There is a strong interest in increasing the frequency response of electrochemical capacitors (ECs) from typically less than 1 Hz to the hundreds or the kilo Hz range, so that such high-frequency ECs (HF-ECs) could replace conventional capacitors for AC line-frequency filtering and other capacitor applications. The development of such HF-ECs is hindered by their typically low capacitance density and operation voltage. Herein, by treating ZIF-67 particulate films in CH 4 /H 2 plasma, edge-oriented graphene (EOG) formed around the carbonized ZIF-67 particulate skeleton, and this EOG was coupled with carbon nanotubes (CNTs) that were grown with the aid of Co catalyst nanoparticles, which were generated by reducing the Co 2+ ions associated with ZIF in the plasma. Used as electrodes, these EOG/CNT/carbonized ZIF-67 composites exhibited a large electrode areal capacitance of 1.0 mF cm −2 and an excellent frequency response of −84° phase angle at 120 Hz in aqueous electrolyte cells, whereas values of 0.67 mF cm −2 and −78° for the electrode areal capacitance and the phase angle at 120 Hz, respectively, were obtained in organic electrolyte cells with the operation voltage of 2.5 V. Using three pairs of electrodes stacked together, a single integrated cell operating at 7.5 V and having a characteristic frequency of ∼3.8 kHz at −45° phase angle, was demonstrated. These results suggest the potential to use this EOG/CNT/carbonized ZIF-67 composite structure for developing HF-ECs.
more »
« less
This content will become publicly available on December 19, 2025
Carbon Nanostructures Derived from In Situ Grown ZIF Nanocages within Bacterial Cellulose for AC‐Filtering Electrochemical Capacitors
Abstract Electrochemical capacitors (ECs) offer superior specific capacitance for energy storage compared to traditional electrolytic capacitors but face limitations in alternating current (AC) filtering due to the need for balancing fast response and high capacitance. This study addresses these challenges by developing a freestanding nanostructured carbon electrode, derived from the rapid carbonization of bacterial cellulose (BC) embedded with zeolitic imidazolate framework 8 (ZIF‐8) and in situ formed carbon nanotubes (CNTs). The electrode exhibits an exceptionally low area resistance of 9.8 mΩ cm2and a high specific capacitance of 2.1 mF cm−2at 120 Hz, maintaining performance even at high frequencies. Stacking these electrodes enhances the capacitance to 5.3 mF cm−2, with the phase angle degrading to −74.4° at 120 Hz; however, they retain a phase angle below −45° up to ≈50 kHz, demonstrating excellent high‐frequency performance. Furthermore, connecting three aqueous units in series as an integrated cell or utilizing organic electrolytes extends the voltage window to 2.4 V, enhancing their suitability for high‐voltage applications. Ripple voltage analysis under various loads and frequencies indicates effective filtering capabilities, highlighting the potential of these nanostructured ECs for next‐generation electronic applications.
more »
« less
- Award ID(s):
- 2122921
- PAR ID:
- 10571515
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Small
- Volume:
- 21
- Issue:
- 5
- ISSN:
- 1613-6810
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract An ultra‐fast electrochemical capacitor (EC) designed for efficient ripple current smoothing was fabricated using vertically oriented MoS2(VOM) nanoflakes deposited on freestanding carbonized cellulose (CC) sheets as electrodes. The daily used cellulose tissue sheets were transformed into electrode scaffolds through a rapid pyrolysis process within a preheated furnace, on which VOM nanoflakes were formed in a conventional hydrothermal process. With these ~10 μm thick VOM‐CC electrodes, ultrafast ECs with tunable frequency response and specific capacitance density were fabricated. The ECs with a cell‐level areal capacitance density of 0.8 mF/cm2at 120 Hz were demonstrated for ripple current filtering from 60 Hz to 60 kHz. At a lower frequency response level, EC cell with a large capacitance density of 4.8 mF/cm2was also demonstrated. With the facile and easily scaled up process to producing the nanostructured electrode, the miniaturized VOM‐CC based ECs have the potential to substitute the bulky aluminum electrolytic capacitors for current smoothing and pulse power applications.more » « less
-
ABSTRACT Compact-size kilohertz (kHz) AC-supercapacitors are being pursued for ripple current filtering and pulsed energy storage. However, their development is limited by a small areal capacitance density due to very thin electrode used for meeting frequency requirement. In our work, crosslinked carbon nanofiber aerogel (CCNFA) was investigated as freestanding electrode for kHz AC-supercapacitors with an areal capacitance density as large as 4.5 mF cm -2 at 120 Hz, 5-10 times larger than most reports. The CCNFA was obtained in a rapid plasma carbonization process of bacterial cellulose. The fabrication route adopted here is simple and straightforward, and the produced CCNFA electrode was found to be very suitable for high-frequency AC-supercapacitors. The operating voltage range of CCNFA based AC-supercapacitors can be expanded to 3 V by utilizing an organic electrolyte. In addition to AC-Supercapacitor performance, the morphology and material properties of bacterial cellulose aerogel and CCNFA were also reported.more » « less
-
Supercapacitors and batteries are essential for sustainable energy development. However, the bottleneck is the associated high cost, which limits bulk use of batteries and supercapacitors. In this context, realizing that the cost of energy‐storage device mainly depends on materials, synthesis processes/procedures, and device fabrication, an effort is made to rationally design and develop novel low‐cost electrode materials with enhanced electrochemical performance in asymmetric supercapacitors. Herein, surface functionalization approach is adopted to design low‐cost 3D mesoporous and nanostructured nickel–nickel oxide electrode materials using facile synthesis for application in supercapacitors. It is demonstrated that the 3D mesoporous Ni provides the high surface area and enhanced ionic conductivity, while germanium functionalization improves the electrical conductivity and reduces the charge‐transfer resistance of NiO. Surface functionalization with Ge demonstrates the significant improvement in specific capacitance of NiO. The asymmetric supercapacitor using these Ge‐functionalized NiO–Ni electrodes provides a specific capacitance of 304 Fg−1(94 mF cm−2), energy density of 23.8 Wh kg−1(7.35 μWh cm−2), and power density of 6.8 kW kg−1(2.1 mW cm−2) with excellent cyclic stability of 92% after 10 000 cycles. To validate their practical applications, powering the digital watch using the asymmetric supercapacitors in laboratory conditions is demonstrated.more » « less
-
Bonizzoni, Edoardo (Ed.)This brief presents an ultra-low-power class-D voltage-controlled oscillator (VCO) designed for GHz applications that mandate decent phase noise performance. A waveform-centric approach of phase noise reduction by controlling the ratio between the floating and single-ended (SE) capacitors in an oscillator tank is proposed. By co-designing an RF choke with the tank inductor to introduce high impedance for the floating capacitors, the optimum capacitance ratio is maintained across the tuning range. The VCO is fabricated in 65nm Bulk CMOS technology and achieves a measured phase noise of -118.36 dBc/Hz and -138.64 dBc/Hz, and figure-of-merit of 192.89 dBc/Hz and 194.52 dBc/Hz at 1 MHz and 10 MHz offset frequencies, respectively. The VCO’s lowest measured 1/f3 corner is approximately 50kHz, which enables a decent figure-of-merit (FoM) down to a frequency offset of 10 kHz. The VCO features a tuning range of 40% (3.1 GHz -4.66 GHz) using a one-bit switch to realize two-point modulation in phase-locked loops (PLLs) with milliwatt-level power consumption.more » « less