Title: Evolution of Yb 3+ Speciation in Cl – /Br – - and Yb 3+ /Gd 3+ -Alloyed Quantum-Cutting Lead-Halide Perovskite Nanocrystals
Award ID(s):
1719797 2308979
NSF-PAR ID:
10469279
Author(s) / Creator(s):
; ; ; ;
Publisher / Repository:
Chemistry of Materials
Date Published:
Journal Name:
Chemistry of Materials
Volume:
35
Issue:
19
ISSN:
0897-4756
Page Range / eLocation ID:
8057 to 8064
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. null (Ed.)
  2. Broadband near infrared (NIR) emission materials are of interest for various applications including non-destructive biomedical imaging. In this work, ytterbium ions (Yb 3+ ) were successfully doped into Cs 2 AgInCl 6 :Cr 3+ (CAIC:Cr 3+ ) double perovskite single crystals (DPSCs) by a facile hydrothermal method. Under 365 nm excitation, the co-doped CAIC:Cr 3+ ,Yb 3+ DPSCs showed broad NIR emission ranging from 800 to 1400 nm, which spanned the NIR-I (700–900 nm) and NIR-II (1000–1700 nm) bio-windows, with an emission band at 1000 nm and a full-width at half maximum (FWHM) of 188 nm. It is found that Yb 3+ ion doping could effectively improve the photoluminescence (PL) performance of CAIC:Cr 3+ DPSCs. Compared to the photoluminescence quantum yield (PLQY) of 22.5% for the single doped CAIC:Cr 3+ , the co-doped CAIC:Cr 3+ ,Yb 3+ DPSCs show a higher PLQY of ∼45%, which is attributed to the synergistic effect of reduced non-radiative recombination due to defect passivation and increase in crystallinity, and energy transfer (ET) of self-trapped excitons (STEs) to Cr 3+ . As a demonstration of applications, NIR pc-LEDs were fabricated by combining the as-synthesized NIR-emitting phosphor CAIC:Cr 3+ ,Yb 3+ with InGaN UV chips ( λ em = 365 nm) and used to image veins in a palm and for night vision using a NIR camera. The results suggest that the synthesized CAIC:Cr 3+ ,Yb 3+ DPSCs have great potential in biological applications. 