skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Fabrication and preliminary testing of patterned silver cathodes for proton conducting IT-SOFCs
Dense silver (Ag) cathodes with defined triple phase boundary (TPB between the interface of electrolyte, electrode, and gas) lengths (LTPB) and electrode areas (AELT) were fabricated by photolithography and E-beam evaporation over a proton conducting BaZr0.4Ce0.4Y0.1Yb0.1O3−δ (BZCYYb4411) electrolyte. A bi-layer lift-off resist method appears to be more versatile than a single layer lift-off resist method for successful patterned cathode fabrication. The electrochemical behaviors of the patterned Ag cathodes over the BZCYYb4411 electrolyte were tested by electrochemical impedance spectroscopy (EIS) at different temperatures in atmospheres with different concentrations of O2 and H2O. The results were processed using Distribution of Relaxation Times (DRT) and reaction order analyses and also fitted to equivalent circuits. The directions for future work on patterned electrodes with different LTPB and AELT and theoretical calculations to gain further insights into the kinetics and mechanism of the cathode oxygen reduction reaction (ORR) over proton conducting electrolytes are pointed out.  more » « less
Award ID(s):
1848305
PAR ID:
10490147
Author(s) / Creator(s):
; ; ; ; ; ;
Publisher / Repository:
Royal Society of Chemistry
Date Published:
Journal Name:
Materials Advances
ISSN:
2633-5409
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; (, ECS Advances)
    BaCo0.4Fe0.4Zr0.1Y0.1O3−σ (BCFZY) is a proton, oxygen-ion, and electron-hole conducting cathode material for intermediate temperature solid oxide fuel cells. Its electrode reaction mechanism in air with moisture is not well understood. In this study, three types of symmetrical cells with the same BCFZY cathode were fabricated over three related proton conducting electrolytes: BaZr0.8−xCexY0.1Yb0.1O3−δ (x = 0.1, 0.4, and 0.7). The cathode shows similar performance over three different electrolytes in dry air but different responses to moisture introduction. The differences are hypothesized to relate to the mutual diffusion at the cathode/electrolyte interface. Such a hypothesis is supported by different techniques such as XRD Rietveld refinement of BCFZY cathode in mixtures with different electrolytes after firing, energy-dispersive X-ray spectroscopy (EDS) line scanning for element concentration distribution at the cathode/electrolyte interface, as well as electrochemical test for a related BaCoFeO-type cathode with Zr replaced by Ce. 
    more » « less
  2. ; ; ; ; (, Advanced Functional Materials)
    Abstract A traditional composite cathode for proton‐conducting solid oxide fuel cells (H‐SOFCs) is typically obtained by mixing cathode materials and proton conducting electrolyte of BaCe0.7Y0.2Zr0.1O3–δ(BZCY), providing chemical and thermal compatibility with the electrolyte. Here, a series of triple‐conducing and cobalt‐free iron‐based perovskites as cathodes for H‐SOFCs is reported. Specifically, BaCexFe1–xO3–δ(x = 0.36, 0.43, and 0.50) shows various contents of two single phase perovskites with an in situ heterojunction structure as well as triple conductivity by tailoring the Ce/Fe ratios. The cell performance with the optimized BaCe0.36Fe0.64O3–δ(BCF36) cathode composition reaches 1056 mW cm−2at 700 °C. Moreover, a record cell performance of 1525 mW cm−2at 700 °C is obtained by modifying the BCF36 cathode microstructure through a spraying method, demonstrating high promise with Co‐free cathodes for H‐SOFCs. 
