Abstract Hafnium carbide (HfC) is an ultrahigh‐temperature ceramic with high melting point, chemical stability, hardness, and wear resistance. However, its low fracture toughness and poor thermal shock resistance limit its structural applications in extreme environments. In this study, co‐curing of liquid precursors was carried out prior to complete pyrolysis of individual polymeric precursors. First, HfC preceramic polymer precursor was cured, followed by silicon carbonitride (SiCN) precursor curing on a 2D carbon fiber (CF) cloth using the drop‐coating process. The infiltrated CFs were pyrolyzed at 800°C to achieve CF/HfC‐SiCN ceramic mini‐composites. The cross‐linked precursor‐to‐ceramic yield was observed to be as high as 65% when the procedure was carried out in an inert environment. Although stable up to 1200°C, CF/HfC‐SiCN samples demonstrated susceptibility to oxidation at 1500°C in ambient air. The oxidation of HfC in the presence of SiC leads to the formation of a hafnium‐containing silicate (HfxSiyOz) along with hafnia (HfO2). This compound of silicate and hafnia limits oxygen diffusion better than SiO2and HfO2individually. The incorporation of SiCN in HfC ceramic led to improved phase stability compared to a neat HfC system. The results of this study also show that the use of liquid‐phase precursors for HfC and SiCN in the polymer‐infiltrated pyrolysis method is a promising approach to fabricating high‐temperature structural ceramic matrix composites with good oxidation resistance.
more »
« less
Low‐temperature synthesis of HfC/HfO 2 nanocomposites from a commercial single‐source precursor
Abstract A liquid‐phase polymer‐to‐ceramic approach is reported for the synthesis of hafnium carbide (HfC)/hafnium oxide (HfO2) composite particles from a commercial precursor. Typically, HfC ceramics have been obtained by sintering of fine powders, which usually results in large particle size and high porosity during densification. In this study a single‐source liquid precursor was first cured at low temperature and then pyrolyzed at varying conditions to achieve HfC ceramics. The chemical structure of the liquid and cured precursors, and the resulting HfC ceramics was studied using various analytical techniques. The nuclear magnetic resonance and Fourier transform infrared spectroscopy indicated the presence of partially hydrated hafnium oxychloride (Hf–O–Cl·nH2O) in the precursor. Scanning electron microscopy of the resulting HfC crystals showed a size distribution in the range of approx. 600–700 nm. The X‐ray diffraction of the pyrolyzed samples confirmed the formation of crystalline HfC along with monoclinic‐HfO2and free carbon phase. The formation of HfO2in the ceramics was significantly reduced by controlling the low‐temperature curing temperature. Pyrolysis at various temperatures showed that HfC formation occurred even at 1000°C. These results show that the reported precursor could be promising for the direct synthesis of ultrahigh temperature HfC ceramics and for precursor infiltration pyrolysis of reinforced ceramic matrix composites.
