Abstract The challenge of growing rare-earth (RE) sesquioxide crystals can be overcome by tailoring their structural stability and melting point via composition engineering. This work contributes to the advancement of the field of crystal growth of high-entropy oxides. A compound with only small REs (Lu,Y,Ho,Yb,Er) 2 O 3 maintains a cubic C-type structure upon cooling from the melt, as observed via in-situ high-temperature neutron diffraction on aerodynamically levitated samples. On the other hand, a compound with a mixture of small and large REs (Lu,Y,Ho,Nd,La) 2 O 3 crystallizes as a mixture of a primary C-type phase with an unstable secondary phase. Crystals of compositions (Lu,Y,Ho,Nd,La) 2 O 3 and (Lu,Y,Gd,Nd,La) 2 O 3 were grown by the micro-pulling-down (mPD) method with a single monoclinic B-type phase, while a powder of (Lu,Y,Ho,Yb,Er) 2 O 3 did not melt at the maximum operating temperature of an iridium-rhenium crucible. The minimization of the melting point of the two grown crystals is attributed to the mismatch in cation sizes. The electron probe microanalysis reveals that the general element segregation behavior in the crystals depends on the composition.
more »
« less
This content will become publicly available on July 12, 2024
Crystal growth and phase formation of high‐entropy rare‐earth monoclinic aluminates
For the first time, high‐entropy rare‐earth monoclinic aluminate crystals were grown via directional solidification using the micro‐pulling‐down method. Five high‐entropy compositions were formulated with a general formula RE4Al2O9, where RE is an equiatomic mixture of five rare‐earth elements. The rare‐earth elements included were Lu, Yb, Er, Y, Ho, Dy, Tb, Gd, Eu, Sm, Nd, and La. High‐temperature powder X‐ray diffraction and Rietveld structure refinement indicated that all crystals were a single monoclinic phase and that rare‐earth average ionic radius did not affect phase purity. At room temperature, the refined lattice parameters increased consistently with increasing average ionic radii of the five compositions. One of the crystals had a typical high‐temperature phase transition of single‐RE RE4Al2O9in the range of 1100–1150°C, which consisted of a lattice contraction upon heating. Differential scanning calorimetry indicated a thermal event corresponding to that phase transition. Electron probe microanalysis revealed Al‐rich inclusions on the surface of the crystals. Crystals containing Tb had dark surface features that became lighter after annealing in a reducing atmosphere, which indicated that Tb4+may be responsible for the dark features.
more » « less- Award ID(s):
- 1846935
- NSF-PAR ID:
- 10441443
- Publisher / Repository:
- Wiley-Blackwell
- Date Published:
- Journal Name:
- Journal of the American Ceramic Society
- Volume:
- 106
- Issue:
- 11
- ISSN:
- 0002-7820
- Page Range / eLocation ID:
- p. 7123-7132
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The effects of composition on the phase formation of multicomponent garnet crystals grown via directional solidification by the micro-pulling-down method are studied. A relatively wide range of rare-earth (RE) average ionic radii (AIR) is explored by formulating ten compositions from the system (Lu,Y,Ho,Dy,Tb,Gd) 3 Al 5 O 12 . Crystals were grown at either 0.05 or 0.20 mm min −1 . The hypothesis is that multicomponent compounds with large AIR will form secondary phases as the single-RE aluminum garnets formed by larger Tb 3+ or Gd 3+ ; this will result in crystals of poor optical quality. Crystals with large AIR have a central opaque region in optical microscopy images, which is responsible for their reduced transparency compared to crystals with small AIR. Slow pulling rates suppress the formation of the opaque region in crystals with intermediate AIR. Powder and single-crystal X-ray diffraction and electron probe microanalysis results indicate that the opaque region is a perovskite phase. Scanning electron microscopy and energy dispersive spectroscopy measurements reveal eutectic inclusions at the outer surface of the crystals. The concentration of the eutectic inclusions increases with increasing AIR.more » « less
-
