Abstract The postdrawing process is poorly understood for polymer nanofibers due to the difficulty of manipulating nanofiber structures. Here, an angled track system facilitates postdrawing of individual nanofibers with control of parameters including molecular weight, draw rate, draw ratio, and solvent evaporation time. In this study, the effects of molecular weight, draw rate, and relative residual solvent content on final nanofiber properties are investigated. Molecular weight is first investigated to clarify any influence polymer chain length can have on drawing in facilitating or hindering chain extensibility. Polyacrylonitrile nanofibers with 50 and 150 kDa molecular weights behave similarly with postdrawing resulting in reduced diameters and enhanced mechanics. Since solvent quantity during drawing is a time sensitive component it is meaningful to assess the impact of draw rate on the chemical and structural makeup of postdrawn fibers. Chemical bond vibrations and chain orientation are sensitive to draw rate when polycaprolactone nanofibers are dried for 3 minutes prior to postdrawing, but this dependency to draw rate is not observed when fibers are postdrawn immediately upon collection. These findings demonstrate that the amount of retained solvent at collection is relevant to this postprocessing approach, and highlights the dynamics of solvent evaporation during postdrawing.
more »
« less
Precise Fabrication and Manipulation of Individual Polymer Nanofibers
Polymer nanofibers hold promise in a wide range of applications owing to their diverse properties, flexibility, and cost effectiveness. In this study, we introduce a polymer nanofiber drawing process in a scanning electron microscope and focused ion beam (SEM/FIB) instrument with in situ observation. We employed a nanometer-sharp tungsten needle and prepolymer microcapsules to enable nanofiber drawing in a vacuum environment. This method produces individual polymer nanofibers with diameters as small as ∼500 nm and lengths extending to millimeters, yielding nanofibers with an aspect ratio of 2000:1. The attachment to the tungsten manipulator ensures accurate transfer of the polymer nanofiber to diverse substrate types as well as fabrication of assembled structures. Our findings provide valuable insights into ultrafine polymer fiber drawing, paving the way for high-precision manipulation
more »
« less
- PAR ID:
- 10519446
- Publisher / Repository:
- American Chemical Society
- Date Published:
- Journal Name:
- Nano Letters
- Volume:
- 24
- Issue:
- 20
- ISSN:
- 1530-6984
- Page Range / eLocation ID:
- 6038 to 6042
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Laser zone‐drawing is shown to significantly enhance control over nanofiber properties. This study investigates the dynamics of nanofiber laser zone‐drawing. It is hypothesized that the equilibrium between heating and cooling guides fiber temperature. The high heating rate of laser irradiation and the high convective cooling rate of nanofibers facilitate fast heating and cooling kinetics. Results showed fiber thinning in the presence of laser irradiation until reaching a steady‐state diameter. Final fiber diameter is correlated to laser power independent of initial fiber diameter. The relationship between final fiber diameter and laser power is used to estimate the heat transfer coefficient, which is used to create a computational model of the thermodynamic system. These simulations predict rapid heating and cooling up to 36 000 K min−1for the lowest fiber diameters tested experimentally. While laser‐induced softening of polymer nanofibers is described in detail, the forces driving fiber drawing, particularly under different thermal kinetics, remain unexplored. This research showcases the capabilities of laser zone‐drawing in nanofiber manufacturing and facilitates future investigations aimed at enhancing fiber processing by producing highly aligned molecular structures via rapid cooling. This work signifies a pivotal methodological leap, promising transformative nanofiber materials useful across multiple industries including aerospace, electronics, and biomedicine.more » « less
-
In an effort to develop and design next generation high power target materials for particle physics research, the possibility of fabricating nonwoven metallic or ceramic nanofibers by electrospinning process is explored. A low-cost electrospinning unit is set up for in-house production of various ceramic nanofibers. Yttria-stabilized zirconia nanofibers are successfully fabricated by electrospinning a mixture of zirconium carbonate with high-molecular weight polyvinylpyrrolidone polymer solution. Some of the inherent weaknesses of electrospinning process like thickness of nanofiber mat and slow production rate are overcome by modifying certain parts of electrospinning system and their arrangements to get thicker nanofiber mats of millimeter order at a faster rate. Continuous long nanofibers of about hundred nanometers in diameter are produced and subsequently heat treated to get rid of polymer and allow crystallize zirconia. Specimens were prepared to meet certain minimum physical properties such as thickness, structural integrity, thermal stability, and flexibility. An easy innovative technique based on atomic force microscopy was employed for evaluating mechanical properties of single nanofiber, which were found to be comparable to bulk zirconia. Nanofibers were tested for their high-temperature resistance using an electron beam. It showed resistance to radiation damage when irradiated with 1 MeV Kr2+ ion. Some zirconia nanofibers were also tested under high-intensity pulsed proton beam and maintained their structural integrity. This study shows for the first time that a ceramic nanofiber has been tested under different beams and irradiation condition to qualify their physical properties for practical use as accelerator targets. Advantages and challenges of such nanofibers as potential future targets over bulk material targets are discussed.more » « less
-
Abstract A parallel automated track collector is integrated with a rationally designed centrifugal spinning head to collect aligned polyacrylonitrile (PAN) nanofibers. Centrifugal spinning is an extremely promising nanofiber fabrication technology due to high production rates. However, continuous oriented fiber collection and processing presents challenges. Engineering solutions to these two challenges are explored in this study. A 3D‐printed head design, optimized through a computational fluid dynamics simulation approach, is utilized to limit unwanted air currents that disturb deposited nanofibers. An automated track collecting device has pulled deposited nanofibers away from the collecting area. This results in a continuous supply of individual aligned nanofibers as opposed to the densely packed nanofiber mesh ring that is deposited on conventional static post collectors. The automated track collector allows for simple integration of the postdraw processing step that is critical to polymer fiber manufacturing for enhancing macromolecular orientation and mechanical properties. Postdrawing has enhanced the mechanical properties of centrifugal spun PAN nanofibers, which have different crystalline properties compared with conventional PAN microfiber. These technological developments address key limitations of centrifugal spinning that can facilitate high production rate commercial fabrication of highly aligned, high‐performance polymer nanofibers.more » « less
-
Abstract Nanofibers have attracted significant interest due to their unique properties such as high specific surface area, high aspect ratio, and spatial interconnectivity. Nanofibers can exhibit multifunctional properties and unique opportunities for promising applications in a wide variety of fields. Hierarchical design strategies are being used to prescribe the internal structure of nanofibers, such as core-sheath, concentric layers, particles distributed randomly or on a lattice, and co-continuous network phases. This review presents a comprehensive overview of design strategies being used to produce the next generation of nanofiber systems. It includes a description of nanofiber processing methods and their effects on the nano- and microstructure. Physico-chemical effects, such as self-assembly and phase separation, on the ultimate morphology of fibers made from designed emulsions, polymer blends, and block copolymers, are then described. This review concludes with perspectives on existing challenges and future directions for hierarchical design strategies to produce internally structured nanofibers.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1021/acs.nanolett.4c00799