Abstract Hf 0.5 Zr 0.5 O 2 (HZO) thin films are promising candidates for non-volatile memory and other related applications due to their demonstrated ferroelectricity at the nanoscale and compatibility with Si processing. However, one reason that HZO has not been fully scaled into industrial applications is due to its deleterious wake-up and fatigue behavior which leads to an inconsistent remanent polarization during cycling. In this study, we explore an interfacial engineering strategy in which we insert 1 nm Al 2 O 3 interlayers at either the top or bottom HZO/TiN interface of sequentially deposited metal-ferroelectric-metal capacitors. By inserting an interfacial layer while limiting exposure to the ambient environment, we successfully introduce a protective passivating layer of Al 2 O 3 that provides excess oxygen to mitigate vacancy formation at the interface. We report that TiN/HZO/TiN capacitors with a 1 nm Al 2 O 3 at the top interface demonstrate a higher remanent polarization (2P r ∼ 42 μ C cm −2 ) and endurance limit beyond 10 8 cycles at a cycling field amplitude of 3.5 MV cm −1 . We use time-of-flight secondary ion mass spectrometry, energy dispersive spectroscopy, and grazing incidence x-ray diffraction to elucidate the origin of enhanced endurance and leakage properties in capacitors with an inserted 1 nm Al 2 O 3 layer. We demonstrate that the use of Al 2 O 3 as a passivating dielectric, coupled with sequential ALD fabrication, is an effective means of interfacial engineering and enhances the performance of ferroelectric HZO devices.
more »
« less
Impact of Electric Field Pulse Duration on Ferroelectric Hafnium Zirconium Oxide Thin Film Capacitor Endurance
While ferroelectric HfO2shows promise for use in memory technologies, limited endurance is one factor that challenges its widespread application. Herein, endurance is investigated through field cycling W/Hf0.5Zr0.5O2/W capacitors above the coercive field while manipulating the time under field using bipolar pulses of varying pulse duration or duty cycle. Both remanent polarization and leakage current increase with increasing pulse duration. Additionally, an order of magnitude decrease in the pulse duration from 20 to 2 μs results in an increase in endurance lifetime of nearly two orders of magnitude from 3 × 106to 2 × 108cycles. These behaviors are attributed to increasing time under field allowing for charged oxygen vacancy migration, initially unpinning domains, or driving phase transformations before segregating to grain boundaries and electrode interfaces. This oxygen vacancy migration causes increasing polarization before creating conducting percolation paths that result in degradation and premature device failure. This process is suppressed for 2 μs pulse duration field cycling where minimal wake‐up and lower leakage before device failure are observed, suggesting that very short pulses can be used to significantly increase device endurance. These results provide insight into the impact of pulse duration on device performance and highlight consideration of use of conditions when endurance testing.
more »
« less
- PAR ID:
- 10475417
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- physica status solidi (a)
- ISSN:
- 1862-6300
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Layered oxide cathode with a Li‐O‐vacancy configuration offers high capacity by leveraging additional oxygen redox reactions. However, it faces severe challenges of sluggish kinetics of oxygen redox reactions and lattice oxygen loss, resulting in slow Li+diffusion and rapid electrochemical degradation. Herein, Ti is introduced as electrochemical inactive element into Li‐O‐vacancy configuration to form Mn/vacancy/Ti arrangement within transition metal layers of layered oxide, achieving a marked increase in average output voltage at high current density compared with Ti‐free counterpart. Not only voltage hysteresis between charge and discharge processes can be significantly reduced, but rate capability can be heightened in Li4/7[□1/7Ti1/7Mn5/7]O2by means of retrained over‐potential and improved Li+diffusivity. Furthermore, theoretical calculations suggest that these improvements stem from Ti substitution, which elongates the Li─O bond and lowers the Li+migration energy barrier. Besides, in situ differential electrochemical mass spectrometry and soft X‐ray absorption spectroscopy reveal the modified Li‐O‐vacancy configuration enables reversible anionic and cationic redox behaviors during cycling. These findings provide a promising strategy for tailoring oxygen redox activity and accelerating Li+diffusion kinetics in layered cathode materials with oxygen redox chemistry.more » « less
-
Abstract Warming‐induced changes in precipitation regimes, coupled with anthropogenically enhanced nitrogen (N) deposition, are likely to increase the prevalence, duration, and magnitude of soil respiration pulses following wetting via interactions among temperature and carbon (C) and N availability. Quantifying the importance of these interactive controls on soil respiration is a key challenge as pulses can be large terrestrial sources of atmospheric carbon dioxide (CO2) over comparatively short timescales. Using an automated sensor system, we measured soil CO2flux dynamics in the Colorado Desert—a system characterized by pronounced transitions from dry‐to‐wet soil conditions—through a multi‐year series of experimental wetting campaigns. Experimental manipulations included combinations of C and N additions across a range of ambient temperatures and across five sites varying in atmospheric N deposition. We found soil CO2pulses following wetting were highly predictable from peak instantaneous CO2flux measurements. CO2pulses consistently increased with temperature, and temperature at time of wetting positively correlated to CO2pulse magnitude. Experimentally adding N along the N deposition gradient generated contrasting pulse responses: adding N increased CO2pulses in low N deposition sites, whereas adding N decreased CO2pulses in high N deposition sites. At a low N deposition site, simultaneous additions of C and N during wetting led to the highest observed soil CO2fluxes reported globally at 299.5 μmol CO2 m−2 s−1. Our results suggest that soils have the capacity to emit high amounts of CO2within small timeframes following infrequent wetting, and pulse sizes reflect a non‐linear combination of soil resource and temperature interactions. Importantly, the largest soil CO2emissions occurred when multiple resources were amended simultaneously in historically resource‐limited desert soils, pointing to regions experiencing simultaneous effects of desertification and urbanization as key locations in future global C balance.more » « less
-
We report thermal and mechanical responses accompanying electrical characteristics of depletion mode GaN high electron mobility transistors exposed to gamma radiation up to 107rads. Changes in the lattice strain and temperature were simultaneously characterized by changes in the phonon frequency of E2(high) and A1(LO) from the on-state and unpowered/pinched off reference states. Lower doses of radiation improved electrical properties; however, degradation initiated at about 106rads. We observed about 16% decrease in the saturation current and 6% decrease in the transconductance at the highest dose. However, a leakage current increase by three orders of magnitude was the most notable radiation effect. We observed temperature increase by 40% and mechanical stress increase by a factor of three at a dose of 107rads compared to the pristine devices. Spatial mapping of mechanical stress along the channel identifies the gate region as a mechanically affected area, whereas the thermal degradation was mostly uniform. Transmission electron microscopy showed contrast changes reflecting a high vacancy concentration in the gate region. These findings suggest that localized stress (mechanical hotspots) may increase vulnerability to radiation damage by accommodating higher concentration of defects that promote the leakage current.more » « less
-
Abstract Chalcogenide optical phase change materials (PCMs) have garnered significant interest for their growing applications in programmable photonics, optical analog computing, active metasurfaces, and beyond. Limited endurance or cycling lifetime is however increasingly becoming a bottleneck toward their practical deployment for these applications. To address this issue, a systematic study elucidating the cycling failure mechanisms of Ge2Sb2Se4Te (GSST) is performed, a common optical PCM tailored for infrared photonic applications, in an electrothermal switching configuration commensurate with their applications in on‐chip photonic devices. Further a set of design rules building on insights into the failure mechanisms is proposed, and successfully implemented them to boost the endurance of the Ge2Sb2Se4Te (GSST) device to over 67 000 cycles.more » « less