile properties, such as yield strength and elongation, and testing conditions. Data records with comparable conditions are graphically visualized by plots. The dataset is hosted in Materials Cloud, an open data repository.
more »
« less
- Award ID(s):
- 1809640
- PAR ID:
- 10436663
- Date Published:
- Journal Name:
- Scientific Data
- Volume:
- 10
- Issue:
- 1
- ISSN:
- 2052-4463
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
2D materials such as graphene, monolayer MoS2 and MXene are highly functional for their unique mechanical, thermal and electrical features and are considered building blocks for future ultrathin, flexible electronics. However, they can easily fracture from flaws or defects and thus it is important to increase their toughness in applications. Here, inspired by natural layered composites and architected 3D printed materials of high toughness, we introduce architected defects to the 2D materials and study their fracture in molecular dynamics simulations. We find that the length of the defects in the shape of parallel bridges is crucial to fracture toughness, as long bridges can significantly increase the toughness of graphene and MoS2 but decrease the toughness of MXene, while short bridges show opposite effects. This strategy can increase the toughness of 2D materials without introducing foreign materials or altering the chemistry of the materials, providing a general method to improve their mechanics.more » « less
-
It is now a well-established fact that even simple topology variations can drastically change the fracture response of structures. With the objective of gaining quantitative insight into this phenomenon, this paper puts forth a density-based topology optimization framework for the fracture response of structures subjected to quasistatic mechanical loads. One of the two key features of the proposed framework is that it makes use of a complete phase-field fracture theory that has been recently shown capable of accurately describing the nucleation and propagation of brittle fracture in a wide range of nominally elastic materials under a wide range of loading conditions. The other key feature is that the framework is based on a multi-objective function that allows optimizing in a weighted manner: ( ) the initial stiffness of the structure, ( ) the first instance at which fracture nucleates, and ( ) the energy dissipated by fracture propagation once fracture nucleation has occurred. The focus is on the basic case of structures made of a single homogeneous material featuring an isotropic linear elastic behavior alongside an isotropic strength surface and toughness. Novel interpolation rules are proposed for each of these three types of material properties. As a first effort to gain quantitative insight, the framework is deployed to optimize the fracture response of 2D structures wherein the fracture is bound to nucleate in three different types of regions: within the bulk, from geometric singularities (pre-existing cracks and sharp corners), and from smooth parts of the boundary. The obtained optimized structures are shown to exhibit significantly enhanced fracture behaviors compared to those of structures that are optimized according to conventional stiffness maximization. Furthermore, the results serve to reveal a variety of strengthening and toughening mechanisms. These include the promotion of highly porous structures, the formation of tension-compression asymmetric regions, and the removal of cracks and sharp corners. The particular mechanism that is preferred by a given structure, not surprisingly, correlates directly to the elastic, strength, and toughness properties of the material that is made of.more » « less
-
- (Ed.)Rubber-like materials have a broad scope of applications due to their unique properties like high stretchability and increased toughness. Hence, computational models for simulating their fracture behavior are paramount for designing them against failures. In this study, the phase field fracture approach is integrated with a multiscale polymer model for predicting the fracture behavior in elastomers. At the microscale, damaged polymer chains are modeled to be made up of a number of elastic chain segments pinned together. Using the phase field approach, the damage in the chains is represented using a continuous variable. Both the bond stretch internal energy and the entropic free energy of the chain are assumed to drive the damage, and the advantages of this assumption are expounded. A framework for utilizing the non-affine microsphere model for damaged systems is proposed by considering the minimization of a hypothetical undamaged free energy, ultimately connecting the chain stretch to the macroscale deformation gradient. At the macroscale, a thermodynamically consistent formulation is derived in which the total dissipation is assumed to be mainly due to the rupture of molecular bonds. Using a monolithic scheme, the proposed model is numerically implemented and the resulting three-dimensional simulation predictions are compared with existing experimental data. The capability of the model to qualitatively predict the propagation of complex crack paths and quantitatively estimate the overall fracture behavior is verified. Additionally, the effect of the length scale parameter on the predicted fracture behavior is studied for an inhomogeneous system.more » « less
-
An experimental study is performed to investigate the quasi-static fracture toughness and damage monitoring capabilities of liquid metal (75.5% Gallium/24.5% Indium) reinforced intraply glass/carbon hybrid composites. Two different layups (G-0, where glass fibers are along the crack propagation direction; C-0, where carbon fibers are along the crack propagation direction) and two different weight percentages of liquid metal (1% and 2%) are considered in the fabrication of the composites. A novel four-probe technique is employed to determine the piezo-resistive damage response under mode-I fracture loading conditions. The effect of layups and liquid metal concentrations on fracture toughness and changes in piezo-resistance response is discussed. The C-composite without liquid metal demonstrated higher fracture toughness compared to that of the G-composite due to carbon fiber breakage. The addition of liquid metal decreases the fracture initiation toughness of both G- and C-composites. Scanning electron microscopy images show that liquid metal takes the form of large liquid metal pockets and small spherical droplets on the fracture surfaces. In both C- and G-composites, the peak resistance change of composites with 2% liquid metal is substantially lower than that of both no-liquid metal and 1% liquid metal composites.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1038/s41597-022-01911-4