There is a strong interest in increasing the frequency response of electrochemical capacitors (ECs) from typically less than 1 Hz to the hundreds or the kilo Hz range, so that such high-frequency ECs (HF-ECs) could replace conventional capacitors for AC line-frequency filtering and other capacitor applications. The development of such HF-ECs is hindered by their typically low capacitance density and operation voltage. Herein, by treating ZIF-67 particulate films in CH 4 /H 2 plasma, edge-oriented graphene (EOG) formed around the carbonized ZIF-67 particulate skeleton, and this EOG was coupled with carbon nanotubes (CNTs) that were grown with the aid of Co catalyst nanoparticles, which were generated by reducing the Co 2+ ions associated with ZIF in the plasma. Used as electrodes, these EOG/CNT/carbonized ZIF-67 composites exhibited a large electrode areal capacitance of 1.0 mF cm −2 and an excellent frequency response of −84° phase angle at 120 Hz in aqueous electrolyte cells, whereas values of 0.67 mF cm −2 and −78° for the electrode areal capacitance and the phase angle at 120 Hz, respectively, were obtained in organic electrolyte cells with the operation voltage of 2.5 V. Using three pairs of electrodes stacked together, a single integrated cell operating at 7.5 V and having a characteristic frequency of ∼3.8 kHz at −45° phase angle, was demonstrated. These results suggest the potential to use this EOG/CNT/carbonized ZIF-67 composite structure for developing HF-ECs.
more »
« less
This content will become publicly available on October 17, 2024
MoS 2 Nanoflakes based Kilohertz Electrochemical Capacitors
An ultra‐fast electrochemical capacitor (EC) designed for efficient ripple current smoothing was fabricated using vertically oriented MoS2(VOM) nanoflakes deposited on freestanding carbonized cellulose (CC) sheets as electrodes. The daily used cellulose tissue sheets were transformed into electrode scaffolds through a rapid pyrolysis process within a preheated furnace, on which VOM nanoflakes were formed in a conventional hydrothermal process. With these ~10 μm thick VOM‐CC electrodes, ultrafast ECs with tunable frequency response and specific capacitance density were fabricated. The ECs with a cell‐level areal capacitance density of 0.8 mF/cm2at 120 Hz were demonstrated for ripple current filtering from 60 Hz to 60 kHz. At a lower frequency response level, EC cell with a large capacitance density of 4.8 mF/cm2was also demonstrated. With the facile and easily scaled up process to producing the nanostructured electrode, the miniaturized VOM‐CC based ECs have the potential to substitute the bulky aluminum electrolytic capacitors for current smoothing and pulse power applications.
more » « less- Award ID(s):
- 2122921
- NSF-PAR ID:
- 10485827
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Batteries & Supercaps
- Volume:
- 7
- Issue:
- 1
- ISSN:
- 2566-6223
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
ABSTRACT Compact-size kilohertz (kHz) AC-supercapacitors are being pursued for ripple current filtering and pulsed energy storage. However, their development is limited by a small areal capacitance density due to very thin electrode used for meeting frequency requirement. In our work, crosslinked carbon nanofiber aerogel (CCNFA) was investigated as freestanding electrode for kHz AC-supercapacitors with an areal capacitance density as large as 4.5 mF cm -2 at 120 Hz, 5-10 times larger than most reports. The CCNFA was obtained in a rapid plasma carbonization process of bacterial cellulose. The fabrication route adopted here is simple and straightforward, and the produced CCNFA electrode was found to be very suitable for high-frequency AC-supercapacitors. The operating voltage range of CCNFA based AC-supercapacitors can be expanded to 3 V by utilizing an organic electrolyte. In addition to AC-Supercapacitor performance, the morphology and material properties of bacterial cellulose aerogel and CCNFA were also reported.more » « less
-
more » « less
