Title: Crystallization and melting of polymer chains on graphene and graphene oxide
This study employs all-atomistic (AA) molecular dynamics (MD) simulations to investigate the crystallization and melting behavior of polar and nonpolar polymer chains on monolayers of graphene and graphene oxide (GO). Polyvinyl alcohol (PVA) and polyethylene (PE) are used as representative polar and nonpolar polymers, respectively. A modified order parameter is introduced to quantify the degree of two-dimensional (2D) crystallization of polymer chains. Our results show that PVA and PE chains exhibit significantly different crystallization behavior. PVA chains tend to form a more rounded, denser, and folded-stemmed lamellar structure, while PE chains tend to form an elongated straight pattern. The presence of oxidation groups on the GO substrate reduces the crystallinity of both PVA and PE chains, which is derived from the analysis of modified order parameter. Meanwhile, the crystallization patterns of polymer chains are influenced by the percentage, chemical components, and distribution of the oxidation groups. In addition, our study reveals that 2D crystalized polymer chains exhibit different melting behavior depending on their polarity. PVA chains exhibit a more molecular weight-dependent melting temperature than PE chains, which have a lower melting temperature and are relatively insensitive to molecular weight. These findings highlight the critical role of substrate and chain polarity in the crystallization and melting of polymer chains. Overall, our study provides valuable insights into the design of graphene-based polymer heterostructures and composites with tailored properties.  more » « less
Award ID(s):
2308163 2305529 2331017
NSF-PAR ID:
10465480
Author(s) / Creator(s):
; ; ; ;
Date Published:
Journal Name:
Nanoscale
Volume:
15
Issue:
29
ISSN:
2040-3364
Page Range / eLocation ID:
12235 to 12244
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Combining experimental and computational studies of nanocomposite interfaces is highly needed to gain insight into their performance. However, there are very few literature reports, combining well-controlled atomic force microscopy experiments with molecular dynamic simulations, which explore the role of polymer chemistry and assembly on interface adhesion and shear strength. In this work, we investigate graphene oxide (GO)-polymer interfaces prevalent in nanocomposites based on a nacre-like architectures. We examine the interfacial strength resulting from van der Waals and hydrogen bonding interactions by comparing the out-of-plane separation and in-plane shear deformations of GO-polyethylene glycol (PEG) and GO-polyvinyl alcohol (PVA). The investigation reveals an overall better mechanical performance for the anhydrous GO-PVA system in both out-of-plane and in-plane deformation modes, highlighting the benefits of the donor-acceptor hydrogen bond formation present in GO-PVA. Such bond formation results in interchain hydrogen bond networks leading to stronger interfaces. By contrast, PEG, a hydrogen bond acceptor only, relies primarily on van der Waals inter-chain interactions, typically resulting in weaker interactions. The study also predicts that water addition increases the adhesion of GOPEG but decreases the adhesion of GO-PVA, and slightly increases the shear strength in both systems. Furthermore, by comparing simulations and experiments, we show that the CHARMM force field has enough accuracy to capture the effect of polymer content, water distribution, and to provide quantitative guidance for achieving optimum interfacial properties. Therefore, the study demonstrates an effective methodology, in the Materials Genome spirit, toward the design of 2D materials-polymer nanocomposites system for applications demanding mechanical robustness. 
    more » « less
  2. The performance of sustainable polymers can be modified and enhanced by incorporating functional groups in the backbone of the polymer chain that increases intermolecular interactions, thus impacting the thermal properties of the material. However, in-depth studies on the role of intermolecular interactions on the crystallization of these polymers are still needed. This work aims to ascertain whether incorporating functional groups able to induce intermolecular interactions can be used as a suitable systematic strategy to modify the polymer thermal properties and crystallization kinetics. Thus, amide and additional ester groups have been incorporated into aliphatic polyesters (PEs). The impact of intermolecular interactions on the melting and crystallization behavior, crystallization kinetics, and crystalline structure has been determined. Functional groups that form strong intermolecular interactions increase both melting and crystallization temperatures but retard the crystallization kinetics. Selecting appropriate functional groups allows tuning the crystallinity degree, which can potentially improve the mechanical properties and degradability in semicrystalline materials. The results demonstrate that it is possible to tune the thermal transitions and the crystallization kinetics of PEs independently by varying their chemical structure. 
