Quenching and partitioning (Q&P) processing of third-generation advanced high strength steels generates multiphase microstructures containing metastable retained austenite. Deformation-induced martensitic transformation of retained austenite improves strength and ductility by increasing instantaneous strain hardening rates. This paper explores the influence of martensitic transformation and strain hardening on tensile performance. Tensile tests were performed on steels with nominally similar compositions and microstructures (11.3 to 12.6 vol. pct retained austenite and 16.7 to 23.4 vol. pct ferrite) at 980 and 1180 MPa ultimate tensile strength levels. For each steel, tensile performance was generally consistent along different orientations in the sheet relative to the rolling direction, but a greater amount of austenite transformation occurred during uniform elongation along the rolling direction. Neither the amount of retained austenite prior to straining nor the total amount of retained austenite transformed during straining could be directly correlated to tensile performance. It is proposed that stability of retained austenite, rather than austenite volume fraction, greatly influences strain hardening rate, and thus controls strength and ductility. If true, this suggests that tailoring austenite stability is critical for optimizing the forming response and crash performance of quenched and partitioned grades.
more »
« less
This content will become publicly available on March 1, 2026
Martensitic transformation induced strength-ductility synergy in additively manufactured maraging 250 steel by thermal history engineering
Maraging steels are known for their exceptional strength but suffer from limited work hardening and ductility. Here, we report an intermittent printing approach to tailor the microstructure and mechanical properties of maraging 250 steel via engineering of the thermal history during plasma arc additive manufacturing (PAAM). Through introducing a dwell time between adjacent layers, the maraging 250 steel is cooled below the martensite start temperature, triggering a thermally driven, in-situ martensitic transformation during the printing process. Re-heating or thermal cycling during subsequent layer deposition impedes complete martensitic transformation, enabling coexistence of martensite and retained austenite phases with elemental segregation. The enrichment of Ni in the austenite phase promotes stabilization of the retained austenite upon cooling down to room temperature. The retained austenite is yet metastable during deformation, leading to stress-induced martensitic transformation under loading. Specifically, a 3 min interlayer dwell time produces a maraging 250 steel with approximately 8% retained austenite, resulting in improved work hardening via martensitic transformation induced plasticity (TRIP) during deformation. Meanwhile, the higher cooling rate induced by the dwell time results in substantially refined grain structures with an increased dislocation density, leading to a simultaneously improved yield strength. Notably, the yield strength increases from 836 MPa (0 min dwell) to 990 MPa (3 min dwell), and the uniform elongation increases from 3.2% (0 min dwell) to 6.5% (3 min dwell). This intermittent deposition strategy demonstrates the potential to tune the microstructure and mechanical properties of maraging steels through engineering the thermal history during additive manufacturing.
more »
« less
- Award ID(s):
- 2207965
- PAR ID:
- 10519056
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Journal of Materials Science & Technology
- Volume:
- 211
- Issue:
- C
- ISSN:
- 1005-0302
- Page Range / eLocation ID:
- 212 to 225
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Microstructure refinement strategies in simulated carburized microstructures were evaluated because of their potential for improving the fatigue performance of case carburized components. Commercial 52100 steel was used to simulate the high carbon content in the case. Specimens were subjected to various thermal treatments in a quenching dilatometer. Reheating cycles to austenitizing temperatures were evaluated with respect to both prior austenite grain size (PAGS) and associated martensite and retained austenite (RA) refinement. Quantitative stereological measurements were performed to evaluate the micro-geometry of plate martensite and the size distribution of RA regions. Decreasing the reheating temperature resulted in finer PAGS, and multiple reheating cycles resulted in a more narrow PAGS distribution. Refinement in PAGS led to a reduction in martensite plate size and finer distribution of RA. Additionally, interrupted quenching below MS temperature was evaluated. This processing route results in a refinement of martensite plates and more stable RA. The stabilization of austenite may be mechanical or chemical in nature, owing to deformation of austenite during primary transformation, or due to partitioning of carbon into austenite similar to quenching and partitioning steels.more » « less
-
In a recent work, we have reported outstanding strength and work hardening exhibited by a metastable high entropy alloy (HEA), Fe42Mn28Co10Cr15Si5 (in at. %), undergoing the strain-induced martensitic transformation from metastable gamma austenite (γ) to stable epsilon martensite (ε). However, the alloy exhibited poor ductility, which was attributed to the presence of the brittle sigma (σ) phase in its microstructure. The present work reports the evolution of microstructure, strength, and ductility of a similar HEA, Fe38.5Mn20Co20Cr15Si5Cu1.5 (in at. %), designed to suppress the formation of σ phase. A cast and then rolled plate of the alloy was processed into four conditions by annealing for 10 and 30 min at 1100 °C and by friction stir processing (FSP) at tool rotation rates of 150 and 400 revolutions per minute (RPM) to facilitate detailed examinations of variable initial grain structures. Neutron diffraction and electron microscopy were employed to characterize the microstructure and texture evolution. The initial materials had variable grain size but nearly 100% γ structure. Diffusionless strain induced γ→ε phase transformation took place under compression with higher rate initially and slower rate at the later stages of deformation, independent on the initial grain size. The transformation facilitated part of plastic strain accommodation and rapid strain hardening owing to a transformation-induced dynamic Hall-Petch-type barrier effect, increase in dislocation density, and texture. The peak strength of nearly 2 GPa was achieved under compression using the structure created by double pass FSP (150 RPM followed by 150 RPM). Remarkably, the tensile elongation exhibited by the alloy was nearly 20% with fracture surfaces featuring a combination of ductile dimples and cleavage.more » « less
-
Abstract The individual effects of strain rate and temperature on the strain hardening rate of a quenched and partitioned steel have been examined. During quasistatic tests, resistive heating was used to simulate the deformation-induced heating that occurs during high-strain-rate deformation, while the deformation-induced martensitic transformation was tracked by a combination of x-ray and electron backscatter diffraction. Unique work hardening rates under various thermal–mechanical conditions are discussed, based on the balance between the concurrent dislocation slip and transformation-induced plasticity deformation mechanisms. The diffraction and strain hardening data suggest that the imposed strain rate and temperature exhibited dissonant influences on the martensitic phase transformation. Increasing the strain rate appeared to enhance the martensitic transformation, while increasing the temperature suppressed the martensitic transformation.more » « less
-
Daehn G., Cao J. (Ed.)Controlling the microstructure of components is of interest to achieve optimal final part properties, i.e., materials by design. The manufacturing process itself can affect a material’s characteristics by changing the microstructure. For example, past research has shown that austenite to martensite phase transformation in stainless steel occurs during deformation. Temperature is known to have a significant influence on this phenomenon. In this paper, the effect of temperature on the austenitic to martensite phase transformation in SS 316L under uniaxial tension is investigated. Both a cooling system and a heat exchanger were employed in a uniaxial tension experimental setup to control the temperature. Tensile specimens were strained to fracture at four temperatures of −15, 0, 10, and 20 °C. Digital imaging correlation (DIC) and a thermal imaging camera were used for tests at 0 °C and above to capture strain and temperature data, respectively. Strain and temperature data could not be obtained at −15 °C due to the DIC paint flaking during testing. X-ray diffraction was used to measure the volume fraction of martensite in both the as-received and the tensile-tested materials.more » « less