SUMMARY Cyclic loading at elevated temperatures occurs either naturally during tectonic or volcanic-induced earthquakes or can be human-induced due to various geological engineering activities. The aim of this study is to test if mechanical fatigue in rocks can be monitored by magnetic methods. For this purpose, the effect of cyclic-mechanical loading (150 ± 30 MPa) on the magnetic susceptibility and its anisotropy of a magnetite-bearing ore with varying temperatures (400 and 500 °C) and environment (air and vacuum) was investigated. Our study shows that magnetic susceptibility decreases significantly (up to 23 per cent) under air conditions and in vacuum (up to 4 per cent) within the first ca. 1000 cycles. Further loading does not significantly affect the magnetic susceptibility which then remains more or less constant. The decrease of susceptibility parameters is stronger at 500 °C compared to 400 °C under both experimental conditions. Magnetic susceptibility was always measured after decompression of the loaded sample at room temperature so that magnetostriction can be excluded as a reason for these changes. The higher the temperature at which samples were loaded the more pronounced is the oxidation of magnetite to haematite. The transformation of magnetite into haematite under ambient conditions is the most important mechanism influencing bulk magnetic properties. The weak changes in magnetic susceptibility after vacuum loadings are probably caused by intragranular microcracks formed on the surface of magnetite grains. These surface deformation structures are accompanied by the refinement of magnetic domains, which is observed by magnetic force microscopy. Bulk magnetic grain size modifications are also confirmed by hysteresis parameters as well as by the increasing Hopkinson peak ratios determined from magnetic susceptibility measurements over Curie point. The degree of magnetic anisotropy and shape factor only change for the air-treated samples and are therefore related to the haematite formation and not to irreversible ductile deformation in magnetite. Our experimental study shows that cyclic loading can change significantly the magnetic properties of a rock due to mineral transformation below < 1000 cycles and that the first stages of mechanical fatigue, which are a precursor of the failure of rock, are closely associated with these transformations.
more »
« less
This content will become publicly available on January 26, 2025
Restoration and Transformation: The Response of Shocked and Oxidized Magnetite to Temperature
Large impact craters on Earth are associated with prominent magnetic anomalies, residing in magnetite of the shocked target rocks and impactites. Shock experiments on magnetite suggest that up to 90% of magnetic susceptibility is lost at pressures >5 GPa, but can be partially restored by post‐shock thermal annealing. The magnetic property changes are caused by shock induced grain size reduction and fragmentation, as well as domain wall‐pinning at crystal lattice defects. A recent study of granitoids from the peak‐ring of the Chicxulub crater found that annealing may occur naturally, but can also be overprinted by high‐temperature hematite‐to‐magnetite transformation in non‐oxidizing environments. In this study, we isolate the effect of defect annealing and hematite‐to‐magnetite transformation using the evolution of hysteresis, isothermal remanent magnetization components and first order reversal curve (FORC) diagrams at different high‐temperature steps. We used a laboratory‐shocked magnetite‐quartz ore, a non‐shocked naturally oxidized granite, and a naturally shocked and oxidized granite. Our findings suggest that annealing of shock‐induced lattice defects partially restores some pre‐shock magnetic behavior and causes an apparent average bulk‐sample domain state increase. Hematite‐to‐magnetite transformation creates new fine‐grained magnetite that strongly overprints the original signal, and decreases the average bulk‐sample domain state. Where annealing and hematite‐to‐magnetite transformation both occur, the new magnetite masks the annealing‐induced property restoration and apparent domain state modification in the shocked magnetite. As magnetite oxidation is a ubiquitous process in surface rocks, these findings are fundamental to understand hematite‐to‐magnetite transformation as a potential overprint mechanism, and could have broad implications for paleomagnetic interpretations.
