Metal–organic frameworks (MOFs) and MOF‐derived nanostructures are recently emerging as promising catalysts for electrocatalysis applications. Herein, 2D MOFs nanosheets decorated with Fe‐MOF nanoparticles are synthesized and evaluated as the catalysts for water oxidation catalysis in alkaline medium. A dramatic enhancement of the catalytic activity is demonstrated by introduction of electrochemically inert Fe‐MOF nanoparticles onto active 2D MOFs nanosheets. In the case of active Ni‐MOF nanosheets (Ni‐MOF@Fe‐MOF), the overpotential is 265 mV to reach a current density of 10 mA cm−2in 1
This content will become publicly available on September 26, 2024
Overcoming slow kinetics and high overpotential in electrocatalytic oxygen evolution reaction (OER) requires innovative catalysts and approaches that transcend the scaling relationship between binding energies for intermediates and catalyst surfaces. Inorganic complexes provide unique, customizable geometries, which can help enhance their efficiencies. However, they are unstable and susceptible to chemical reaction under extreme pH conditions. Immobilizing complexes on substrates creates single‐molecule catalysts (SMCs) with functional similarities to single‐atom catalysts (SACs). Here, an efficient SMC, composed of dichloro(1,3‐bis(diphenylphosphino)propane) nickel [NiCl2dppp] anchored to a graphene acid (GA), is presented. This SMC surpasses ruthenium‐based OER benchmarks, exhibiting an ultra‐low onset and overpotential at 10 mAcm−2when exposed to a static magnetic field. Comprehensive experimental and theoretical analyses imply that an interfacial charge transfer from the Ni center in NiCl2dppp to GA enhances the OER activity. Spectroscopic investigations reveal an in situ geometrical transformation of the complex and the formation of a paramagnetic Ni center, which under a magnetic field, enables spin‐selective electron transfer, resulting in enhanced OER performance. The results highlight the significance of in situ geometric transformations in SMCs and underline the potential of an external magnetic field to enhance OER performance at a single‐molecule level.
more » « less- NSF-PAR ID:
- 10465350
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Energy Materials
- Volume:
- 13
- Issue:
- 42
- ISSN:
- 1614-6832
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract m KOH, which is lowered by ≈100 mV after hybridization due to the 2D nanosheet morphology and the synergistic effect between Ni active centers and Fe species. Similar performance improvement is also successfully demonstrated in the active NiCo‐MOF nanosheets. More importantly, the real catalytic active species in the hybrid Ni‐MOF@Fe‐MOF catalyst are unraveled. It is found that, NiO nanograins (≈5 nm) are formed in situ during oxygen evolution reaction (OER) process and act as OER active centers as well as building blocks of the porous nanosheet catalysts. These findings provide new insights into understanding MOF‐based catalysts for water oxidation catalysis, and also shed light on designing highly efficient MOF‐derived nanostructures for electrocatalysis. -
more » « less
Abstract Fe-containing transition-metal (oxy)hydroxides are highly active oxygen-evolution reaction (OER) electrocatalysts in alkaline media and ubiquitously form across many materials systems. The complexity and dynamics of the Fe sites within the (oxy)hydroxide have slowed understanding of how and where the Fe-based active sites form—information critical for designing catalysts and electrolytes with higher activity and stability. We show that where/how Fe species in the electrolyte incorporate into host Ni or Co (oxy)hydroxides depends on the electrochemical history and structural properties of the host material. Substantially less Fe is incorporated from Fe-spiked electrolyte into Ni (oxy)hydroxide at anodic potentials, past the nominally Ni2+/3+redox wave, compared to during potential cycling. The Fe adsorbed under constant anodic potentials leads to impressively high per-Fe OER turn-over frequency (TOFFe) of ~40 s−1at 350 mV overpotential which we attribute to under-coordinated “surface” Fe. By systematically controlling the concentration of surface Fe, we find TOFFeincreases linearly with the Fe concentration. This suggests a changing OER mechanism with increased Fe concentration, consistent with a mechanism involving cooperative Fe sites in FeO
x clusters. -
more » « less
Abstract The large‐scale hydrogen production and application through electrocatalytic water splitting depends crucially on the development of highly efficient, cost‐effective electrocatalysts for oxygen evolution reaction (OER), which, however, remains challenging. Here, a new electrocatalyst of trimetallic Fe–Co–Ni hydroxide (denoted as FeCoNiO
x Hy ) with a nanotubular structure is developed through an enhanced Kirkendall process under applied potential. The FeCoNiOx Hy features synergistic electronic interaction between Fe, Co, and Ni, which not only notably increases the intrinsic OER activity of FeCoNiOx Hy by facilitating the formation of *OOH intermediate, but also substantially improves the intrinsic conductivity of FeCoNiOx Hy to facilitate charge transfer and activate catalytic sites through electrocatalyst by promoting the formation of abundant Co3+. Therefore, FeCoNiOx Hy delivers remarkably accelerated OER kinetics and superior apparent activity, indicated by an ultra‐low overpotential potential of 257 mV at a high current density of 200 mA cm−2. This work is of fundamental and practical significance for synergistic catalysis related to advanced energy conversion materials and technologies. -
more » « less
Abstract Nickel sulfide (Ni3S2) is a promising hydrogen evolution reaction (HER) catalyst by virtue of its metallic electrical conductivity and excellent stability in alkaline medium. However, the reported catalytic activities for Ni3S2are still relatively low. Herein, an effective strategy to boost the H adsorption capability and HER performance of Ni3S2through nitrogen (N) doping is demonstrated. N‐doped Ni3S2nanosheets achieve a fairly low overpotential of 155 mV at 10 mA cm−2and an excellent exchange current density of 0.42 mA cm−2in 1.0
m KOH electrolyte. The mass activity of 16.9 mA mg−1and turnover frequency of 2.4 s−1obtained at 155 mV are significantly higher than the values reported for other Ni3S2‐based HER catalysts, and comparable to the performance of best HER catalysts in alkaline medium. These experimental data together with theoretical analysis suggest that the outstanding catalytic activity of N‐doped Ni3S2is due to the enriched active sites with favorable H adsorption free energy. The activity in the Ni3S2is highly correlated with the coordination number of the surface S atoms and the charge depletion of neighbor Ni atoms. These new findings provide important guidance for future experimental design and synthesis of optimal HER catalysts. -
more » « less
Abstract Transition metal‐nitrogen‐carbon materials with atomically dispersed active sites are promising catalysts for oxygen evolution reaction (OER) since they combine the strengths of both homogeneous and heterogeneous catalysts. However, the canonically symmetric active site usually exhibits poor OER intrinsic activity due to its excessively strong or weak oxygen species adsorption. Here, a catalyst with asymmetric MN4sites based on the 3‐s‐triazine of g‐C3N4(termed as a‐MN4@NC) is proposed. Compared to symmetric, the asymmetric active sites directly modulate the oxygen species adsorption via unifying planar and axial orbitals (d
x 2‐y 2, dz 2), thus enabling higher OER intrinsic activity. In Silico screening suggested that cobalt has the best OER activity among familiar nonprecious transition metal. These experimental results suggest that the intrinsic activity of asymmetric active sites (179 mV overpotential at onset potential) is enhanced by 48.4% compared to symmetric under similar conditions. Remarkably, a‐CoN4@NC showed excellent activity in alkaline water electrolyzer (AWE) device as OER catalyst, the electrolyzer only required 1.7 V and 2.1 V respectively to reach the current density of 150 mA cm−2and 500 mA cm−2. This work opens an avenue for modulating the active sites to obtain high intrinsic electrocatalytic performance including, but not limited to, OER.