Self‐assembly continuously gains attention as an excellent method to create novel nanoscale structures with a wide range of applications in photonics, optoelectronics, biomedical engineering, and heat transfer applications. However, self‐assembly is governed by a diversity of complex interparticle forces that cause fabricating defectless large scale (>1 cm) colloidal crystals, or opals, to be a daunting challenge. Despite numerous efforts to find an optimal method that offers the perfect colloidal crystal by minimizing defects, it has been difficult to provide physical interpretations that govern the development of defects such as grain boundaries. This study reports the control over grain domains and intentional defect characteristics that develop during evaporative vertical deposition. The degree of particle crystallinity and evaporation conditions is shown to govern the grain domain characteristics, such as shapes and sizes. In particular, the grains fabricated with 300 and 600 nm sphere diameters can be tuned into single‐column structures exceeding ≈1 mm by elevating heating temperature up to 93 °C. The understanding of self‐assembly physics presented in this work will enable the fabrication of novel self‐assembled structures with high periodicity and offer fundamental groundworks for developing large‐scale crack‐free structures.
more » « less- NSF-PAR ID:
- 10461915
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Small
- Volume:
- 15
- Issue:
- 12
- ISSN:
- 1613-6810
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
null (Ed.)Over the last three decades, photonic crystals (PhCs) have attracted intense interests thanks to their broad potential applications in optics and photonics. Generally, these structures can be fabricated via either “top-down” lithographic or “bottom-up” self-assembly approaches. The self-assembly approaches have attracted particular attention due to their low cost, simple fabrication processes, relative convenience of scaling up, and the ease of creating complex structures with nanometer precision. The self-assembled colloidal crystals (CCs), which are good candidates for PhCs, have offered unprecedented opportunities for photonics, optics, optoelectronics, sensing, energy harvesting, environmental remediation, pigments, and many other applications. The creation of high-quality CCs and their mass fabrication over large areas are the critical limiting factors for real-world applications. This paper reviews the state-of-the-art techniques in the self-assembly of colloidal particles for the fabrication of large-area high-quality CCs and CCs with unique symmetries. The first part of this review summarizes the types of defects commonly encountered in the fabrication process and their effects on the optical properties of the resultant CCs. Next, the mechanisms of the formation of cracks/defects are discussed, and a range of versatile fabrication methods to create large-area crack/defect-free two-dimensional and three-dimensional CCs are described. Meanwhile, we also shed light on both the advantages and limitations of these advanced approaches developed to fabricate high-quality CCs. The self-assembly routes and achievements in the fabrication of CCs with the ability to open a complete photonic bandgap, such as cubic diamond and pyrochlore structure CCs, are discussed as well. Then emerging applications of large-area high-quality CCs and unique photonic structures enabled by the advanced self-assembly methods are illustrated. At the end of this review, we outlook the future approaches in the fabrication of perfect CCs and highlight their novel real-world applications.more » « less
-
To translate the exceptional properties of colloidal nanoparticles (NPs) to macroscale geometries, assembly techniques must bridge a 106‐fold range of length. Moreover, for successfully attaining a final mechanically robust nanocomposite macroscale material, some of the intrinsic NPs’ properties have to be maintained while minimizing the density of strength‐limiting defects. However, the assembly of nanoscale building blocks into macroscopic dimensions, and their effective macroscale properties, are inherently affected by the precision of the conditions required for assembly and emergent flaws including point defects, dislocations, grain boundaries, and cracks. Herein, a direct‐write self‐assembly technique is used to construct free‐standing, millimeter‐scale columns comprising spherical iron oxide NPs (15 nm diameter) surface functionalized with oleic acid (OA), which self‐assemble into face‐centered cubic (FCC) supercrystals in minutes during the direct‐writing process. The subsequent crosslinking of OA molecules results in nanocomposites with a maximum strength of 110 MPa and elastic modulus up to 58 GPa. These mechanical properties are interpreted according to the flaw size distribution and are as high as newly engineered platelet‐based nanocomposites. The findings indicate a broad potential to create mechanically robust, multifunctional 3D structures by combining additive manufacturing with colloidal assembly.
-
Abstract Colloidal assembly is an attractive means to control material properties via hierarchy of particle composition, size, ordering, and macroscopic form. However, despite well‐established methods for assembling colloidal crystals as films and patterns on substrates, and within microscale confinements such as droplets or microwells, it has not been possible to build freeform colloidal crystal structures. Direct‐write colloidal assembly, a process combining the bottom‐up principle of colloidal self‐assembly with the versatility of direct‐write 3D printing, is introduced in the present study. By this method, centimeter‐scale, free‐standing colloidal structures are built from a variety of materials. A scaling law that governs the rate of assembly is derived; macroscale structural color is tailored via the size and crystalline ordering of polystyrene particles, and several freestanding structures are built from silica and gold particles. Owing to the diversity of colloidal building blocks and the means to control their interactions, direct‐write colloidal assembly could therefore enable novel composites, photonics, electronics, and other materials and devices.
-
Abstract Linear defect‐disclinations are of fundamental interest in understanding complex structures explored by soft matter physics, elementary particles physics, cosmology, and various branches of mathematics. These defects are also of practical importance in materials applications, such as programmable origami, directed colloidal assembly, and command of active matter. Here an effective engineering approach is demonstrated to pattern molecular orientations at two flat confining surfaces that produce complex yet designable networks of singular disclinations of strength 1/2. Depending on the predesigned director patterns at the bounding plates, the produced disclinations are either surface‐anchored, connecting desired sites at the boundaries, or freely suspended in bulk, forming ordered arrays of polygons and wavy lines. The capability is shown to control the radius of curvature, size, and shape of disclinations by varying uniform alignment orientation on one of these confining plates. The capabilities to precisely design and create highly complex 3D disclination networks promise intriguing applications in stimuli‐responsive reconfigurable materials, directed self‐assembly of molecules, micro‐ and nanoparticles, and transport and sorting in microfluidic applications.
-
Abstract Materials made by directed self‐assembly of colloids can exhibit a rich spectrum of optical phenomena, including photonic bandgaps, coherent scattering, collective plasmonic resonance, and wave guiding. The assembly of colloidal particles with spatial selectivity is critical for studying these phenomena and for practical device fabrication. While there are well‐established techniques for patterning colloidal crystals, these often require multiple steps including the fabrication of a physical template for masking, etching, stamping, or directing dewetting. Here, the direct‐writing of colloidal suspensions is presented as a technique for fabrication of iridescent colloidal crystals in arbitrary 2D patterns. Leveraging the principles of convective assembly, the process can be optimized for high writing speeds (≈600 µm s−1) at mild process temperature (30 °C) while maintaining long‐range (cm‐scale) order in the colloidal crystals. The crystals exhibit structural color by grating diffraction, and analysis of diffraction allows particle size, relative grain size, and grain orientation to be deduced. The effect of write trajectory on particle ordering is discussed and insights for developing 3D printing techniques for colloidal crystals via layer‐wise printing and sintering are provided.