Biomass–fungi composite materials primarily consist of biomass particles (sourced from agricultural residues) and a network of fungal hyphae that bind the biomass particles together. These materials have potential applications across diverse industries, such as packaging, furniture, and construction. 3D printing offers a new approach to manufacturing parts using biomass–fungi composite materials, as an alternative to traditional molding-based methods. However, there are challenges in producing parts with desired quality (for example, geometric accuracy after printing and height shrinkage several days after printing) by using 3D printing-based methods. This paper introduces an innovative approach to enhance part quality by incorporating ionic crosslinking into the 3D printing-based methods. While ionic crosslinking has been explored in hydrogel-based bioprinting, its application in biomass–fungi composite materials has not been reported. Using sodium alginate (SA) as the hydrogel and calcium chloride as the crosslinking agent, this paper investigates their effects on quality (geometric accuracy and height shrinkage) of 3D printed samples and physiochemical characteristics (rheological, chemical, and texture properties) of biomass–fungi composite materials. Results show that increasing SA concentration led to significant improvements in both geometric accuracy and height shrinkage of 3D printed samples. Moreover, crosslinking exposure significantly enhanced hardness of the biomass–fungi mixture samples prepared for texture profile analysis, while the inclusion of SA notably improved cohesiveness and springiness of the biomass–fungi mixture samples. Furthermore, Fourier transform infrared spectroscopy confirms the occurrence of ionic crosslinking within 3D printed samples. Results from this study can be used as a reference for developing new biomass–fungi mixtures for 3D printing in the future.
- Award ID(s):
- 2134488
- PAR ID:
- 10481927
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Cement and Concrete Research
- Volume:
- 175
- Issue:
- C
- ISSN:
- 0008-8846
- Page Range / eLocation ID:
- 107380
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
more » « less
To combat climate change, one approach is to manufacture products from biomass-fungi composite materials instead of petroleum-based plastics. These products can be used in packaging, furniture, and construction industries. A 3D printing-based manufacturing method was developed for these biomass-fungi composite materials, eliminating the need for molds, and enabling customized product design. However, previous studies on the 3D printing-based method showed significant shrinkage of printed samples. In this paper, an approach is proposed to reduce the shrinkage by incorporating ionic crosslinking into biomass-fungi composite materials. This paper reports two sets of experiments regarding the effects of sodium alginate (SA) and calcium chloride (CaCl2) on fungal growth and fungal viability. The first set of experiments was conducted using Petri dishes with fungi isolated from colonized biomass-fungi material and different concentrations of SA and CaCl2. Fungal growth was measured by the circumference of fungal colonies. The results showed that concentrations of SA and CaCl2 had significant effects on fungal growth and no fungal growth was observed on Petri dishes with 15% CaCl2. Some of these Petri dishes were also observed under confocal microscopy. The results confirmed the differences obtained by measuring the circumference of fungal colonies. The second set of experiments was conducted using Petri dishes with biomass-fungi mixtures that were treated with different concentrations of SA and exposure times in a CaCl2 (crosslinking) solution. Fungal viability was measured by counting colony-forming units. The results showed that the addition of the SA solution and exposure times in the crosslinking solution had statistically significant effects on fungal viability. The 2SA solution was prepared by dissolving 2 g of SA in 100 mL of water, the 5SA solution was prepared by dissolving 5 g of SA in 100 mL of water, and the crosslinking solution was prepared by dissolving 5 g of CaCl2 in 100 mL of water. The results also showed that fungal viability was not too low in biomass-fungi mixtures that included 2SA solution and were exposed to the crosslinking solution for 1 min.
-
Amziane, S. ; Merta, I. ; Page, J. (Ed.)Sustainable earthen building materials provide a pathway to mitigating the environmental impacts of the modern construction sector. While the application of these materials has been limited due to the inherent heterogeneity, erosivity, and weak mechanical properties of soil, the physical and thermal properties can be improved through the addition of ubiquitous, non-toxic, sustainable biopolymers. Yet, the fundamental understanding of the physiochemical bonding mechanisms between clays and biopolymers in this system is limited. In this work, a ‘micro to macro’ methodological approach was applied to investigate the bonding characteristics of common clays and clay-stabilizing biopolymers. At the micro-scale, fundamental interactions of clays (i.e., kaolinite, bentonite) with biopolymer additives (i.e., xanthan gum, guar gum, sodium alginate, microcrystalline cellulose) were assessed through mineral binding characterization techniques, including Fourier-transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). The findings were used to interpret unconfined compressive strength (UCS) tests results for macro-scale soil-biopolymer composites samples (1% biopolymer by soil mass). The results from this study illustrate the utility of understanding the mechanisms of clay-biopolymer interactions for improving the design of strong and durable earthen materials and structures.more » « less
-
null (Ed.)more » « less
Abstract Following the success of 3D printing with synthetic polymers like ABS, FLA, Nylon, etc., scientists and researchers have been putting efforts into fabricating bio-compatible materials. It has not only broadened the field of bioengineering and manufacturing but also regenerative medicine. Unlike the traditional 3D printing process, additive bio-manufacturing, also known as 3D bio-printing has a lot of challenges like cell survivability and proliferation, and the mechanical properties of the biomaterials which involve printability and the ability to hold its structural integrity. Proper design of experiments with extensive rheological investigation can help identify useful mechanical property ranges which are directly related to the geometric fidelity of 3D bio-printed scaffolds. Therefore, to investigate the printability of a low viscosity Alginate-Carboxymethyl Cellulose (CMC), multiple concentrations of the mixture were tested maintaining a 8% (w/v) solid content. A set of rheological tests such as the Steady Rate Sweep Test, Three Point Thixotropic Test (3ITT), and Amplitude test were performed. The outcome of those tests showed that the rheological properties can be controlled with the percentage of CMC in the mixtures. The fabricated filaments and scaffolds in the 5 combinations of CMC percentages were analyzed for flowability and shape fidelity. The rheological results and the printability and shape fidelity results were analyzed.
-
more » « less
Abstract 3D bioprinting improves orientation of
in vitro tumor models by offering layer by layer positioning of cancer cells and cancer associated fibroblasts (CAFs) which can replicate tumor microenvironment. Aim of this study was to develop a sodium alginate -gelatin (SA-GL) hydrogel by optimizing rheological parameters to print non-small cell lung cancer (NSCLC) patient derived xenograft (PDX) cells and lung CAFs co-cultures. SA-GL hydrogels were prepared, and rheological properties were evaluated. Both the cells were mixed with the hydrogel and printed using INKREDIBLE bioprinter. Hydrogels prepared with 3.25% and 3.5% (w/v) SA and 4% (w/v) GL showed higher printability and cell viability. A significant decline in viscosity with shear rate was observed in these hydrogels suggesting the shear thinning property of hydrogels. Spheroid size distribution after 15 days was in the diameter range of 50–1100 µm. Up-regulation of vimentin, α-SMA and loss of E-cadherin in co-culture spheroids confirmed cellular crosstalk. This study demonstrates that rheological optimization of SA-GL hydrogel enhances printability and viability of NSCLC PDX and CAF co-culture which allows 3D co-culture spheroid formation within the printed scaffold. Therefore, this model can be used for studying high throughput drug screening and other pre-clinical applications.
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1016/j.cemconres.2023.107380