Abstract Increasing demand for self-powered wearable sensors has spurred an urgent need to develop energy harvesting systems that can reliably and sufficiently power these devices. Within the last decade, reverse electrowetting-on-dielectric (REWOD)-based mechanical motion energy harvesting has been developed, where an electrolyte is modulated (repeatedly squeezed) between two dissimilar electrodes under an externally applied mechanical force to generate an AC current. In this work, we explored various combinations of electrolyte concentrations, dielectrics, and dielectric thicknesses to generate maximum output power employing REWOD energy harvester. With the objective of implementing a fully self-powered wearable sensor, a “zero applied-bias-voltage” approach was adopted. Three different concentrations of sodium chloride aqueous solutions (NaCl-0.1 M, NaCl-0.5 M, and NaCl-1.0 M) were used as electrolytes. Likewise, electrodes were fabricated with three different dielectric thicknesses (100 nm, 150 nm, and 200 nm) of Al2O3and SiO2with an additional layer of CYTOP for surface hydrophobicity. The REWOD energy harvester and its electrode–electrolyte layers were modeled using lumped components that include a resistor, a capacitor, and a current source representing the harvester. Without using any external bias voltage, AC current generation with a power density of 53.3 nW/cm2was demonstrated at an external excitation frequency of 3 Hz with an optimal external load. The experimental results were analytically verified using the derived theoretical model. Superior performance of the harvester in terms of the figure-of-merit comparing previously reported works is demonstrated. The novelty of this work lies in the combination of an analytical modeling method and experimental validation that together can be used to increase the REWOD harvested power extensively without requiring any external bias voltage.
-
Titanium carbide/reduced graphene oxide (Ti 3 C 2 T z /rGO) gels were prepared by a one-step hydrothermal process. The gels show a highly porous structure with a surface area of ∼224 m 2 g −1 and average pore diameter of ∼3.6 nm. The content of GO and Ti 3 C 2 T z nanosheets in the reaction precursor was varied to yield different microstructures. The supercapacitor performance of Ti 3 C 2 T z /rGO gels varied significantly with composition. Specific capacitance initially increased with increasing Ti 3 C 2 T z content, but at high Ti 3 C 2 T z content gels cannot be formed. Also, the retention of capacitance decreased with increasing Ti 3 C 2 T z content. Ti 3 C 2 T z /rGO gel electrodes exhibit enhanced supercapacitor properties with high potential window (1.5 V) and large specific capacitance (920 F g −1 ) in comparison to pure rGO and Ti 3 C 2 T z . The synergistic effect of EDLC from rGO and redox capacitance from Ti 3 C 2 T z was the reason for the enhanced supercapacitor performance. A symmetric two-electrode supercapacitor cell was constructed with Ti 3 C 2 T z /rGO, which showed very high areal capacitance (158 mF cm −2 ), large energy density (∼31.5 μW h cm −2 corresponding to a power density of ∼370 μW cm −2 ), and long stability (∼93% retention) after 10 000 cycles.more » « less
-
more » « less
Transparent microelectrodes that facilitate simultaneous optical and electrophysiological interfacing are desirable tools for neuroscience. Electrodes made from transparent conductors such as graphene and indium tin oxide (ITO) show promise but are often limited by poor charge‐transfer properties. Herein, microelectrodes are demonstrated that take advantage of the transparency and volumetric capacitance of poly(3,4‐ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS). Ring‐shaped microelectrodes are fabricated by inkjet‐printing PEDOT:PSS, encapsulating with Parylene C, and then exposing a contact site that is much smaller than the microelectrode outer diameter. This unique structure allows the encapsulated portion of the microelectrode volume surrounding the contact site to participate in signal transduction, which reduces impedance and enhances charge storage capacity. While using the same 100 μm diameter contact site, increasing the outer diameter of the encapsulated electrode from 300 to 550 μm reduces the impedance from 294 ± 21 to 98 ± 2 kΩ, respectively, at 1 Hz. Similarly, the charge storage capacity is enhanced from 6 to 21 mC cm−2. The PEDOT:PSS microelectrodes provide a low‐haze, high‐transmittance optical interface, demonstrating their suitability for optical neuroscience applications. They remain functional after a million 1 V stimulation cycles, up to 600 μA of stimulation current, and more than 1000 mechanical bending cycles.