    more » « less
  3. ; ; ; ; ; ; ; ; ; (, Advanced Energy Materials)
    Abstract Prussian blue analogues (PBAs) cathodes can host diverse monovalent and multivalent metal ions due to their tunable structure. However, their electrochemical performance suffers from poor cycle life associated with chemo‐mechanical instabilities. This study investigates the driving forces behind chemo‐mechanical instabilities in Ni‐ and Mn‐based PBAs cathodes for K‐ion batteries by combining electrochemical analysis, digital image correlation, and spectroscopy techniques. Capacity retention in Ni‐based PBA is 96% whereas it is 91.5% for Mn‐based PBA after 100 cycles at C/5 rate. During charge, the potassium nickel hexacyanoferrate (KNHCF) electrode experiences a positive strain generation whereas the potassium manganese hexacyanoferrate (KMHCF) electrode undergoes initially positive strain generation followed by a reduction in strains at a higher state of charge. Overall, both cathodes undergo similar reversible electrochemical strains in each charge–discharge cycle. There is ~0.80% irreversible strain generation in both cathodes after 5 cycles. XPS studies indicated richer organic layer compounds in the cathode‐electrolyte interface (CEI) layer formed on KMHCF cathodes compared to the KNHCF ones. Faster capacity fades in Mn‐based PBA, compared to Ni‐based ones, is attributed to the formation of richer organic compounds in CEI layers, rather than mechanical deformations. Understanding the driving forces behind instabilities provides a guideline to develop material‐based strategies for better electrochemical performance. 
    more » « less
  4. ; ; (, ECS Meeting Abstracts)
    Na-ion batteries have taken more interest in recent years as an alternative battery chemistry to Li-ion batteries because of material abundance, cost, and sufficient volumetric energy density for large-scale energy storage applications. However, Na-ion batteries suffer from rapid capacity fade associated with chemo-mechanical instabilities such as the formation of resistive solid-electrolyte / cathode-electrolyte interphase (SEI/CEI) layers, irreversible phase formations, and particle fracture. The cathode materials are fragile, especially metal oxides, therefore Na-ion cathodes are more prone to mechanical deformations upon larger volumetric expansions/reductions during Na-ion intercalation. Electrolyte additives have been utilized to improve the electrochemical performance of Li-ion and Na-ion batteries by modifying the chemistry of the SEI layers. In situ stress measurements on Si anode in Li-ion batteries demonstrated the generation of less mechanical deformations in the electrode when cycled in the presence of FEC additives.1However, there is not much known about the impact of electrolyte additives on the chemo-mechanical properties of CEI layers in Na-ion battery cathodes. Furthermore, the question still stands about how the electrolyte additives may impact the mechanical stability of the Na-ion cathodes. To address this gap, we systematically investigated the role of FEC additives on the electrochemical performance and associated chemo-mechanical instabilities in NaCrO2 cathodes. Experiments were performed in organic electrolytes with/without FEC additives. First, the talk will start with presenting the impact of FEC additives on the capacity retention and cyclic voltammeter profiles of NaCrO2 cathodes. Then, digital image correlation and multi-beam optical stress sensor techniques were employed to probe electrochemical strain and stress generation in the composite NaCrO2 cathodes during electrochemical cycling in organic electrolytes with/without FEC additives. Surface chemistry of the NaCrO2 cathodes after cycling was investigated with the FT-IR measurements. In summary, the talk will present contrast differences in the electrochemical and chemo-mechanical properties of NaCrO2 cathodes when cycled in the presence of the FEC additives. Acknowledgement: This work is supported by National Science Foundation (award number 2321405). Reference: 1) Tripathi et al 2023 J. Electrochem. Soc. 170 090544 
    more » « less
  5. ; (, Journal of the Electrochemical Society)
    The production of precious metals from Cu-rich sources such as ore products or secondary sources is slow and complex largely due to limited solubility in aqueous electrolytes. This results in sequential processing with various electrolytes and chemistries, where first Cu is electrorefined, followed by Ag, followed by Au and the platinum group metals. These are separate processes, often conducted in separate electrorefining and electrowinning facilities. The chemical properties of molten sulfides, and their ability to operate at a temperature where liquid metal cathodes are used, suggest the possibility of an alternative, streamlined processing route for Cu and precious metals. Unfortunately, little thermodynamic or electrochemical information is available regarding the behavior of Cu and precious metal sulfides in molten sulfide electrolytes. Herein, the relative activity of the Cu2S-Ag2S pseudobinary dissolved in a BaS-La2S3 supporting electrolyte is measured at 1523 K. It was found that the supporting electrolyte favors mixing with Ag2S over Cu2S. Molten sulfide electrolysis of Cu and Ag was conducted, with results in good agreement with the thermodynamic model. It is found that the Ag-Cu cathode chemistry will influence the electrochemical selectivity in the Ag-Cu-Ba-La-S system. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email