Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • NSF Public Access
  • Search Results
  • Mechanical properties of molybdenum containing MoO2 and HfO2 processed by field assisted sintering technology (FAST): Characterization and modeling
Title: Mechanical properties of molybdenum containing MoO2 and HfO2 processed by field assisted sintering technology (FAST): Characterization and modeling
Molybdenum and its alloys are of interest for applications with extreme thermomechanical requirements such as nuclear energy systems, electronics, aerospace vehicles, and hypersonic vehicles. In the present study, pure molybdenum and samples with added hafnium carbide (HfC) grain refiners were produced using field assisted sintering technology (FAST). The molybdenum and HfC reacted with oxygen to produce MoO2 and HfO2, and increased HfC content from 1 wt% to 5 wt% decreased grain size while the microhardness correspondingly increased. Room temperature three-point bending tests were conducted, and finite element modeling was used to define HfC-dependent bilinear material models. The presence of oxygen most severely affected pure molybdenum, which exhibited little strength and limited ductility, whereas for samples with added HfC, HfO2 was present, resulting in increased toughness hypothesized to be due to microcrack toughening. The samples with 1 wt% added HfC had the greatest energy absorption capability.  more » « less
Award ID(s):
1652575
PAR ID:
10503143
Author(s) / Creator(s):
; ; ; ;
Publisher / Repository:
Elsevier
Date Published:
Journal Name:
International Journal of Refractory Metals and Hard Materials
Volume:
115
Issue:
C
ISSN:
0263-4368
Page Range / eLocation ID:
106317
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; (, Inorganic Chemistry)
    Details of the carbothermic reduction/nitridation to synthesize hafnium nitride (HfN) and hafnium carbide (HfC) are scarce in the literature. Therefore, this current study was carried out to evaluate two pathways for synthesizing these two refractory materials: direct nitridation and carbothermic reduction/nitridation. Two mixtures of hafnium dioxide and carbon with C/ HfO2 molar ratios of 2.15 and 3.1 were nitridized directly using flowing nitrogen gas at elevated temperatures (1300−1700 °C). The 3.1 C/HfO2 molar ratio mixture was also carbothermically reduced under flowing argon gas to synthesize HfC, which was converted into HfN by introducing a nitridation step under both N2(g) and N2(g)-10% H2(g). X-ray diffraction results showed the formation of HfN at 1300 and 1400 °C and HfC1−yNy at ≥1400 °C under direct nitridation of samples using a C/HfO2 molar ratio of 2.15. These phase analysis data together with lower lattice strain and greater crystallite sizes of HfC1−yNy that formed at higher temperatures suggested that the HfC1−yNy phase is preferred over HfN at those temperatures. Carbothermic reduction of 3.1 C/HfO2 molar ratio samples under an inert atmosphere produced single-phased HfC with no significant levels of dissolved oxygen. Carbothermic reduction nitridation made two phases of different carbon levels (HfC1−yNy and HfC1−y′Ny′, where y′ < y), while direct nitridation produced a single HfC1−yNy phase under both N2 and N2-10% H2 cover gas environments. 
    more » « less
  2. ; ; ; ; (, Advanced Engineering Materials)
    Tantalum carbide (TaC) and hafnium carbide (HfC) have some of the highest melting temperatures among the transition metal carbides, borides, and nitrides, making them promising materials for high‐speed flight and high‐temperature structural applications. Solid solutions of TaC and HfC are of particular interest due to their enhanced oxidation resistance compared to pure TaC or HfC. This study looks at the effect of Hf content on the oxidation resistance of TaC–HfC sintered specimens. Five compositions are fabricated into bulk samples using spark plasma sintering (2173 K, 50 MPa, 10 min hold). Oxidation behavior of a subset of the compositions (100 vol% TaC, 80 vol% TaC + 20 vol% HfC, and 50 vol% TaC + 50 vol% HfC) is analyzed using an oxyacetylene torch for 60 s. The TaC–HfC samples exhibit a reduction in the oxide scale thickness and the mass ablation rate with increasing HfC content. The improved oxidation resistance can be attributed to the formation of a Hf6Ta2O17phase. This phase enhances oxidation resistance by reducing oxygen diffusion and serving as a protective layer for the unoxidized material. The superior oxidation resistance of TaC–HfC samples makes these materials strong contenders for the development of high‐speed flight coatings. 