Abstract Two new high-entropy ceramics (HECs) in the weberite and fergusonite structures, along with the unexpected formation of ordered pyrochlore phases with ultrahigh-entropy compositions and an abrupt pyrochlore-weberite transition, are discovered in a 21-component oxide system. While the Gibbs phase rule allows 21 equilibrium phases, 9 out of the 13 compositions examined possess single HEC phases (with ultrahigh ideal configurational entropies: ∼2.7 k B per cation or higher on one sublattice in most cases). Notably, (15RE 1/15 )(Nb 1/2 Ta 1/2 )O 4 possess a single monoclinic fergusonite (C2/ c ) phase, and (15RE 1/15 ) 3 (Nb 1/2 Ta 1/2 ) 1 O 7 form a single orthorhombic (C222 1 ) weberite phase, where 15RE 1/15 represents Sc 1/15 Y 1/15 La 1/15 Pr 1/15 Nd 1/15 Sm 1/15 Eu 1/15 Gd 1/15 Tb 1/15 Dy 1/15 Ho 1/15 Er 1/15 Tm 1/15 Yb 1/15 Lu 1/15 . Moreover, a series of eight (15RE 1/15 ) 2+ x (Ti 1/4 Zr 1/4 Ce 1/4 H 1/4 ) 2−2 x (Nb 1/2 Ta 1/2 ) x O 7 specimens all exhibit single phases, where a pyrochlore-weberite transition occurs within 0.75 < x < 0.8125. This cubic-to-orthorhombic transition does not change the temperature-dependent thermal conductivity appreciably, as the amorphous limit may have already been achieved in the ultrahigh-entropy 21-component oxides. These discoveries expand the diversity and complexity of HECs, towards many-component compositionally complex ceramics (CCCs) and ultrahigh-entropy ceramics.more » « less
-
Abstract Temperature limitations in nickel‐base superalloys have resulted in the emergence of SiC‐based ceramic matrix composites as a viable replacement for gas turbine components in aviation applications. Higher operating temperatures allow for reduced fuel consumption but present a materials design challenge related to environmental degradation. Rare‐earth disilicates (RE 2 Si 2 O 7 ) have been identified as coatings that can function as environmental barriers and minimize hot component degradation. In this work, single‐ and multiple‐component rare‐earth disilicate powders were synthesized via a sol‐gel method with compositions selected to exist in the monoclinic C 2/ m phase ( β phase). Phase stability in multiple cation compositions was shown to follow a rule of mixtures and the C 2/ m phase could be realized for compositions that contained up to 25% dysprosium, which typically only exists in a triclinic, P , phase. All compositions exhibited phase stability from room temperature to 1200°C as assessed by X‐ray diffraction. The thermal expansion tensors for each composition were determined from high‐temperature synchrotron X‐ray diffraction and accompanying Rietveld refinements. It was observed that ytterbium‐containing compositions had larger changes in the α 31 shear component with increasing temperature that led to a rotation of the principal axes. Principal axes rotation of up to 47° were observed for ytterbium disilicate. The results suggest that microstructure design and crystallographic texture may be essential future avenues of investigation to ensure thermo‐mechanical robustness of rare‐earth disilicate environmental barrier coatings.more » « less
-
null (Ed.)Phase transformations in multicomponent rare earth sesquioxides were studied by splat quenching from the melt, high temperature differential thermal analysis and synchrotron X-ray diffraction on laser-heated samples. Three compositions were prepared by the solution combustion method: (La,Sm,Dy,Er,RE)2O3, where all oxides are in equimolar ratios and RE is Nd or Gd or Y. After annealing at 800 °C, all powders contained mainly a phase of C-type bixbyite structure. After laser melting, all samples were quenched in a single-phase monoclinic B-type structure. Thermal analysis indicated three reversible phase transitions in the range 1900–2400 °C, assigned as transformations into A, H, and X rare earth sesquioxides structure types. Unit cell volumes and volume changes on C-B, B-A, and H-X transformations were measured by X-ray diffraction and consistent with the trend in pure rare earth sesquioxides. The formation of single-phase solid solutions was predicted by Calphad calculations. The melting point was determined for the (La,Sm,Dy,Er,Nd)2O3 sample as 2456 ± 12 °C, which is higher than for any of constituent oxides. An increase in melting temperature is probably related to nonideal mixing in the solid and/or the melt and prompts future investigation of the liquidus surface in Sm2O3-Dy2O3, Sm2O3-Er2O3, and Dy2O3-Er2O3 systems.more » « less