skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • NSF Public Access
  • Search Results
  • Enhancing the Interlaminar Shear Strength and Void Control of 3D-Printed Continuous Carbon-Fiber-Reinforced Polymer Composites Using a Robotic Magnetic Compaction Force-Assisted Additive Manufacturing (MCFA-AM) Process and Carbon-Nanofiber Z-Threads
Title: Enhancing the Interlaminar Shear Strength and Void Control of 3D-Printed Continuous Carbon-Fiber-Reinforced Polymer Composites Using a Robotic Magnetic Compaction Force-Assisted Additive Manufacturing (MCFA-AM) Process and Carbon-Nanofiber Z-Threads
Three-dimensional (3D) printing with continuous carbon-fiber-reinforced polymer (C-CFRP) composites is under increasing development, as it offers more versatility than traditional molding processes, such as the out-of-autoclave-vacuum bag only (OOA-VBO) process. However, due to the layer-by-layer deposition of materials, voids can form between the layers and weaken some of the parts’ properties, such as the interlaminar shear strength (ILSS). In this paper, a novel mold-less magnetic compaction force-assisted additive manufacturing (MCFA-AM) method was used to print carbon nanofiber (CNF) z-threaded CFRP (ZT-CFRP) laminates with significantly improved ILSS and reduced void content compared to traditional C-CFRP laminates, which are printed using a no-pressure 3D-printing process (similar to the fused-deposition-modeling process). The radial flow alignment (RFA) and resin-blending techniques were utilized to manufacture a printing-compatible fast-curing ZT-CFRP prepreg tape to act as the feedstock for a MCFA-AM printhead, which was mounted on a robotic arm. In terms of the ILSS, the MCFA-AM method coupled with ZT-CFRP nanomaterial technology significantly outperformed the C-CFRP made with both the traditional no-pressure 3D-printing process and the OOA-VBO molding process. Furthermore, the mold-less MCFA-AM process more than doubled the production speed of the OOA-VBO molding process. This demonstrates that through the integration of new nanomaterials and 3D-printing techniques, a paradigm shift in C-CFRP manufacturing with significantly better performance, versatility, agility, efficiency, and lower cost is achievable.  more » « less
Award ID(s):
2044513
PAR ID:
10482576
Author(s) / Creator(s):
; ; ;
Editor(s):
Manoj Gupta
Publisher / Repository:
MDPI
Date Published:
Journal Name:
Applied Sciences
Volume:
13
Issue:
10
ISSN:
2076-3417
Page Range / eLocation ID:
5914
Subject(s) / Keyword(s):
magnetic compaction force-assisted additive manufacturing (MCFA-AM) carbon-nanofiber z-threaded cfrp (ZT-CFRP) continuous carbon-fiber-reinforced polymer (C-CFRP) composite short-beam shear test interlaminar shear strength (ILSS) void compaction pressure fast-curing resin
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; (, CAMX 2023 Technical Proceedings)
    The matrix sensitive weaknesses of Carbon Fiber Reinforced Polymer (CFRP) laminates are usually magnified by mainstream additive manufacturing (AM) methods due to the AM-process-induced voids and defects. In this paper, a novel Magnetic Compaction Force Assisted-Additive Manufacturing (MCFA-AM) method is used to print Carbon Nanofibers (CNF) Z-threaded CFRP (i.e., ZT-CFRP) composite laminates. The MCFA-AM method utilizes a magnetic force to simultaneously support, deposit, and compact Continuous Carbon Fiber Reinforced Polymer (C-CFRP) composites in free space and quickly solidifies the CFRP part without any mold; it effectively reduces the voids. Past research proved that the zig-zag threading pattern of the CNF z-threads reinforces the interlaminar and intralaminar regions in the ZT-CFRP laminates manufactured by the traditional Out of Autoclave-Vacuum Bag Only (OOA-VBO) method, and enhances the matrix sensitive mechanical, thermal, and electrical properties. In this study, the longitudinal compressive test (ASTM D695, i.e., SACMA SRM 1R-94) was performed on the MCFA-AM printed ZT-CFRP laminate. The results were compared with unaligned CNF-modified CFRP (UA-CFRP), control CFRP, and no-pressure CFRP samples’ data to investigate the impact of the CNF z-threads and MCFA-AM process on the CFRP’s performance. The 0.5-bar MCFA-AM printed ZT-CFRP showed comparable longitudinal compressive strength with the 1-bar OOA-VBO cured CFRP. 
    more » « less
  2. ; ; ; ; (, Materials)
    Carbas, Ricardo JC (Ed.)