more » « less- Award ID(s):
- 2153786
- NSF-PAR ID:
- 10497398
- Publisher / Repository:
- American Geophysical Union
- Date Published:
- Journal Name:
- Journal of Geophysical Research: Solid Earth
- Volume:
- 129
- Issue:
- 2
- ISSN:
- 2169-9313
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
SUMMARY Lamellar magnetism is a source of remanent magnetization in natural rocks different from common bulk magnetic moments in ferrimagnetic minerals. It has been found to be a source for a wide class of magnetic anomalies with extremely high Koenigsberger ratio. Its physical origin are uncompensated interface moments in contact layers of nanoscale ilmenite lamellae inside an hematite host, which also generate unusual low-temperature (low-T) magnetic properties, such as shifted low-T hysteresis loops due to exchange bias. The atomic-magnetic basis for the exchange bias discovered in the hematite-ilmenite system is explored in a series of papers. In this third article of the series, simple models are developed for lamellae interactions of different structures when samples are either cooled in zero-field, or field-cooled in 5 T to temperatures below the ordering temperature of ilmenite. These models are built on the low-temperature measurements described earlier in Paper II. The important observations include: (i) the effects of lamellar shapes on magnetic coupling, (ii) the high-T acquisition of lamellar magnetism and low-T acquisition of magnetization of ilmenite lamellae, (iii) the intensity of lamellar magnetism and the consequent ilmenite magnetism in populations of randomly oriented crystals, (iv) lattice-preferred orientation of the titanohematite host crystal populations and (v) the effects of magnetic domain walls in the host on hysteresis properties. Based on exemplary growth models of lamellae with different geometries and surface couplings we here provide simple models to assess and explain the different observations listed above. Already the simplified models show that the shapes of the edges of ilmenite lamellae against their hematite hosts can control the degree of low-T coupling between ilmenite, and the lamellar magnetic moments. The models also explain certain features of the low-T exchange bias in the natural samples and emphasize the role of lattice-preferred orientation upon the intensity of remanent magnetization. The inverse link between ilmenite remanence and exchange-bias shift in bimodal low-T ilmenite lamellae is related to different densities of hematite domain walls induced by the clusters of ilmenite lamellae.more » « less
-
more » « less
Abstract The goal of classifying shock metamorphic features in meteorites is to estimate the corresponding shock pressure conditions. However, the temperature variability of shock metamorphism is equally important and can result in a diverse and heterogeneous set of shock features in samples with a common overall shock pressure. In particular, high-pressure (HP) minerals, which were previously used as a solid indicator of high shock pressure in meteorites, require complex pressure–temperature–time (
P–T–t ) histories to form and survive. First, parts of the sample must be heated to melting temperatures, at high pressure, to enable rapid formation of HP minerals before pressure release. Second, the HP minerals must be rapidly cooled to below a critical temperature, before the pressure returns to ambient conditions, to avoid retrograde transformation to their low-pressure polymorphs. These two constraints require the sample to contain large temperature heterogeneities, e.g. melt veins in a cooler groundmass, during shock. In this study, we calculated shock temperatures and possibleP–T paths of chondritic and differentiated mafic–ultramafic rocks for various shock pressures. TheseP–T conditions and paths, combined with observations from shocked meteorites, are used to constrain shock conditions andP–T –t histories of HP-mineral bearing samples. The need for rapid thermal quench of HP phases requires a relatively low bulk-shock temperature and therefore moderate shock pressures below ~ 30 GPa, which matches the stabilities of these HP minerals. The low-temperature moderate-pressure host rock generally shows moderate shock-deformation features consistent with S4 and, less commonly, S5 shock stages. Shock pressures in excess of 50 GPa in meteorites result in melt breccias with high overall post-shock temperatures that anneal out HP-mineral signatures. The presence of ringwoodite, which is commonly considered an indicator of the S6 shock stage, is inconsistent with pressures in excess of 30 GPa and does not represent shock conditions different from S4 shock conditions. Indeed, ringwoodite and coexisting HP minerals should be considered as robust evidence for moderate shock pressures (S4) rather than extreme shock (S6) near whole-rock melting. -