    more » « less
  3. (, Thin solid films)
    Many biological lab-on-a-chip applications require electrical and optical manipulation as well as detection of cells and biomolecules. This provides an intriguing challenge to design robust microdevices that resist adverse electrochemical side reactions yet achieve optical transparency. Physical isolation of biological samples from microelectrodes can prevent contamination, electrode fouling, and electrochemical byproducts; thus this manuscript explores hafnium oxide (HfO2) films - originating from traditional transistor applications – for suitability in electrokinetic microfluidic devices for biological applications. HfO2 films with deposition times of 6.5, 13, and 20 min were sputter deposited onto silicon and glass substrates. The structural, optical, and electrical properties of the HfO2 films were investigated using atomic force microscopy (AFM), X-ray diffraction, energy dispersive X-ray spectroscopy, Fourier transform infrared spectroscopy, ellipsometry, and capacitance voltage. Electric potential simulations of the HfO2 films and a biocompatibility study provided additional insights. Film grain size after corrosive Piranha treatment was observed via AFM. The crystalline structure investigated via X-ray diffraction revealed all films exhibited the (111) characteristic peak with thicker films exhibiting multiple peaks indicative of anisotropic structures. Energy dispersive X-ray spectroscopy via field emission scanning electron microscopy and Fourier transform infrared spectroscopy both corroborated the atomic ratio of the films as HfO2. Ellipsometry data from Si yielded thicknesses of 58, 127, and 239 nm and confirmed refractive index and extinction coefficients within the normal range for HfO2; glass data yielded unreliable thickness verifications due to film and substrate transparency. Capacitance-voltage results produced an average dielectric constant of 20.32, and the simulations showed that HfO2 dielectric characteristics were sufficient to electrically passivate planar microelectrodes. HfO2 biocompatibility was determined with human red blood cells by quantifying the hemolytic potential of the HfO2 films. Overall results support hafnium oxide as a viable passivation material for biological lab-on-a-chip applications. 
    more » « less
  4. ; ; (, Journal of the American Ceramic Society)
    Abstract Zirconium carbide (ZrC) powder, batched to a ratio of 0.98 C/Zr, was prepared by carbothermal reduction of ZrO2with carbon black. Nominally phase‐pure ZrC powder had a mean particle size of 2.4 μm. The synthesized powder was hot‐pressed at 2150°C to a relative density of > 95%. The mean grain size was 2.7 ± 1.4 μm with a maximum observed grain size of 17.5 μm. The final hot‐pressed billets had a C/Zr ratio of 0.92, and oxygen content of 0.5 wt%, as determined by gas fusion analysis. The mechanical properties of ZrC0.92O0.03were measured at room temperature. Vickers’ hardness decreased from 19.5 GPa at a load of 0.5 kgf to 17.0 GPa at a load of 1 kgf. Flexural strength was 362.3 ± 46 MPa, Young's modulus was 397 ± 13 MPa, and fracture toughness was 2.9 ± 0.1 MPa•m1/2. Analysis of mechanical behavior revealed that the largest ZrC grains were the strength‐limiting flaw in these ceramics. 
    more » « less
  5. ; ; ; ; ; ; ; ; ; ; et al (, ECS transactions)
    This work investigates the role of extra oxygen vacancies, introduced by a hydrogen plasma at midpoint of deposition of a 6 nm thick HfO2 to reduce the switching power consumption in a RRAM device. Initially TiN, which is a commonly used metal in CMOS technology, was used as the top electrode for treated HfO2. Subsequently Ru and TaN as top electrodes were explored to enhance the switching behavior and power consumption. A range of compliance currents from 1 nA to 1 µA were used to evaluate the switching characteristics. The role of both TaN and Ru as bottom metal was also evaluated. With Ru as top metal the device switched at a compliance current of 1 nA and higher. Whereas when Ru was used as bottom electrode, devices were unable to switch below a compliance current of 50 µA. For TaN as top metal electrode, devices switched at and above 1 µA CC whereas with TaN as bottom metal the initial switching was at CC of 2 µA. It was observed that use of Ru as a top metal significantly reduced the switching energy of the plasma treated HfO2 RRAM device but was ineffective when used as a bottom metal. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email