skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Direct observation and quantification of nanosecond laser induced amorphization inside silicon
The nature of structural changes of nanosecond laser modification inside silicon is investigated. Raman spectroscopy and transmission electron microscopy measurements of cross sections of the modified channels reveal highly localized crystal deformation. Raman spectroscopy measurements prove the existence of amorphous silicon inside nanosecond laser induced modifications, and the percentage of amorphous silicon is calculated based on the Raman spectrum. For the first time, the high-resolution transmission electron microscopy images directly show the appearance of amorphous silicon inside nanosecond laser induced modifications, which corroborates the indirect measurements from Raman spectroscopy. The laser modified channel consists of a small amount of amorphous silicon embedded in a disturbed crystal structure accompanied by strain. This finding may explain the origin of the positive refractive index change associated with the written channels that may serve as optical waveguides.  more » « less
Award ID(s):
2107715 2129006
PAR ID:
10507174
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ;
Publisher / Repository:
AIP
Date Published:
Journal Name:
Journal of Laser Applications
Volume:
36
Issue:
2
ISSN:
1042-346X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; (, Advanced Engineering Materials)
    The concept for fabrication of waveguides by an in‐volume laser direct writing in single‐crystal silicon is explored using a nanosecond pulse laser. The key innovation of this technology relies on the generation of amorphous silicon, which has a higher refractive index than that of crystalline silicon. Herein, transmission electron microscopy (TEM) together with selected area electron diffraction (SAED) and high‐resolution TEM (HRTEM) characterizations are used to better understand the microstructural evolutions. TEM images reveal the core‐shell structures, while SAED patterns and HRTEM directly observe the presence of amorphous silicon in the core surrounded by a crystalline silicon shell. With a lower laser scanning speed, a higher density of defects yet less amorphous silicon is formed by laser direct writing. 
    more » « less
  2. ; ; ; ; ; ; (, Optics Express)
    We demonstrate, for the first time, the direct writing of curved optical waveguides in monocrystalline silicon with curve radii from 2 mm to 6 cm. The bending loss of the curved waveguides is measured and a good agreement with theoretical values is found. Raman spectroscopy measurements suggest the formation of inhomogeneous amorphous and polycrystalline phases in the laser-modified region. This direct laser-writing method may advance fabrication capabilities for integrated 3D silicon photonic devices. 
    more » « less
  3. ; ; ; ; ; ; ; (, Materials Science in Semiconductor Processing)
    High-fluence femtosecond laser pulses can induce physical and chemical changes in materials that are unrealizable under standard laboratory conditions. The exact nature of these changes can depend strongly on the gaseous environment in which the material is irradiated since near-surface chemical reactions can occur between the two materials. Surface modifications of silicon are of particular interest due to its significance in semiconductor-based applications. Specifically, the formation of silicon nitride (Si3N4) structures is desirable for multiple applications due to its high stability and low dielectric constant. Herein, we report on femtosecond laser-induced morphological and chemical modifications of silicon in a nitrogen atmosphere. We observed an extremely fast chemical reaction in the silicon-nitrogen system. The presence of crystalline Si3N4 was confirmed using high-resolution transmission electron microscopy, representing the first reported synthesis of Si3N4 nanocrystals through femtosecond laser-based methods. In addition, the surface was found to contain alternating layers of amorphous and crystalline silicon. Provided are plausible mechanisms for the formation of each of these structures. Taken together, these findings on surface modification of silicon using femtosecond laser irradiation may provide new pathways for manufacturing of nanoscale devices. 
    more » « less
  4. ; ; ; ; ; (, Nanoscale)
    We report a pulsed laser annealing method to convert carbon fibers and nanotubes into diamond fibers at ambient temperature and pressure in air. The conversion of carbon nanofibers and nanotubes into diamond nanofibers involves melting in a super undercooled state using nanosecond laser pulses, and quenching rapidly to convert into phase-pure diamond. The conversion process occurs at ambient temperature and pressure, and can be carried out in air. The structure of diamond fibers has been confirmed by selected-area electron diffraction in transmission electron microscopy, electron-back-scatter-diffraction in high-resolution scanning electron microscopy, all showing characteristic diffraction lines for the diamond structure. The bonding characteristics were determined by Raman spectroscopy with a strong peak near 1332 cm −1 , and high-resolution electron-energy-loss spectroscopy in transmission electron microscopy with a characteristic peak at 292 eV for σ* for sp 3 bonding and the absence of π* for sp 2 bonding. The Raman peak at 1332 cm −1 downshifts to 1321 cm −1 for diamond nanofibers due to the phonon confinement in nanodiamonds. These laser-treated carbon fibers with diamond seeds are used to grow larger diamond crystallites further by using standard hot-filament chemical vapor deposition (HFCVD). We compare these results with those obtained without laser treating the carbon fibers. The details of diamond conversion and HFCVD growth are presented in this paper. 
    more » « less
  5. ; ; ; ; ; (, Chemosensors)
    Silicon nanotubes (Si NTs) have a unique structure among the silicon nanostructure family, which is useful for diverse applications ranging from therapeutics to lithium storage/recycling. Their well-defined structure and high surface area make them ideal for sensing applications. In this work, we demonstrate the formation of Au nanoparticles (NPs) functionalized with 4-Mercaptophenylboronic acid (MPBA) on porous Si NTs (pSi NTs) fabricated using ZnO nanowires as a template. The system was characterized, and the proposed structure was confirmed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). Varying glucose concentrations in phosphate-buffered saline (PBS) (0.5–80 mM) were introduced to the Si NT nanocomposite system. The glucose is detectable at low concentrations utilizing surface-enhanced Raman spectroscopy (SERS), which shows a concentration-dependent peak shift in the benzene ring breathing mode (~1071 cm−1) of MPBA. Complementing these measurements are simulations of the Raman hot spots associated with plasmonic enhancement of the Au NPs using COMSOL. This biocompatible system is envisioned to have applications in nanomedicine and microfluidic devices for real-time, non-invasive glucose sensing. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email