Title: Low‐Voltage Magnetoelectric Coupling in Fe 0.5 Rh 0.5 /0.68PbMg 1/3 Nb 2/3 O 3 ‐0.32PbTiO 3 Thin‐Film Heterostructures
Abstract

The rapid development of computing applications demands novel low‐energy consumption devices for information processing. Among various candidates, magnetoelectric heterostructures hold promise for meeting the required voltage and power goals. Here, a route to low‐voltage control of magnetism in 30 nm Fe0.5Rh0.5/100 nm 0.68PbMg1/3Nb2/3O3‐0.32PbTiO3(PMN‐PT) heterostructures is demonstrated wherein the magnetoelectric coupling is achieved via strain‐induced changes in the Fe0.5Rh0.5mediated by voltages applied to the PMN‐PT. We describe approaches to achieve high‐quality, epitaxial growth of Fe0.5Rh0.5on the PMN‐PT films and, a methodology to probe and quantify magnetoelectric coupling in small thin‐film devices via studies of the anomalous Hall effect. By comparing the spin‐flop field change induced by temperature and external voltage, the magnetoelectric coupling coefficient is estimated to reach ≈7 × 10−8 s m−1at 325 K while applying a −0.75 V bias.

 
more » « less
Award ID(s):
1708615
NSF-PAR ID:
10446852
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Functional Materials
Volume:
31
Issue:
40
ISSN:
1616-301X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    Electric‐field‐controlled magnetism is of importance in realizing energy efficient, dense and fast information storage and processing. Strain‐mediated converse magneto‐electric (ME) coupling between ferromagnetic and ferroelectric heterostructure shows promise for realizing electric‐controlled magnetism at room temperature and is attracting a number of recent investigations. However, such ME‐effect studies have mainly focus on magnetic metals. In this work, high quality yttrium iron garnet (Y3Fe5O12(YIG)) films are deposited directly onto (100)‐oriented single‐crystal Pb (Mg1/3Nb2/3)0.7Ti0.3O3(PMN‐PT) substrates by means of magnetron sputtering. The electric‐field‐induced polarization switching and lattice strain in the PMN‐PT substrate results in two distinct magnetization states in the YIG film that are nonvolatile and electrically reversible. Because of the direct contact between the YIG and the PMN‐PT substrate, an efficient ME coupling and an almost 90° rotation of the easy axis of the YIG film can be realized. Furthermore, the electric‐field‐controlled hysteresis loop‐like ferromagnetic resonance field shifts and spin pumping signals are observed in Pt/YIG/PMN‐PT heterostructures. Thus, the obstacle is overcome via growing high‐quality YIG thin films directly onto PMN‐PT substrates and an efficient manipulation of magnetism and pure spin current transport by electric field is thereby realized. These findings are instructive for future low‐power magnetic insulator‐based spintronic devices.

     
    more » « less
  2. Abstract

    The local compositional heterogeneity associated with the short‐range ordering of Mg and Nb in PbMg1/3Nb2/3O3(PMN) is correlated with its characteristic relaxor ferroelectric behavior. Fully ordered PMN is not prepared as a bulk material. This work examines the relaxor behavior in PMN thin films grown at temperatures below 1073 K by artificially reducing the degree of disorder via synthesis of heterostructures with alternate layers of Pb(Mg2/3Nb1/3)O3and PbNbO3, as suggested by the random‐site model. 100 nm thick, phase‐pure films are grown epitaxially on (111) SrTiO3substrates using alternate target timed pulsed‐laser deposition of Pb(Mg2/3Nb1/3)O3and PbNbO3targets with 20% excess Pb. Selected area electron diffraction confirms the emergence of (1/2, 1/2, 1/2) superlattice spots with randomly distributed ordered domains as large as ≈150 nm. These heterostructures exhibit a dielectric constant of 800, loss tangents of ≈0.03 and 2× remanent polarization of ≈11 µC cm−2at room temperature. Polarization–electric field hysteresis loops, Rayleigh data, and optical second‐harmonic generation measurements are consistent with the development of ferroelectric domains below 140 K. Temperature‐dependent permittivity measurements demonstrate reduced frequency dispersion compared to short range ordered PMN films. This work suggests a continuum between normal and relaxor ferroelectric behavior in the engineered PMN thin films.

     
    more » « less
  3. Abstract

    Composition and film quality of perovskite are crucial for the further improvement of perovskite solar cells (PSCs), including efficiency, reproducibility, and stability. Here, it is demonstrated that by simply mixing 50% of formamidinium (FA+) into methylammonium lead iodide (MAPbI3), a highly crystalline, stable phase, and compact, polycrystalline grain morphology perovskite is formed by using a solvent‐mediated phase transformation process via the synergism of dimethyl sulfoxide and diethyl ether, which shows long carrier lifetime, low trap state density, and a record certified 21.8% power conversion efficiency (PCE) in pure‐iodide, alkaline‐metal‐free MA0.5FA0.5PbI3perovskite‐based PSCs. These PSCs show very high operational stability, with 85% PCE retention upon 1000 h 1 Sun intensity illumination. A 17.33% PCE module (6.5 × 7 cm2) is also demonstrated, attesting to the scalability of such devices.

     
    more » « less
  4. Abstract

    Ultrafast time‐domain thermoreflectance (TDTR) is utilized to extract the through‐plane thermal conductivity (ΛLSCO) of epitaxial La0.5Sr0.5CoO3−δ(LSCO) of varying thickness (<20 nm) on LaAlO3and SrTiO3substrates. These LSCO films possess ordered oxygen vacancies as the primary means of lattice mismatch accommodation with the substrate, which induces compressive/tensile strain and thus controls the orientation of the oxygen vacancy ordering (OVO). TDTR results demonstrate that the room‐temperatureΛLSCOof LSCO on both substrates (1.7 W m−1K−1) are nearly a factor of four lower than that of bulk single‐crystal LSCO (6.2 W m−1K−1). Remarkably, this approaches the lower limit of amorphous oxides (e.g., 1.3 W m−1K−1for glass), with no dependence on the OVO orientation. Through theoretical simulations, origins of the glass‐like thermal conductivity of LSCO are revealed as a combined effect resulting from oxygen vacancies (the dominant factor), Sr substitution, size effects, and the weak electron/phonon coupling within the LSCO film. The absence of OVO dependence in the measuredΛLSCOis rationalized by two main effects: (1) the nearly isotropic phononic thermal conductivity resulting from the imperfect OVO planes when δ is small; (2) the missing electronic contribution toΛLSCOalong the through‐plane direction for these ultrathin LSCO films on insulating substrates.

     
    more » « less
  5. Abstract

    A unique field termination structure combining a three-step field plate with nitrogen ion implantation to enhance the reverse breakdown performance of Pt/β-Ga2O3Schottky barrier diodes (SBDs) and NiO/β-Ga2O3heterojunction diodes (HJDs) is reported. The fabricated devices showed a lowRon,spof 6.2 mΩ cm2for SBDs and 6.8 mΩ cm2for HJDs. HJDs showed a 0.8 V turn-on voltage along with an ideality factor of 1.1 leading to a low effective on-resistance of 18 mΩ cm2. The devices also showed low reverse leakage current (<1 mA cm−2) and a breakdown voltage of ∼1.4 kV. These results offer an alternative, simpler route for fabricating high-performance kilovolt-classβ-Ga2O3diodes.

     
    more » « less