Short-range atomic order in semiconductor alloys is a relatively unexplored topic that may promote design of new materials with unexpected properties. Here, local atomic ordering is investigated in Ge–Sn alloys, a group-IV system that is attractive for its enhanced optoelectronic properties achievable via a direct gap for Sn concentrations exceeding ≈10 at. %. The substantial misfit strain imposed on Ge–Sn thin films during growth on bulk Si or Ge substrates can induce defect formation; however, misfit strain can be accommodated by growing Ge–Sn alloy films on Ge nanowires, which effectively act as elastically compliant substrates. In this work, Ge core/Ge 1−x Sn x ( x ≈ 0.1) shell nanowires were characterized with extended x-ray absorption fine structure (EXAFS) to elucidate their local atomic environment. Simultaneous fitting of high-quality EXAFS data collected at both the Ge K-edge and the Sn K-edge reveals a large (≈ 40%) deficiency of Sn in the first coordination shell around a Sn atom relative to a random alloy, thereby providing the first direct experimental evidence of significant short-range order in this semiconductor alloy system. Comparison of path length data from the EXAFS measurements with density functional theory simulations provides alloy atomic structures consistent with this conclusion.
more »
« less
Colloidal Synthesis of Homogeneous Ge1-x-ySiySnx Nanoalloys with Composition-Tunable Visible to Near IR Optical Properties
Group IV alloy nanocrystals (NCs) are a class of direct energy gap semiconductors that show high elemental abundance, low to non-toxicity, and composition-tunable absorption and emission properties. These properties have distinguished Ge1-xSnx NCs as an intriguing material for near-infrared (IR) optical studies. Achieving a material with efficient visible emission requires a modified class of Group IV alloys and the computational studies suggest that this can be achieved with Ge1-x-ySiySnx NCs. Herein, we report a colloidal strategy for the synthesis of bulk-like (10.3 ± 2.5 – 25.5 ± 5.3 nm) and quantum-confined (3.2 ± 0.6 – 4.2 ± 1.1 nm) Ge1-x-ySiySnx alloys that show strong size confinement effects and composition-tunable visible to near IR absorption and emission properties. This synthesis produces a homogeneous alloy with diamond cubic Ge structure and tunable Si (0.9 – 16.1%) and Sn (1.8 – 14.9%) compositions, exceeding the equilibrium solubility of Sn (<1%) in crystalline Si and Ge. Raman spectra of Ge1-x-ySiySnx alloys show a prominent redshift of the Ge-Ge peak and the emergence of a Ge-Si peak with increasing Si/Sn, suggesting the growth of homogeneous alloys. The smaller Ge1-x-ySiySnx NCs exhibit absorption onsets from 1.21 to 1.94 eV for x = 1.8 – 6.8% and y = 0.9 – 16.1% compositions, which are blueshifted from those reported for Ge1-x-ySiySnx bulk alloy films and Ge1-xSnx alloy NCs, indicating the influence of Si incorporation and strong size confinement effects. Solid-state photoluminescence (PL) spectra reveal core-related PL maxima from 1.77 – 1.97 eV in agreement with absorption onsets, consistent with the energy gaps calculated for ~3–4 nm alloy NCs. With facile low-temperature solution synthesis and direct control over physical properties, this methodology presents a noteworthy advancement in the synthesis of bulk-like and quantum-confined Ge1-x-ySiySnx alloys as versatile materials for future optical and electronic studies.