    more » « less
  3. Abstract

    Mechanical stacking of two dissimilar materials often has surprising consequences for heterostructure behavior. In particular, a 2D electron gas (2DEG) is formed in the heterostructure of the topological crystalline insulator Pb0.24Sn0.76Te and graphene due to contact of a polar with a nonpolar surface and the resulting changes in electronic structure needed to avoid polar catastrophe. The spintronic properties of this heterostructure with non‐local spin valve devices are studied. This study observes spin‐momentum locking at lower temperatures that transitions to regular spin channel transport only at ≈40 K. Hanle spin precession measurements show a spin relaxation time as high as 2.18 ns. Density functional theory calculations confirm that the spin‐momentum locking is due to a giant Rashba effect in the material and that the phase transition is a Lifshitz transition. The theoretically predicted Lifshitz transition is further evident in the phase transition‐like behavior in the Landé g‐factor and spin relaxation time.

     
    more » « less
  4. Interfacial thermal transport is a critical physical process determining the performance of many material systems with small-scale features. Recently, self-assembled monolayers and polymer brushes have been widely used to engineer material interfaces presenting unprecedented properties. Here, we demonstrate that poly(vinyl alcohol) (PVA) monolayers with hierarchically arranged hydrogen bonds drastically enhance interfacial thermal conductance by a factor of 6.22 across the interface between graphene and poly(methyl methacrylate) (PMMA). The enhancement is tunable by varying the number of grafted chains and the density of hydrogen bonds in the unique hierarchical hydrogen bond network. The extraordinary enhancement results from a synergy of hydrogen bonds and other structural and thermal factors including molecular morphology, chain orientation, interfacial vibrational coupling and heat exchange. Two types of hydrogen bonds, i.e. PVA–PMMA hydrogen bonds and PVA–PVA hydrogen bonds, are analyzed and their effects on various structural and thermal properties are systematically investigated. These results are expected to provide new physical insights for interface engineering to achieve tunable thermal management and energy efficiency in a wide variety of systems involving polymers and biomaterials. 
    more » « less
  5. Abstract. The impact of molecular level surface chemistry for aerosol water-uptake and droplet growth is not well understood. In this work, spherical, nonporous, monodisperse polystyrene latex (PSL) particles treated with different surface functional groups are exploited to isolate the effects of aerosol surface chemistry for droplet activation. PSL is effectively water insoluble and changes in the particle surface may be considered acritical factor in the initial water uptake of water-insoluble material. The droplet growth of two surface modified types of PSL (PSL-NH2 andPSL-COOH) along with plain PSL was measured in a supersaturated environmentwith a Cloud Condensation Nuclei Counter (CCNC). Three droplet growth models – traditional Köhler (TK), Flory–Huggins Köhler (FHK) and the Frenkel–Halsey–Hill adsorption theory (FHH-AT) were compared with experimental data. The experimentally determined single hygroscopicity parameter, κ, was found within the range from 0.002 to 0.04. The traditional Köhler prediction assumes Raoult's law solute dissolution and underestimates the water-uptake ability of the PSL particles. FHK can be applied to polymeric aerosol; however, FHK assumes that the polymer is soluble and hydrophilic. Thus, the FHK model generates a negative result for hydrophobic PSL and predicts non-activation behavior that disagrees with the experimental observation. The FHH-AT model assumes that a particle is water insoluble and can be fit with two empirical parameters (AFHH and BFHH). The FHH-AT prediction agrees with the experimental data and can differentiate the water uptake behavior of the particles owing to surface modification of PSL surface. PSL-NH2 exhibits slightly higher hygroscopicity than the PSL-COOH, whereas plain PSL is the least hygroscopic among the three. This result is consistent with the polarity of surface functional groups and their affinity to water molecules. Thus, changes in AFHH and BFHH can be quantified when surface modification is isolated for the study of water-uptake. The fitted AFHH for PSL-NH2, PSL-COOH, and plain PSL is 0.23, 0.21, and 0.18 when BFHH is unity. To simplify the use of FHH-AT for use in cloud activation models, we also present and test a new single parameter framework for insoluble compounds, κFHH. κFHH is within 5 % agreement ofthe experimental data and can be applied to describe a single-parameterhygroscopicity for water-insoluble aerosol with surface modified properties. 
    more » « less