The removal of lead from commercialized perovskite‐oxide‐based piezoceramics has been a recent major topic in materials research owing to legislation in many countries. In this regard, Sn(II)‐perovskite oxides have garnered keen interest due to their predicted large spontaneous electric polarizations and isoelectronic nature for substitution of Pb(II) cations. However, they have not been considered synthesizable owing to their high metastability. Herein, the perovskite lead hafnate, i.e., PbHfO3in space group
The removal of lead from commercialized perovskite‐oxide‐based piezoceramics has been a recent major topic in materials research owing to legislation in many countries. In this regard, Sn(II)‐perovskite oxides have garnered keen interest due to their predicted large spontaneous electric polarizations and isoelectronic nature for substitution of Pb(II) cations. However, they have not been considered synthesizable owing to their high metastability. Herein, the perovskite lead hafnate, i.e., PbHfO3in space group
- NSF-PAR ID:
- 10465057
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Angewandte Chemie
- Volume:
- 136
- Issue:
- 4
- ISSN:
- 0044-8249
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract Pbam , is shown to react with SnClF at a low temperature of 300 °C, and resulting in the first complete Sn(II)‐for‐Pb(II) substitution, i.e. SnHfO3. During this topotactic transformation, a high purity and crystallinity is conserved withPbam symmetry, as confirmed by X‐ray and electron diffraction, elemental analysis, and119Sn Mössbauer spectroscopy. In situ diffraction shows SnHfO3also possesses reversible phase transformations and is potentially polar between ≈130–200 °C. This so‐called ‘de‐leadification’ is thus shown to represent a highly useful strategy to fully remove lead from perovskite‐oxide‐based piezoceramics and opening the door to new explorations of polar and antipolar Sn(II)‐oxide materials. -
more » « less
Abstract Next‐generation electronics and energy technologies can now be developed as a result of the design, discovery, and development of novel, environmental friendly lead (Pb)‐free ferroelectric materials with improved characteristics and performance. However, there have only been a few reports of such complex materials’ design with multi‐phase interfacial chemistry, which can facilitate enhanced properties and performance. In this context, herein, novel lead‐free piezoelectric materials (1‐
x )Ba0.95Ca0.05Ti0.95Zr0.05O3‐(x )Ba0.95Ca0.05Ti0.95Sn0.05O3, are reported, which are represented as (1‐x )BCZT‐(x )BCST, with demonstrated excellent properties and energy harvesting performance. The (1‐x )BCZT‐(x )BCST materials are synthesized by high‐temperature solid‐state ceramic reaction method by varyingx in the full range (x = 0.00–1.00). In‐depth exploration research is performed on the structural, dielectric, ferroelectric, and electro‐mechanical properties of (1‐x )BCZT‐(x )BCST ceramics. The formation of perovskite structure for all ceramics without the presence of any impurity phases is confirmed by X‐ray diffraction (XRD) analyses, which also reveals that the Ca2+, Zr4+, and Sn4+are well dispersed within the BaTiO3lattice. For all (1‐x )BCZT‐(x )BCST ceramics, thorough investigation of phase formation and phase‐stability using XRD, Rietveld refinement, Raman spectroscopy, high‐resolution transmission electron microscopy (HRTEM), and temperature‐dependent dielectric measurements provide conclusive evidence for the coexistence of orthorhombic + tetragonal (Amm2 +P4mm ) phases at room temperature. The steady transition ofAmm2 crystal symmetry toP4mm crystal symmetry with increasingx content is also demonstrated by Rietveld refinement data and related analyses. The phase transition temperatures, rhombohedral‐orthorhombic (TR‐O), orthorhombic‐ tetragonal (TO‐T), and tetragonal‐cubic (TC), gradually shift toward lower temperature with increasingx content. For (1‐x )BCZT‐(x )BCST ceramics, significantly improved dielectric and ferroelectric properties are observed, including relatively high dielectric constantε r≈ 1900–3300 (near room temperature),ε r≈ 8800–12 900 (near Curie temperature), dielectric loss, tanδ ≈ 0.01–0.02, remanent polarizationP r≈ 9.4–14 µC cm−2, coercive electric fieldE c≈ 2.5–3.6 kV cm−1. Further, high electric field‐induced strainS ≈ 0.12–0.175%, piezoelectric charge coefficientd 33≈ 296–360 pC N−1, converse piezoelectric coefficient ≈ 240–340 pm V−1, planar electromechanical coupling coefficientk p≈ 0.34–0.45, and electrostrictive coefficient (Q 33)avg≈ 0.026–0.038 m4C−2are attained. Output performance with respect to mechanical energy demonstrates that the (0.6)BCZT‐(0.4)BCST composition (x = 0.4) displays better efficiency for generating electrical energy and, thus, the synthesized lead‐free piezoelectric (1‐x )BCZT‐(x )BCST samples are suitable for energy harvesting applications. The results and analyses point to the outcome that the (1‐x )BCZT‐(x )BCST ceramics as a potentially strong contender within the family of Pb‐free piezoelectric materials for future electronics and energy harvesting device technologies. -