more »
« less
- Award ID(s):
- 2211606
- PAR ID:
- 10513376
- Publisher / Repository:
- American Chemical Society
- Date Published:
- Journal Name:
- Chemistry of Materials
- Volume:
- 35
- Issue:
- 21
- ISSN:
- 0897-4756
- Page Range / eLocation ID:
- 9007 to 9018
- Subject(s) / Keyword(s):
- Quantum dots, Gi/Ge/Sn alloys
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Ge1−x−ySixSny alloys were grown on Ge buffers via reactions of SnH4 and GeH3Cl. The latter is a new CVD source designed for epitaxial development of group-IV semiconductors under low thermal budgets and CMOS-compatible conditions. The Ge1−x−ySixSny films were produced at very low temperatures between 160 and 200 °C with 3%–5% Si and ∼5%–11% Sn. The films were characterized using an array of structural probes that include Rutherford backscattering, x-ray photoelectron spectroscopy, high-resolution x-ray diffraction, scanning transmission electron microscopy, and atomic force microscopy. These studies indicate that the films are strained to Ge and exhibit defect-free microstructures, flat surfaces, homogeneous compositions, and sharp interfaces. Raman was used to determine the compositional dependence of the vibrational modes indicating atomic distributions indistinguishable from those obtained when using high-order Ge hydrides. For a better understanding of the growth mechanisms, a parallel study was conducted to investigate the GeH3Cl applicability for synthesis of binary Ge1−ySny films. These grew strained to Ge, but with reduced Sn compositions and lower thicknesses relative to Ge1−x−ySixSny. Bypassing the Ge buffers led to Ge1−ySny-on-Si films with compositions and thicknesses comparable to Ge1−ySny-on-Ge; but their strains were mostly relaxed. Efforts to increase the concentration and thickness of Ge1−ySny-on-Si resulted in multiphase materials containing large amounts of interstitial Sn. These outcomes suggest that the incorporation of even small Si amounts in Ge1−x−ySixSny might compensate for the large Ge–Sn mismatch by lowering bond strains. Such an effect reduces strain energy, enhances stability, promotes higher Sn incorporation, and increases critical thickness.more » « less
-
The near-bandgap optical properties of Ge1-xSnx alloys were characterized by photovoltage spectroscopy and spectral ellipsometry measurements. Contributions of Urbach tailing as well as direct and indirect optical transitions were observed. The compositional dependence of direct bandgaps of strained GeSn films grown on a Ge buffered Si substrate was studied for up to 15% Sn content. The contribution to the photovoltage spectra of Ge1-xSnx alloys (x < 6%) from indirect optical transitions was observed at lower energies than from direct bandgaps. Using bowing parameters, a correlation was detected between calculated and measured indirect and direct bandgaps at 82 K. As the Sn content was increased, the difference between the energies of the indirect and direct bandgaps decreased, resulting in a smaller contribution of the indirect transitions due to competition with direct transitions and Urbach tails. Two sublayers with different Sn content, strain values and bandgaps were observed for samples with x ~12%. The results indicated that strain relaxation in films with thicknesses exceeding a critical value occurs via formation of a Sn-rich top layer with higher direct bandgap. These findings have important implications when designing IR photodetectors or solar cells.more » « less
-
Size-confined Si nanorods (NRs) have gained notable interest because of their tunable photophysical properties that make them attractive for optoelectronic, charge storage, and sensor technologies. However, established routes for fabrication of Si NRs use well-defined substrates and/or nanoscopic seeds as promoters that cannot be easily removed, hindering the investigation of their true potential and physical properties. Herein, we report a facile, one-step route for the fabrication of Si NRs via thermal disproportionation of hydrogen silsesquioxane (HSQ) in the presence of a molecular tin precursor (SnCl4) at a substantially lower temperature (450 ºC) compared to those used in the synthesis of size-confined Si nanocrystals (>1000 ºC). The use of these precursors allows the facile isolation of phase pure Si NRs via HF etching and subsequent surface passivation with 1-dodecene via hydrosilylation. The diameters (7.7–16.5 nm) of the NRs can be controlled by varying the amount of SnCl4 (0.2–3.0%) introduced during the HSQ synthesis. Physical characterization of the NRs suggests that the diamond cubic structure is not affected by the SnCl4, HF etching, and hydrosilylation. Surface analysis of NRs indicates the presence of Si0 and Sin+ species, which can be attributed to core Si and surface Si species bonded to dodecane ligands, respectively, and a systematic variation of Si0: Si-C ratio with the NR diameter. The NRs show strong size confinement effects with solid-state absorption onsets (2.51–2.80 eV) and solution-state (Tauc) indirect energy gaps (2.54–2.70 eV) that can be tuned by varying the diameters (16.5–7.7 nm), respectively. Photoluminescence (PL) and time-resolved PL (TRPL) studies reveal size-dependent emission (1.95–2.20 eV) with short, nanosecond lifetimes across the visible spectrum which trend closely to absorption trends seen in solid-state absorption data. The facile synthesis developed for size-confined Si NRs with high crystallinity and tunable optical properties will promote their application in optoelectronic, charge storage, and sensing studies.more » « less
-
We report on quantum confined Ge1-x-ySiySnxnanocrystals demonstrating both size- and composition-tunable direct visible/NIR emission (1.77 – 2.47 eV) and recombination dynamics. Temperature-dependent time-resolved photoluminescence suggests significant enhancement of oscillator strengths with Si incorporation.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1021/acs.chemmater.3c01644