The interface properties and thermal stability of bismuth (Bi) contacts on molybdenum disulfide (MoS2) shed light on their behavior under various deposition conditions and temperatures. The examination involves extensive techniques including X-ray photoelectron spectroscopy, scanning tunneling microscopy (STM), and scanning tunneling spectroscopy (STS). Bi contacts formed a van der Waals interface on MoS2 regardless of deposition conditions, such as ultrahigh vacuum (UHV, 3 × 10–11 mbar) and high vacuum (HV, 4 × 10–6 mbar), while the oxidation on MoS2 has been observed. However, the semimetallic properties of Bi suppress the impact of defect states, including oxidized-MoS2 and vacancies. Notably, the n-type characteristic of Bi/MoS2 remains unaffected, and no significant changes in the local density of states near the conduction band minimum are observed despite the presence of defects detected by STM and STS. As a result, the Fermi level (EF) resides below the conduction band of MoS2. The study also examines the impact of annealing on the contact interface, revealing no interface reaction between Bi and MoS2 up to 300 °C. These findings enhance our understanding of semimetal (Bi) contacts on MoS2, with implications for improving the performance and reliability of electronic devices.
more »
« less
Natural formation of linear defect structures in MoS2
Near surface defects can significantly impact the quality of metallic interconnects and other interfaces necessary to create device structures incorporating two-dimensional materials. Furthermore, the impact of such defects can strongly depend on their organization. In this study, we present scanning tunneling microscopy images and tunneling spectroscopy of point and linear defects near the surface of natural MoS2. The point defects share similar structural and electronic characteristics and occur with comparable frequency as subsurface sulfur vacancies observed previously on natural MoS2. The linear defects observed here occur less frequently than the point defects but share the same depth profile and electronic structure. These data indicate that the linear defects are actually a one-dimensional organization of subsurface sulfur vacancies. Our density functional calculations agree with this assessment in that, for sufficient local defect concentrations, it is energetically more favorable for the defects to be organized in a linear fashion rather than as clusters or even isolated single point defects. Given these measurements were taken from naturally formed MoS2, this organization likely occurs during crystal formation. Considering the impact of one-dimensional organization on the local properties of layered materials, and the potential for them to be introduced purposefully during crystal formation, research into the formation mechanism and properties of these defects could enable new paths for defect engineering in MoS2-based systems.
more »
« less
- Award ID(s):
- 2300639
- PAR ID:
- 10504150
- Publisher / Repository:
- Applied Physics Letters
- Date Published:
- Journal Name:
- Applied Physics Letters
- Volume:
- 124
- Issue:
- 8
- ISSN:
- 0003-6951
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Two-dimensional transition metal dichalcogenides (2D-TMDs) have been proposed as novel optoelectronic materials for space applications due to their relatively light weight. MoS2 has been shown to have excellent semiconducting and photonic properties. Although the strong interaction of ionizing gamma radiation with bulk materials has been demonstrated, understanding its effect on atomically thin materials has scarcely been investigated. Here, we report the effect of gamma irradiation on the structural and electronic properties of a monolayer of MoS2. We perform Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) studies of MoS2, before and after gamma ray irradiation with varying doses and density functional theory (DFT) calculations. The Raman spectra and XPS results demonstrate that point defects dominate after the gamma irradiation of MoS2. DFT calculations elucidate the electronic properties of MoS2 before and after irradiation. Our work makes several contributions to the field of 2D materials research. First, our study of the electronic density of states and the electronic properties of a MoS2 monolayer irradiated by gamma rays sheds light on the properties of a MoS2 monolayer under gamma irradiation. Second, our study confirms that point defects are formed as a result of gamma irradiation. And third, our DFT calculations qualitatively suggest that the conductivity of the MoS2 monolayer may increase after gamma irradiation due to the creation of additional defect states.more » « less
-
Abstract Edges and point defects in layered dichalcogenides are important for tuning their electronic and magnetic properties. By combining scanning tunneling microscopy (STM) with density functional theory (DFT), the electronic structure of edges and point defects in 2D‐PtSe2are investigated where the 1.8 eV bandgap of monolayer PtSe2facilitates the detailed characterization of defect‐induced gap states by STM. The stoichiometric zigzag edge terminations are found to be energetically favored. STM and DFT show that these edges exhibit metallic 1D states with spin polarized bands. Various native point defects in PtSe2are also characterized by STM. A comparison of the experiment with simulated images enables identification of Se‐vacancies, Pt‐vacancies, and Se‐antisites as the dominant defects in PtSe2. In contrast to Se‐ or Pt‐vacancies, the Se‐antisites are almost devoid of gap states. Pt‐vacancies exhibit defect induced states that are spin polarized, emphasizing their importance for inducing magnetism in PtSe2. The atomic‐scale insights into defect‐induced electronic states in monolayer PtSe2provide the fundamental underpinning for defect engineering of PtSe2‐monolayers and the newly identified spin‐polarized edge states offer prospects for engineering magnetic properties in PtSe2nanoribbons.more » « less
-
Quartz-based minerals in earth’s crust are well-known to contain water-related defects within their volume-constrained lattice, and they are responsible for strength-loss. Experimental observations of natural α-quartz indicate that such defects appear as hydroxyl groups attached to Si atoms, called Griggs defect (Si-OH), and molecular water (H2O) located at the interstitial sites. However, factors contributing to the formation of Griggs and interstitial H2O defects remain unclear. For example, the role of point defects like vacancy sites (O2− and Si4+), and substitutional (Al3+) and interstitial (Li+, K+, Ca2+, Mg2+, etc.) ions has remained largely unexplored. Here, we performed ab initio molecular dynamics at 300 K to examine the energetics and structure of water-related defects in volume-constrained α-quartz. Several configurations were systematically interrogated by incorporating interstitial H2O, O2− and Si4+ vacancies, substitutional Al3+, and interstitial Li+, Ca2+ and Mg2+ ions within α-quartz. Interstitial H2O defect was found to be energetically favorable in the presence of Substitutional Al3+, and interstitial Ca2+, Mg2+, and Li1+. In the presence of O2− and Si4+ vacancies, H2O showed a strong tendency to dissociate into OH—to form Griggs defect—and a proton; even in the presence of substitutional and interstitial ions. These ions distorted the α-quartz lattice and, in the extreme case, disrupted long-range order to form local amorphous domains; consistent with experimental reports. Our study provides an initial framework for understanding the impact of water within the crystal lattice of an anhydrous silicate mineral such as quartz. We provide not only thermodynamic and process-related information on observed defects, but also provides guidelines for future studies of water’s impact on the behavior of silicate minerals.more » « less
-
Abstract Point defects in two-dimensional materials are of key interest for quantum information science. However, the parameter space of possible defects is immense, making the identification of high-performance quantum defects very challenging. Here, we perform high-throughput (HT) first-principles computational screening to search for promising quantum defects within WS2, which present localized levels in the band gap that can lead to bright optical transitions in the visible or telecom regime. Our computed database spans more than 700 charged defects formed through substitution on the tungsten or sulfur site. We found that sulfur substitutions enable the most promising quantum defects. We computationally identify the neutral cobalt substitution to sulfur (Co$${}_{{{{{{{{\rm{S}}}}}}}}}^{0}$$ ) and fabricate it with scanning tunneling microscopy (STM). The Co$${}_{{{{{{{{\rm{S}}}}}}}}}^{0}$$ electronic structure measured by STM agrees with first principles and showcases an attractive quantum defect. Our work shows how HT computational screening and nanoscale synthesis routes can be combined to design promising quantum defects.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1063/5.0191536