more » « less
Sn‐based perovskites are promising Pb‐free photovoltaic materials with an ideal 1.3 eV bandgap. However, to date, Sn‐based thin film perovskite solar cells have yielded relatively low power conversion efficiencies (PCEs). This is traced to their poor photophysical properties (i.e., short diffusion lengths (<30 nm) and two orders of magnitude higher defect densities) than Pb‐based systems. Herein, it is revealed that melt‐synthesized cesium tin iodide (CsSnI3) ingots containing high‐quality large single crystal (SC) grains transcend these fundamental limitations. Through detailed optical spectroscopy, their inherently superior properties are uncovered, with bulk carrier lifetimes reaching 6.6 ns, doping concentrations of around 4.5 × 1017cm−3, and minority‐carrier diffusion lengths approaching 1 µm, as compared to their polycrystalline counterparts having ≈54 ps, ≈9.2 × 1018cm−3, and ≈16 nm, respectively. CsSnI3SCs also exhibit very low surface recombination velocity of ≈2 × 103cm s−1, similar to Pb‐based perovskites. Importantly, these key parameters are comparable to high‐performance p‐type photovoltaic materials (e.g., InP crystals). The findings predict a PCE of ≈23% for optimized CsSnI3SCs solar cells, highlighting their great potential.
-
more » « less
Abstract Understanding interfacial reactions that occur between the active layer and charge‐transport layers can extend the stability of perovskite solar cells. In this study, the exposure of methylammonium lead iodide (CH3NH3PbI3) thin films prepared on poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS)‐coated glass to 70% relative humidity (R.H.) leads to a perovskite crystal structure change from tetragonal to cubic within 2 days. Interface‐sensitive photoluminescence measurements indicate that the structural change originates at the PEDOT:PSS/perovskite interface. During exposure to 30% R.H., the same structural change occurs over a much longer time scale (>200 days), and a reflection consistent with the presence of (CH3)2NH2PbI3is detected to coexist with the cubic phase by X‐ray diffraction pattern. The authors propose that chemical interactions at the PEDOT:PSS/perovskite interface, facilitated by humidity, promote the formation of dimethylammonium, (CH3)2NH2+. The partial A‐site substitution of CH3NH3+for (CH3)2NH2+to produce a cubic (CH3NH3)1−
x [(CH3)2NH2]x PbI3phase explains the structural change from tetragonal to cubic during short‐term humidity exposure. When (CH3)2NH2+content exceeds its solubility limit in the perovskite during longer humidity exposures, a (CH3)2NH2+‐rich, hexagonal phase of (CH3NH3)1−x [(CH3)2NH2]x PbI3emerges. These interfacial interactions may have consequences for device stability and performance beyond CH3NH3PbI3model systems and merit close attention from the perovskite research community. -
more » « less
Abstract Recently, the stability of organic–inorganic perovskite thin films under thermal, photo, and moisture stresses has become a major concern for further commercialization due to the high volatility of the organic cations in the prototype perovskite composition (CH3NH3PbI3). All inorganic cesium (Cs) based perovskite is an alternative to avoid the release or decomposition of organic cations. Moreover, substituting Pb with Sn in the organic–inorganic lead halide perovskites has been demonstrated to narrow the bandgap to 1.2–1.4 eV for high‐performance perovskite solar cells. In this work, a series of CsPb1−
x Snx IBr2perovskite alloys via one‐step antisolvent method is demonstrated. These perovskite films present tunable bandgaps from 2.04 to 1.64 eV. Consequently, the CsPb0.75Sn0.25IBr2with homogeneous and densely crystallized morphology shows a remarkable power conversion efficiency of 11.53% and a highV ocof 1.21 V with a much improved phase stability and illumination stability. This work provides a possibility for designing and synthesizing novel inorganic halide perovskites as the next generation of photovoltaic materials.