more »
« less
- Award ID(s):
- 1743701
- PAR ID:
- 10440356
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- International Journal of Ceramic Engineering & Science
- Volume:
- 5
- Issue:
- 5
- ISSN:
- 2578-3270
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
A significant challenge during the polymer-to-ceramic pyrolysis conversion is to understand the polymer-to-ceramic atomic evolution and correlate the composition changes with the precursor molecular structures, pyrolysis conditions, and resulting ceramic characteristics. In this study, a Reactive Force Field (ReaxFF) simulation approach has been used to simulate silicon oxycarbide (SiOC) ceramic formation from four different polysiloxane precursors. For the first time, we show atomically that pyrolysis time and temperature proportionally impact the new Si-O rich and C rich cluster sizes as well as the composition separation of Si-O from C. Polymer side groups have a more complex effect on the Si-O and C cluster separation and growth, with ethyl group leading to the most Si-O cluster separation and phenyl group leading to the most C cluster separation. We also demonstrate never-before correlations of gas release with polymer molecular structures and functional groups. CH4, C2H6, C2H4, and H2 are preferentially released from the pyrolyzing systems. The sequence is determined by the polymer molecular structures. This work is the first to atomically illustrate the innate correlations between the polymer precursors and pyrolyzed ceramics.more » « less
-
Abstract Polymer‐derived amorphous SiCN has excellent high‐temperature stability and properties. To reduce the shrinkage during pyrolysis and to improve the high‐temperature oxidation resistance, Y2O3was added as a filler. In this study, polymer‐derived SiCN–Y2O3composites were fabricated by mixing a polymeric precursor of SiCN with Y2O3submicron powders in different ratios. The mixtures were cross‐linked and pyrolyzed in argon. SiCN–Y2O3composites were processed using field‐assisted sintering technology at 1350°C for 5 min under vacuum. Dense SiCN–Y2O3composite pellets were successfully made with relative density higher than 98% and homogeneous microstructure. Due to low temperature and short time of the heat‐treatment, the grain growth of Y2O3was substantially inhibited. The Y2O3grain size was ∼1 μm after sintering. The composites’ heat capacity, thermal diffusivity, and thermal expansion coefficients were characterized as a function of temperature. The thermal conductivity of the composites ceramics decreased as the amount of amorphous SiCN increased and the coefficient of thermal expansion (CTE) of the composites increased with Y2O3content. However, the thermal conductivity and CTE did not follow the rule of mixture. This is likely due to the partial oxidation of SiCN and the resultant impurity phases such as Y2SiO5, Y2Si2O7, and Y4.67(SiO4)3O.more » « less
-
null (Ed.)Electrospinning is an emerging technique for synthesizing micron to submicron-sized polymer fibre supports for applications in energy storage, catalysis, filtration, drug delivery and so on. However, fabrication of electrospun ceramic fibre mats for use as a reinforcement phase in ceramic matrix composites or CMCs for aerospace applications remains largely unexplored. This is mainly due to stringent operating requirements that require a combination of properties such as low mass density, high strength, and ultrahigh temperature resistance. Herein we report fabrication of molecular precursor-derived silicon oxycarbide or SiOC fibre mats via electrospinning and pyrolysis of cyclic polysiloxanes-based precursors at significantly lower weight loadings of organic co-spin agent. Ceramic fibre mats, which were free of wrapping, were prepared by a one-step spinning (in air) and post heat-treatment for crosslinking and pyrolysis (in argon at 800 °C). The pyrolyzed fibre mats were revealed to be amorphous and a few microns in diameter. Four siloxane-based pre-ceramic polymers were used to study the influence of precursor molecular structure on the compositional and morphological differences of cross-linked and pyrolyzed products. Further thermal characterization suggested the potential of electrospun ceramic mats in high temperature applications.more » « less
-
Abstract In this study, we demonstrate a novel environmental barrier coating processed from polymer‐derived ceramics (PDCs) with homogeneously distributed sub‐micrometer Y2O3as the filler. Under suitable conditions, dense and crack‐free coatings can be achieved for all the designed compositions with the volumetric content of Y2O3varied from 45 to 93 vol%. To process the PDC SiC–Y2O3composite coatings, Y2O3particles and SiC liquid precursor were uniformly dispersed in hexane and then dip‐coated on SiC substrates. After cross‐linking at 250°C and heat‐treated at 900°C in argon, dense and crack‐free PDC SiC–Y2O3composite coatings were formed. The effect of coating thickness and heat‐treatment temperature on the formation of cracks due to constrained pyrolysis was studied. The critical thickness for realizing crack‐free coatings of three compositions (i.e., 93, 77, and 45 vol% Y2O3) was studied for heat treatment from 1000 to 1300°C using atomic force microscope and scanning electron microscopy. As heat‐treatment temperature increases, the critical coating thickness decreases for the same coating compositions due to enhanced shrinkage at higher temperature. With higher Y2O3content, the critical thickness of the coating increased. The inert Y2O3particles reduce the amount of polymer leading to reduction in the overall constrained shrinkage of the coating during heat treatment.more » « less