Abstract MXenes are among the fastest‐growing families of 2D materials, promising for high‐rate, high‐energy energy storage applications due to their high electronic and ionic conductivity, large surface area, and reversible surface redox ability. The Ti3C2TxMXene shows a capacitive charge storage mechanism in diluted aqueous LiCl electrolyte while achieving abnormal redox‐like features in the water‐in‐salt LiCl electrolyte. Herein, variousoperandotechniques are used to investigate changes in resistance, mass, and electrode thickness of Ti3C2Txduring cycling in salt‐in‐water and water‐in‐salt LiCl electrolytes. Significant resistance variations due to interlayer space changes are recorded in the water‐in‐salt LiCl electrolyte. In both electrolytes, conductivity variations attributed to charge carrier density changes or varied inter‐sheet electron hopping barriers are detected in the capacitive areas, where no thickness variations are observed. Overall, combining thoseoperandotechniques enhances the understanding of charge storage mechanisms and facilitates the development of MXene‐based energy storage devices.
more »
« less
Universal salt-assisted assembly of MXene from suspension on polymer substrates
Abstract Two-dimensional carbides and nitrides, known as MXenes, are promising for water-processable coatings due to their excellent electrical, thermal, and optical properties. However, depositing hydrophilic MXene nanosheets onto inert or hydrophobic polymer surfaces requires plasma treatment or chemical modification. This study demonstrates a universal salt-assisted assembly method that produces ultra-thin, uniform MXene coatings with exceptional mechanical stability and washability on various polymers, including high-performance polymers for extreme temperatures. The salt in the Ti3C2Txcolloidal suspension reduces surface charges, enabling electrostatically hydrophobized MXene deposition on polymers. A library of salts was used to optimize assembly kinetics and coating morphology. A 170 nm MXene coating can reduce radiation temperature by ~200 °C on a 300 °C PEEK substrate, while the coating on Kevlar fabric provides comfort in extreme conditions, including outer space and polar regions.
more »
« less
- PAR ID:
- 10556537
- Publisher / Repository:
- Nature Publishing Group
- Date Published:
- Journal Name:
- Nature Communications
- Volume:
- 15
- Issue:
- 1
- ISSN:
- 2041-1723
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Modification of a surface with polymer brushes has emerged as an effective approach to tune the properties of a substrate. Brushes grown from an inimer‐containing cross‐linkable polymer coating provide significant advantages compared to other “grafting‐from” methods, such as improved stability, increased grafting density, and the potential to control the grafting density. So far, the inimer coating method has only been applied for surface‐initiated controlled radical polymerizations. In this work, an approach is presented for the fabrication of a stable cross‐linked ultra‐thin polymer coating containing hydroxyl groups which serve as initiating sites for surface‐initiated ring‐opening polymerization (SI‐ROP). The polymers used for the fabrication of the coatings consist of 2‐((tetrahydro‐2H‐pyran‐2‐yl)oxy)ethyl methacrylate (THPEMA), a small fraction of a cross‐linkable unit, and a diluent styrene. Three coatings with varying THPEMA and styrene content are fabricated, and poly(dimethyl siloxane) (PDMS) and poly(caprolactone) (PCL) brushes are grown by SI‐ROP of hexamethylcyclotrisiloxane (D3), and ε‐caprolactone respectively. The brushes are characterized by atomic force microscopy (AFM), X‐ray photoelectron spectroscopy (XPS), static contact angle measurements, ellipsometry and size exclusion chromatography (SEC). The results demonstrate a well‐controlled ROP of D3and ability to control grafting density by tuning the THPEMA content of the coatings.more » « less
-
Abstract Highly integrated, flexible, and ultrathin wireless communication components are in significant demand due to the explosive growth of portable and wearable electronic devices in the fifth‐generation (5G) network era, but only conventional metals meet the requirements for emerging radio‐frequency (RF) devices so far. Here, it is reported on Ti3C2TxMXene microstrip transmission lines with low‐energy attenuation and patch antennas with high‐power radiation at frequencies from 5.6 to 16.4 GHz. The radiation efficiency of a 5.5 µm thick MXene patch antenna manufactured by spray‐coating from aqueous solution reaches 99% at 16.4 GHz, which is about the same as that of a standard 35 µm thick copper patch antenna at about 15% of its thickness and 7% of the copper weight. MXene outperforms all other materials evaluated for patch antennas to date. Moreover, it is demonstrated that an MXene patch antenna array with integrated feeding circuits on a conformal surface has comparable performance with that of a copper antenna array at 28 GHz, which is a target frequency in practical 5G applications. The versatility of MXene antennas in wide frequency ranges coupled with the flexibility, scalability, and ease of solution processing makes MXene promising for integrated RF components in various flexible electronic devices.more » « less
-
Abstract In this study, we demonstrate a novel environmental barrier coating processed from polymer‐derived ceramics (PDCs) with homogeneously distributed sub‐micrometer Y2O3as the filler. Under suitable conditions, dense and crack‐free coatings can be achieved for all the designed compositions with the volumetric content of Y2O3varied from 45 to 93 vol%. To process the PDC SiC–Y2O3composite coatings, Y2O3particles and SiC liquid precursor were uniformly dispersed in hexane and then dip‐coated on SiC substrates. After cross‐linking at 250°C and heat‐treated at 900°C in argon, dense and crack‐free PDC SiC–Y2O3composite coatings were formed. The effect of coating thickness and heat‐treatment temperature on the formation of cracks due to constrained pyrolysis was studied. The critical thickness for realizing crack‐free coatings of three compositions (i.e., 93, 77, and 45 vol% Y2O3) was studied for heat treatment from 1000 to 1300°C using atomic force microscope and scanning electron microscopy. As heat‐treatment temperature increases, the critical coating thickness decreases for the same coating compositions due to enhanced shrinkage at higher temperature. With higher Y2O3content, the critical thickness of the coating increased. The inert Y2O3particles reduce the amount of polymer leading to reduction in the overall constrained shrinkage of the coating during heat treatment.more » « less
-
Abstract To advance the MXene field, it is crucial to optimize each step of the synthesis process and create a detailed, systematic guide for synthesizing high‐quality MXene that can be consistently reproduced. In this study, a detailed guide is provided for an optimized synthesis of titanium carbide (Ti3C2Tx) MXene using a mixture of hydrofluoric and hydrochloric acids for the selective etching of the stoichimetric‐Ti3AlC2MAX phase and delamination of the etched multilayered Ti3C2TxMXene using lithium chloride at 65 °C for 1 h with argon bubbling. The effect of different synthesis variables is investigated, including the stoichiometry of the mixed powders to synthesize Ti3AlC2, pre‐etch impurity removal conditions, selective etching, storage, and drying of MXene multilayer powder, and the subsequent delamination conditions. The synthesis yield and the MXene film electrical conductivity are used as the two parameters to evaluate the MXene quality. Also the MXenes are characterized with scanning electron microscopy, x‐ray diffraction, atomic force microscopy, and ellipsometry. The Ti3C2Txfilm made via the optimized method shows electrical conductivity as high as ≈21,000 S/cm with a synthesis yield of up to 38 %. A detailed protocol is also provided for the Ti3C2TxMXene synthesis as the supporting information for this study.more » « less