Title: Designing Mechanical Metamaterials with Kirigami‐Inspired, Hierarchical Constructions for Giant Positive and Negative Thermal Expansion
Abstract Advanced mechanical metamaterials with unusual thermal expansion properties represent an area of growing interest, due to their promising potential for use in a broad range of areas. In spite of previous work on metamaterials with large or ultralow coefficient of thermal expansion (CTE), achieving a broad range of CTE values with access to large thermally induced dimensional changes in structures with high filling ratios remains a key challenge. Here, design concepts and fabrication strategies for a kirigami‐inspired class of 2D hierarchical metamaterials that can effectively convert the thermal mismatch between two closely packed constituent materials into giant levels of biaxial/uniaxial thermal expansion/shrinkage are presented. At large filling ratios (>50%), these systems offer not only unprecedented negative and positive biaxial CTE (i.e., −5950 and 10 710 ppm K−1), but also large biaxial thermal expansion properties (e.g., > 21% for 20 K temperature increase). Theoretical modeling of thermal deformations provides a clear understanding of the microstructure–property relationships and serves as a basis for design choices for desired CTE values. An Ashby plot of the CTE versus density serves as a quantitative comparison of the hierarchical metamaterials presented here to previously reported systems, indicating the capability for substantially enlarging the accessible range of CTE.  more » « less
Award ID(s):
1635443
PAR ID:
10448166
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Materials
Volume:
33
Issue:
3
ISSN:
0935-9648
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract Controlling the thermal expansion of ceramic materials is important for many of their applications that involve high-temperature processing and/or working conditions. In this study, we investigate the thermal expansion properties of additively manufactured alumina that is reinforced with boron nitride nanotubes (BNNTs) over a broad temperature range, from room temperature to 900 °C. The coefficient of thermal expansion (CTE) of the BNNT-alumina nanocomposite increases with temperature but decreases with an increase in BNNT loading. The introduction of 0.6% BNNTs results in an approximate 16% reduction in the CTE of alumina. The observed significant CTE reduction of ceramics is attributed to the BNNT’s low CTE and ultrahigh Young’s modulus, and effective interfacial load transfer at the BNNT-ceramic interface. Micromechanical analysis, based onin situRaman measurements, reveals the transition of thermal-expansion-induced interface straining of nanotubes, which shifts from compression to tension inside the ceramic matrix under thermal loadings. This study provides valuable insights into the thermomechanical behavior of BNNT-reinforced ceramic nanocomposites and contributes to the optimal design of ceramic materials with tunable and zero CTE. 
    more » « less
  2. Abstract Tailor‐made materials featuring large tunability in their thermal transport properties are highly sought‐after for diverse applications. However, achieving `user‐defined’ thermal transport in a single class of material system with tunability across a wide range of thermal conductivity values requires a thorough understanding of the structure‐property relationships, which has proven to be challenging. Herein, large‐scale computational screening of covalent organic frameworks (COFs) for thermal conductivity is performed, providing a comprehensive understanding of their structure‐property relationships by leveraging systematic atomistic simulations of 10,750 COFs with 651 distinct organic linkers. Through the data‐driven approach, it is shown that by strategic modulation of their chemical and structural features, the thermal conductivity can be tuned from ultralow (≈0.02 W m−1K−1) to exceptionally high (≈50 W m−1K−1) values. It is revealed that achieving high thermal conductivity in COFs requires their assembly through carbon–carbon linkages with densities greater than 500 kg m−3, nominal void fractions (in the range of ≈0.6–0.9) and highly aligned polymeric chains along the heat flow direction. Following these criteria, it is shown that these flexible polymeric materials can possess exceptionally high thermal conductivities, on par with several fully dense inorganic materials. As such, the work reveals that COFs mark a new regime of materials design that combines high thermal conductivities with low densities. 
    more » « less
  3. Functionally graded materials enable the spatial tailoring of properties through controlling compositions and phases that appear as a function of position within a component. The present study investigates the ability to reduce the coefficient of thermal expansion (CTE) of an aluminum alloy, Al 2219, through additions of Ti-6Al-4V. Thermodynamic simulations were used for phase predictions, and homogenization methods were used for CTE predictions of the bulk CTE of samples spanning compositions between 100 wt% Al 2219 and 70 wt% Al 2219 (balance Ti-6Al-4V) in 10 wt% increments. The samples were fabricated using directed energy deposition (DED) additive manufacturing (AM). Al2Cu and fcc phases were experimentally identified in all samples, and aluminides were shown to form in the samples containing Ti-6Al-4V. Thermomechanical analysis was used to measure the CTE of the samples, which agreed with the predicted CTE values from homogenization methods. The present study demonstrates the ability to tailor the CTEs of samples through compositional modification, thermodynamic calculations, and homogenization methods for property predictions. 
    more » « less
  4. The role of convection in liquid thermoelectric cells may be difficult to predict because the inter- and intramolecular interactions are not currently incorporated into thermodynamic models. Here, we study the thermoelectric response of a series of five anhydrous 1-methyl-3- alkylimidazolium halide ionic liquids with varied chain length and counterion in a high-aspect-ratio, horizontal-temperature-gradient geometry, where convection is minimal. While a canonical constant-volume thermodynamic model predicts that the longer aliphatic groups exhibit larger Seebeck coefficients, we instead measure the opposite: Longer aliphatic chains correlate with lower densities and greater heat expansion, stronger intermolecular associations, stronger steric repulsion, and lower Seebeck coefficients. As evidence of the critical role of thermal expansion, we measure that the Seebeck effect is nonlinear: Values of −2.8 mV/K with a 10 K temperature difference and −1.8 mV/K with a 50 K difference are measured with ether ion. Our results indicate that steric repulsion and heat expansion are important considerations in ionic liquid design; with large temperature differences, the Seebeck coefficient correlates negatively with heat expansion. Our results suggest that Seebeck values will improve if thermal expansion is limited in a pressurized, isochoric, convection-free design. 
    more » « less
  5. Abstract Tailoring thermal transport by structural parameters could result in mechanically fragile and brittle networks. An indispensable goal is to design hierarchical architecture materials that combine thermal and mechanical properties in a continuous and cohesive network. A promising strategy to create such a hierarchical network targets additive manufacturing of hybrid porous voxels at nanoscale. Here we describe the convergence of agile additive manufacturing of porous hybrid voxels to tailor hierarchically and mechanically tunable objects. In one strategy, the uniformly distributed porous silica voxels, which form the basis for the control of thermal transport, are non-covalently interfaced with polymeric networks, yielding hierarchic super-elastic architectures with thermal insulation properties. Another additive strategy for achieving mechanical strength involves the versatile orthogonal surface hybridization of porous silica voxels retains its low thermal conductivity of 19.1 mW m−1 K−1, flexible compressive recovery strain (85%), and tailored mechanical strength from 71.6 kPa to 1.5 MPa. The printed lightweight high-fidelity objects promise thermal aging mitigation for lithium-ion batteries, providing a thermal management pathway using 3D printed silica objects. 
    more » « less