Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Preparation of Performance-Enhanced Alkali-Activated Slag by Using L-Ascorbic Acid
The applications of alkali-activated slag (AAS) face challenges such as poor workability, rapid setting, and high autogenous shrinkage, which require chemical admixtures (CAs) to adjust the performance of AAS. Unfortunately, there are limited specific CAs available to tune AAS properties. To address this gap, this study proposes using a ubiquitous, naturally occurring compound, L-ascorbic acid (LAA), as a multifunctional performanceenhancing additive for AAS to overcome the major challenges of AAS. The findings showed that LAA can function as a retarder, plasticizer, strength enhancer, and autogenous shrinkage reducer for AAS. When 0.5% LAA was added, the compressive strengths of AAS mortars at 3 and 28 days increased by 28.9% and 19.6%, respectively, and the 28-day autogenous shrinkage decreased by 43.1%. Both surface adsorption and ion complexation have been confirmed as the working mechanisms of LAA in hydrated AAS.  more » « less
Award ID(s):
1761672
PAR ID:
10556807
Author(s) / Creator(s):
; ; ; ;
Publisher / Repository:
ACI
Date Published:
Journal Name:
ACI Materials Journal
Volume:
121
Issue:
5
ISSN:
0889-325X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; (, International Journal of Concrete Structures and Materials)
    Abstract While ultra-high performance concrete (UHPC) offers numerous advantages, it also presents specific challenges, primarily due to its high cost and excessive cement content, which can pose sustainability concerns. To address this challenge, this study aims to develop cost-effective and sustainable UHPC mixtures by incorporating ground granulated blast furnace slag (GGBFS) and limestone powder (LP) as partial replacements for portland cement. Eight fiber-reinforced UHPC mixtures were investigated, with a water-to-cementitious materials (w/cm) ratio of 0.15. In four of the UHPC mixtures, 25% of the cement was replaced with GGBFS, and further, LP was added as a mineral filler, partially substituting up to 20% of the cement. In the remaining four mixtures, cement was replaced with only LP up to 20% (without GGBFS). The 28-day compressive strength of the UHPC mixture with 25% GGBFS and 20% LP was 149 MPa, 3.50% lower than the mixture without GGBFS. Its 28-day flexural strength decreased by 30%. Increasing LP replacement reduced drying and autogenous shrinkage, with a 29% shrinkage reduction at 20% LP replacement. Moreover, UHPC mixtures with GGBFS exhibited lower shrinkage compared to those without GGBFS for all LP replacements up to 20%. For evaluating the sustainability of UHPC mixtures, the cement composition index (CCI) and clinker to cement ratio (CCR) were determined. For 20% LP replacement with 25% GGBFS, CCI was 3.6 and the CCR was 0.5, 38% decrease from the global clinker to cement ratio. Overall, 20% LP replacement UHPC mixtures with and without GGBFS can produce UHPC class performance and reduce the environmental impact. 
    more » « less
  2. ; ; ; (, Construction Materials)
    This paper examines the influence of biochar on the properties of alkali-activated slag pastes using two activator solutions, namely NaOH and Na2CO3. The biochar demonstrated different absorption kinetics in the mixture of slag and the two activator solutions. The pastes with biochar showed a delay in the heat flow peak, compared to the pastes without biochar, but the cumulative heat release in these pastes at later hours was increased, compared to the pastes without biochar. It was found that the use of biochar reduced autogenous shrinkage in the pastes and the reduction in autogenous shrinkage was more pronounced in the alkali-activated slag with NaOH, compared to Na2CO3. The void structure of the pastes was investigated using x-ray micro-computed tomography. It was found that refined pore structure due to reduced effective solution/slag in the pastes with biochar was able to compensate for the decreasing effect of biochar voids on compressive strength. The electrical resistivity was shown to be lower in the pastes with biochar. 
    more » « less
  3. ; ; (, Journal of Composites Science)
    null (Ed.)
    The effect of hydrogels containing nanosilica (NSi) on the autogenous shrinkage, mechanical strength, and electrical resistivity of cement pastes was studied. The interaction between the hydrogels and the surrounding cementitious matrix was examined using thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The addition of hydrogels decreased autogenous shrinkage in the cement pastes and this reduction showed a dependence on the concentration of NSi in the hydrogels. Compressive strength and electrical resistivity were reduced in the cement pastes with hydrogels and this reduction was decreased with increased concentration of NSi in the hydrogel. A change in the phase composition of the cement paste in the region close to the hydrogel was noted, compared to the region away from the hydrogel. In a lime solution with increased pH and temperature, Ca(OH)2 and CaCO3 were found to form within the hydrogels; evidence of calcium-silicate-hydrate (C-S-H) formation in the hydrogels with NSi was obtained, indicating the possible pozzolanic potential of the hydrogels with NSi. 
    more » « less
  4. ; (, Buildings)
    This study investigates the hydration, microstructure, autogenous shrinkage, electrical resistivity, and mechanical properties of Portland cement pastes modified with PEG-PPG triblock copolymers with varied molecular weights. The early age properties including setting time and hydration heat were examined using the Vicat test and isothermal calorimetry. The hydration products and pore size distribution were analyzed using thermogravimetric analysis (TGA) and nitrogen adsorption, respectively. Mechanical properties and electrical resistivity were evaluated using the compressive strength test and electrochemical impedance spectroscopy (EIS). It was shown that the addition of the copolymers reduced the surface tension of the cement paste pore solution due to the presence of a hydrophobic block (PPG) in the molecular structure of the copolymers. The setting time and hydration heat were relatively similar in the control paste as well as the pastes modified with the copolymers. The results showed that copolymers were able to reduce the autogenous shrinkage in the paste due primarily to a reduction in pore solution surface tension. TGA showed a slight increase in the hydration degree of the paste modified with the copolymers. The compressive strength was reduced in the pastes modified with the copolymers that showed an increased volume of air voids. The addition of copolymers did not affect the electrical resistivity of the pastes except in the case where there was a large volume of air voids, which acted as electrical insulators. 
    more » « less
  5. ; (, Construction and Building Materials)
    A novel internal conditioning (InCon) technique based on saturated sodium montmorillonite (sMT) functionalized with two non-ionic surfactants, polyoxyethylene (9) nonylphenylether and t-octyl phenoxy poly ethoxyethanol, is investigated in this study. With the integration of water for internal curing and pozzolanic reactivity in a single system, the role of InCon in modifying cement hydration kinetics is comprehensively elucidated. The results indicate that, in the presence of InCon, both silicate reaction and secondary aluminate reaction rates are enhanced, and the apparent activation energy (Ea) of cement hydration was decreased from 34.3 KJ/mol to 28.7 KJ/mol indicating a lower temperature sensitivity and threshold of the cement hydration reactions. In addition, decreased CH contents, improved degree of hydration, increased chemical shrinkage, and the formation of additional Csingle bondSsingle bondH and aluminum-containing phases were obtained from the cement with InCon. The autogenous shrinkage of cement and the negative impact of dry sMT on the early age strength of cement can be offset by InCon paving a new path to improve the overall properties of concrete. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email