    Low fiber-direction compressive strength is a well-recognized weakness of carbon fiber-reinforced polymer (CFRP) composites. When a CFRP is produced using 3D printing, the compressive strength is further degraded. To solve this issue, in this paper, a novel magnetic compaction force-assisted additive manufacturing (MCFA-AM) method is used to print CFRP laminates reinforced with carbon nanofiber (CNF) z-threads (i.e., ZT-CFRP). MCFA-AM utilizes a magnetic force to simultaneously levitate, deposit, and compact fast-curing CFRP prepregs in free space and quickly solidifies the CFRP laminate part without any mold nor supporting substrate plate; it effectively reduces the voids. The longitudinal compressive test was performed on five different sample types. ZT-CFRP/MCFA-AM samples were printed under two different magnetic compaction rolling pressures, i.e., 0.5 bar and 0.78 bar. Compared with the longitudinal compressive strength of a typical CFRP manufactured by the traditional out-of-autoclave–vacuum-bag-only (OOA-VBO) molding process at the steady-state pressure of 0.82 bar, the ZT-CFRP/MCFA-AM samples showed either comparable results (by −1.00% difference) or enhanced results (+7.42% improvement) by using 0.5 bar or 0.78 bar magnetic rolling pressures, respectively. 
    more » « less
  3. ; ; (, International Conference on Composite Materials (ICCM))
    Previous studies have shown that carbon nanofiber (CNF) z-threaded carbon fiber-reinforced polymer (ZT-CFRP) laminates exhibit improved mechanical performance in comparison to traditional carbon fiber-reinforced polymer (CFRP) laminates when exposed to extreme elevated temperatures. Z-threaded reinforcement is a technique for strengthening the through-thickness of a laminate by introducing perpendicularly aligned carbon nanomaterial to be threading into the continuous fiber array. Improved performance has already been observed in properties such as interlaminar shear strength (ILSS) without extreme heat exposure, but there has also been evidence that z-thread inclusion may mitigate strength loss due to thermal degradation of the matrix. This study examined how ILSS was diminished in both CFRP and ZT-CFRP samples with matrix degradation caused by extreme temperature exposure. Test samples were heated to 350 ˚C for 10 minutes and then allowed to return to room temperature. SBS testing in accordance with ASTM D2344 was conducted on both untreated and heat-treated samples for comparison. All samples were at room temperature during testing. It was found that ZT-CFRP samples (with 0.5wt% CNF concentration the matrix) exhibited higher ILSS with and without heat treatment over the traditional CFRP samples with and without heat treatment by +33.96% and +25.12%, respectively. ZT-CFRP ILSS was found to decrease by 10.584 MPa (-14.56%) after the extreme heat treatment, while CFRP ILSS decreased by only 4.627 MPa (-8.53%). Microscopic image analysis was also performed to provide insight into how the CNF z-threads may have provided a mechanism for retaining ILSS performance even with matrix thermal degradation. 
    more » « less
  4. ; ; (, Society for the Advancement of Material and Process Engineering)
    Previously reported vertical UL-94 testing results showed that carbon nanofiber z-threaded carbon fiber-reinforced polymer (ZT-CFRP) laminates have significantly improved flame resistance capabilities compared to traditional carbon fiber-reinforced (CFRP) laminates. Shorter flame self-extinguishing times and no flame propagation were reported. These characteristics provided evidence that ZT-CFRP’s unique microstructure, combined with its inherent strengthened mechanical, thermal, and electrical properties, has the potential to have more favorable high-temperature applications than traditional CFRP. This study examined the interlaminar shear strength (ILSS) enhancement of ZT-CFRP laminates, in comparison to traditional CFRP, when exposed to gradually increased temperatures. This was accomplished through the use of a furnace and an in-house constructed three-point bending apparatus capable of supplying static loading to determine the temperature at which failure occurred. The apparatus was loaded with a specimen and then placed inside the furnace where the temperature was allowed to increase based upon a consistent heating schedule. It was observed that ZT-CFRP samples had an approximately 30 ˚C improvement in temperature handling capabilities while exposed to an interlaminar shear load when compared to CFRP samples. Microscopic image analysis was also performed to observe how CNF z-threads contributed to the improved performance observed for ZT-CFRP at extreme elevated temperatures. 
    more » « less
  5. ; ; ; (, SAMPE 2022 Conference Proceedings, Charlotte, NA, May 23-26, 2022)
    Moisture is a known issue for carbon fiber reinforced polymer (CFRP) manufacturing. During the process, in which a CFRP prepreg is carefully thawed, cut, stacked, and cured into a laminate, any bad moisture control can cause voids, affect the curing, and degrade the laminate. Recent studies of carbon nanofiber z-threaded CFRP (i.e., ZT-CFRP) prepreg and its laminates showed significant multifunctional improvements in the mechanical strengths, toughness, thermal conductivity, and electrical conductivity. The carbon nanofibers zig-zag thread among the carbon fibers in the through-thickness direction (i.e., z-direction) and mechanically interlock the fiber system together to form an effective 3D-fiber-network reinforced laminate. This paper presents a preliminary experimental study on the ZT-CFRP prepreg when facing the moisture exposure during the prepreg handling and lamination process. Both the ZT-CFRP and traditional CFRP prepregs, subjected to different humidity conditions, will be cut, and cured into laminate samples. The samples will be tested for their interlaminar shear strengths (ILSS) and hardness. Microscope pictures of the samples' fracture patterns will be compared for explaining the combined impact of the moistures and the carbon nanofiber z-threading strategy on the laminates' interlaminar shear strength and curing state. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email