Abstract Partition coefficients for rare earth elements (REEs) between apatite and basaltic melt were determined as a function of oxygen fugacity (fO2; iron-wüstite to hematite-magnetite buffers) at 1 bar and between 1110 and 1175 °C. Apatite-melt partitioning data for REE3+ (La, Sm, Gd, Lu) show near constant values at all experimental conditions, while bulk Eu becomes more incompatible (with an increasing negative anomaly) with decreasing fO2. Experiments define three apatite calibrations that can theoretically be used as redox sensors. The first, a XANES calibration that directly measures Eu valence in apatite, requires saturation at similar temperature-composition conditions to experiments and is defined by: ( E u 3 + ∑ E u ) Apatite = 1 1 + 10 - 0.10 ± 0.01 × l o g ( f o 2 ) - 1.63 ± 0.16 . The second technique involves analysis of Sm, Eu, and Gd in both apatite and coexisting basaltic melt (glass), and is defined by: ( Eu E u * ) D Sm × Gd = 1 1 + 10 - 0.15 ± 0.03 × l o g ( f o 2 ) - 2.46 ± 0.41 . The third technique is based on the lattice strain model and also requires analysis of REE in both apatite and basalt. This calibration is defined by ( Eu E u * ) D lattice strain = 1 1 + 10 - 0.20 ± 0.03 × l o g ( f o 2 ) - 3.03 ± 0.42 . The Eu valence-state partitioning techniques based on (Sm×Gd) and lattice strain are virtually indistinguishable, such that either methodology is valid. Application of any of these calibrations is best carried out in systems where both apatite and coexisting glass are present and in direct contact with one another. In holocrystalline rocks, whole rock analyses can be used as a guide to melt composition, but considerations and corrections must be made to either the lattice strain or Sm×Gd techniques to ensure that the effect of plagioclase crystallization either prior to or during apatite growth can be removed. Similarly, if the melt source has an inherited either a positive or negative Eu anomaly, appropriate corrections must also be made to lattice strain or Sm×Gd techniques that are based on whole rock analyses. This being the case, if apatite is primary and saturates from the parent melt early during the crystallization sequence, these corrections may be minimal. The partition coefficients for the REE between apatite and melt range from a maximum DEu3+ = 1.67 ± 0.25 (as determined by lattice strain) to DLu3+ = 0.69 ± 0.10. The REE partition coefficient pattern, as observed in the Onuma diagram, is in a fortuitous situation where the most compatible REE (Eu3+) is also the polyvalent element used to monitor fO2. These experiments provide a quantitative means of assessing Eu anomalies in apatite and how they be used to constrain the oxygen fugacity of silicate melts.more » « less
-
SUMMARY Anisotropy of remanent magnetization and magnetic susceptibility are highly sensitive and important indicators of geological processes which are largely controlled by mineralogical parameters of the ferrimagnetic fraction in rocks. To provide new physical insight into the complex interaction between magnetization structure, shape, and crystallographic relations, we here analyse ‘slice-and-view’ focused-ion-beam (FIB) nano-tomography data with micromagnetic modelling and single crystal hysteresis measurements. The data sets consist of 68 magnetite inclusions in orthopyroxene (Mg60) and 234 magnetite inclusions in plagioclase (An63) were obtained on mineral separates from the Rustenburg Layered Suite of the Bushveld Intrusive Complex, South Africa. Electron backscatter diffraction was used to determine the orientation of the magnetite inclusions relative to the crystallographic directions of their silicate hosts. Hysteresis loops were calculated using the finite-element micromagnetics code MERRILL for each particle in 20 equidistributed field directions and compared with corresponding hysteresis loops measured using a vibrating sample magnetometer (VSM) on silicate mineral separates from the same samples. In plagioclase the ratio of remanent magnetization to saturation magnetization (Mrs/Ms) for both model and measurement agree within 1.0 per cent, whereas the coercivity (Hc) of the average modelled curve is 20 mT lower than the measured value of 60 mT indicating the presence of additional sources of high coercivity in the bulk sample. The VSM hysteresis measurements of the orthopyroxene were dominated by multidomain (MD) magnetite, whereas the FIB location was chosen to avoid MD particles and thus contains only particles with diameters <500 nm that are considered to be the most important carriers of palaeomagnetic remanence. To correct for this sampling bias, measured MD hysteresis loops from synthetic and natural magnetites were combined with the average hysteresis loop from the MERRILL models of the FIB region. The result shows that while the modelled small-particle fraction only explains 6 per cent of the best fit to the measured VSM hysteresis loop, it contributes 28 per cent of the remanent magnetization. The modelled direction of maximal Mrs/Ms in plagioclase is subparallel to [001]plag, whereas Hc does not show a strong orientation dependence. The easy axis of magnetic remanence is in the direction of the magnetite population normal to (150)plag and the maximum calculated susceptibility (χ*) is parallel to [010]plag. For orthopyroxene, the maximum Mrs/Ms, maximum χ* and the easy axis of remanence is strongly correlated to the elongation axes of magnetite in the [001]opx direction. The maximum Hc is oriented along [100]opx and parallel to the minimum χ*, which reflects larger vortex nucleation fields when the applied field direction approaches the short axis. The maximum Hc is therefore orthogonal to the maximum Mrs/Ms, controlled by axis-aligned metastable single-domain states at zero field. The results emphasize that the nature of anisotropy in natural magnetite does not just depend on the particle orientations, but on the presence of different stable and metastable domain states, and the mechanism of magnetic switching between them. Magnetic modelling of natural magnetic particles is therefore a vital method to extract and process anisotropic hysteresis parameters directly from the primary remanence carriers.more » « less