Recent research in multi-principal element alloys (MPEAs) has increasingly focused on the role of short-range order (SRO) on material performance. However, the mechanisms of SRO formation and its precise control remain elusive, limiting the progress of SRO engineering. Here, leveraging advanced additive manufacturing techniques that produce samples with a wide range of cooling rates (up to 107 K s−1) and an enhanced semi-quantitative electron microscopy method, we characterize SRO in three CoCrNi-based face-centered-cubic (FCC) MPEAs. Surprisingly, irrespective of the processing and thermal treatment history, all samples exhibit similar levels of SRO. Atomistic simulations reveal that during solidification, prevalent local chemical order arises in the liquid-solid interface (solidification front) even under the extreme cooling rate of 1011 K s−1. This phenomenon stems from the swift atomic diffusion in the supercooled liquid, which matches or even surpasses the rate of solidification. Therefore, SRO is an inherent characteristic of most FCC MPEAs, insensitive to variations in cooling rates and even annealing treatments typically available in experiments.
This content will become publicly available on December 1, 2025
The far-from-equilibrium solidification during additive manufacturing often creates large residual stresses that induce solid-state cracking. Here we present a strategy to suppress solid-state cracking in an additively manufactured AlCrFe2Ni2high-entropy alloy via engineering phase transformation pathway. We investigate the solidification microstructures formed during laser powder-bed fusion and directed energy deposition, encompassing a broad range of cooling rates. At high cooling rates (104−106 K/s), we observe a single-phase BCC/B2 microstructure that is susceptible to solid-state cracking. At low cooling rates (102−104 K/s), FCC phase precipitates out from the BCC/B2 matrix, resulting in enhanced ductility (~10 %) and resistance to solid-state cracking. Site-specific residual stress/strain analysis reveals that the ductile FCC phase can largely accommodate residual stresses, a feature which helps relieve residual strains within the BCC/B2 phase to prevent cracking. Our work underscores the value of exploiting the toolbox of phase transformation pathway engineering for material design during additive manufacturing.
more » « less- Award ID(s):
- 2238204
- NSF-PAR ID:
- 10523867
- Publisher / Repository:
- Nature Publishing Group
- Date Published:
- Journal Name:
- Communications Materials
- Volume:
- 5
- Issue:
- 1
- ISSN:
- 2662-4443
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
In functionally graded materials (FGMs) fabricated using directed energy deposition (DED) additive manufacturing (AM), cracks may form due to interdendritic stress during solidification, the formation of deleterious phases, or the buildup of residual stresses. This study builds on our previously proposed concept of FGM feasibility diagrams to identify gradient pathways that avoid deleterious phases in FGMs by also considering hot cracking. Here, five hot cracking criteria were integrated into the feasibility diagrams, and equilibrium simulations were carried out based on Scheil results (termed hybrid Scheil-equilibrium simulation) to predict phase formation below the solidus temperature considering solidification micro-segregation. The new feasibility diagrams were applied to four previously studied FGMs, and the newly proposed approach predicted high crack susceptibility, detrimental phase formation, or interdendritic BCC phase formation in the experimentally observed cracking region. This demonstrates the utility of the proposed framework for crack prediction in the design of future FGMs gradient pathways.more » « less
-
Both CALPHAD (CALculation of PHAse Diagrams) and machine-learning (ML) approaches were employed to analyze the phase formation in 2,436 experimentally measured high entropy alloy (HEA) compositions consisting of various quinary mixtures of Al, Co, Cr, Cu, Fe, Mn, and Ni. CALPHAD was found to have good capabilities in predicting the BCC/B2 and FCC phase formation for the 1,761 solid-solution-only compositions, excluding HEAs containing an amorphous phase (AM) or/and intermetallic compound (IM). Phase selection rules were examined systematically using several parameters and it revealed that valency electron concentration (VEC) < 6.87 and VEC > 9.16 are the conditions for the formation of single-phase BCC/B2 and FCC, respectively; and CALPHAD could predict this with essentially 100% accuracy. Both CALPHAD predictions and experimental observations show that more BCC/B2 alloys are formed over FCC alloys as the atomic size difference between the elements increases. Four machine learning (ML) algorithms, decision tree (DT), k-nearest neighbor (KNN), support vector machine (SVM), and artificial neural network (ANN), were employed to study the phase selection rules for two different datasets, one consisting of 1,761 solid-solution (SS) HEAs without AM and/or IM phases, and the other set consisting of all the 2,436 HEA compositions. Cross validation (CV) was performed to optimize the ML models and the CV accuracies are found to be 91.4%, 93.1%, 90.2%, 89.1% for DT, KNN, SVM, and ANN respectively in predicting the formation of BCC/B2, BCC/B2 + FCC, and FCC; and 93.6%, 93.3%, 95.5%, 92.7% for DT, KNN, SVM, and ANN respectively in predicting SS, AM, SS + AM, and IM phases. Sixty-six experimental bulk alloys with SS structures are predicted with trained ANN model, and the accuracy reaches 81.8%. VEC is found to be most important parameter in phase prediction for BCC/B2, BCC/B2 + FCC, and FCC phases. Electronegativity difference and FCC-BCC-index (FBI) are the two additional dominating features in determining the formation of SS, AM, SS + AM, and IM. A separation line ΔH_mix=28.97×VEC-246.77 was found in the VEC-vs-ΔH_mix plot to predict the formation of single-phase BCC/B2 or FCC with a 96.2% accuracy (ΔH_mix = mixing enthalpy). These insights will be very valuable for designing HEAs with targeted crystal structures.more » « less
-
more » « less
Abstract This paper examined the effect of Si addition on the cracking resistance of Inconel 939 alloy after laser additive manufacturing (AM) process. With the help of CALculation of PHAse Diagrams (CALPHAD) software Thermo-Calc, the amounts of specific elements (C, B, and Zr) in liquid phase during solidification, cracking susceptibility coefficients (CSC) and cracking criterion based on
$$\left| {{\text{d}}T/{\text{d}}f_{{\text{s}}}^{1/2} } \right|$$ T : solidification temperature,f s: mass fraction of solid during solidification) were evaluated as the indicators for composition optimization. It was found that CSC together with$$\left| {{\text{d}}T/{\text{d}}f_{{\text{s}}}^{1/2} } \right|$$ Graphical abstract -
more » « less
Abstract A face-centered-cubic (fcc) oriented FeCoCrNiAl0.5dual-phase high entropy alloy (HEA) was plastically strained in uniaxial compression at 77K and 293K and the underlying deformation mechanisms were studied. The undeformed microstructure consists of a body-centered-cubic (bcc)/B2 interdendritic network and precipitates embedded in 〈001〉-oriented fcc dendrites. In contrast to other dual-phase HEAs, at both deformation temperatures a steep rise in the stress-strain curves occurs above 23% total axial strain. As a result, the hardening rate associated saturates at the unusual high value of ~6 GPa. Analysis of the strain partitioning between fcc and bcc/B2 by digital image correlation shows that the fcc component carries the larger part of the plastic strain. Further, electron backscatter diffraction and transmission electron microscopy evidence ample fcc deformation twinning both at 77K and 293K, while slip activity only is found in the bcc/B2. These results may guide future advancements in the design of novel alloys with superior toughening characteristics.