Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • NSF Public Access
  • Search Results
  • The Effect of Elastomer Content and Annealing on the Physical Properties of Upcycled Polyethylene Terephthalate-Maleated Styrene Ethylene Butylene Styrene Blends for Additive Manufacturing
Title: The Effect of Elastomer Content and Annealing on the Physical Properties of Upcycled Polyethylene Terephthalate-Maleated Styrene Ethylene Butylene Styrene Blends for Additive Manufacturing
In the work presented here, we explore the upcycling of polyethylene terephthalate (PET) that was derived from water bottles. The material was granulated and extruded into a filament compatible with fused filament fabrication (FFF) additive manufacturing platforms. Three iterations of PET combined with a thermoplastic elastomer, styrene ethylene butylene styrene with a maleic anhydride graft (SEBS-g-MA), were made with 5, 10, and 20% by mass elastomer content. The elastomer and specific mass percentages were chosen based on prior successes involving acrylonitrile butadiene styrene (ABS), in which the maleic anhydride graft enabled compatibility between different materials. The rheological properties of PET and the PET/SEBS blends were characterized by the melt flow index and dynamic mechanical analysis. The addition of SEBS-g-MA did not have a significant impact on mechanical properties, as determined by tensile and impact testing, where all test specimens were manufactured by FFF. Delamination of the tensile specimens convoluted the ability to discern differences in the mechanical properties, particularly % elongation. Annealing of the specimens enabled the observation of the effect of elastomer content on the mechanical properties, particularly in the case of impact testing, where the impact strength increased with the increase in SEBS content. However, annealing led to shrinkage of the specimens, detracting from the realized benefits of the thermal process. Scanning electron microscopy of spent tensile specimens revealed that, in the non-annealed condition, SEBS formed nodules that would detach from the PET matrix during the tensile test, indicating that a robust bond was not present. The addition of SEBS-g-MA did allow for shape memory property characterization, where deformation of tensile specimens occurred at room temperature. Specimens from the 20% by mass elastomer content sample group exhibited a shape fixation ratio on the order of 99% and a shape recovery ratio on the order of 80%. This work demonstrates a potential waste reduction strategy to tackle the problem of polymer waste by upcycling discarded plastic into a feedstock material for additive manufacturing with shape memory properties.  more » « less
Award ID(s):
2227573
PAR ID:
10562660
Author(s) / Creator(s):
; ;
Editor(s):
Santagata, Antonio
Publisher / Repository:
MDPI
Date Published:
Journal Name:
Materials
Volume:
17
Issue:
24
ISSN:
1996-1944
Page Range / eLocation ID:
6272
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; (, Materials)
    The goal of this paper was to establish a metric, which we refer to as the resilience parameter, to evaluate the ability of a material to retain tensile strength after damage recovery for shape memory polymer (SMP) systems. In this work, three SMP blends created for the additive manufacturing process of fused filament fabrication (FFF) were characterized. The three polymer systems examined in this study were 50/50 by weight binary blends of the following constituents: (1) polylactic acid (PLA) and maleated styrene-ethylene-butylene-styrene (SEBS-g-MA); (2) acrylonitrile butadiene styrene (ABS) and SEBS-g-MA); and (3) PLA and thermoplastic polyurethane (TPU). The blends were melt compounded and specimens were fabricated by way of FFF and injection molding (IM). The effect of shape memory recovery from varying amounts of initial tensile deformation on the mechanical properties of each blend, in both additively manufactured and injection molded forms, was characterized in terms of the change in tensile strength vs. the amount of deformation the specimens recovered from. The findings of this research indicated a sensitivity to manufacturing method for the PLA/TPU blend, which showed an increase in strength with increasing deformation recovery for the injection molded samples, which indicates this blend had excellent resilience. The ABS/SEBS blend showed no change in strength with the amount of deformation recovery, indicating that this blend had good resilience. The PLA/SEBS showed a decrease in strength with an increasing amount of initial deformation, indicating that this blend had poor resilience. The premise behind the development of this parameter is to promote and aid the notion that increased use of shape memory and self-healing polymers could be a strategy for mitigating plastic waste in the environment. 
    more » « less
  2. ; ; ; (, Scientific Data)
    Abstract Additive manufacturing (AM) is now widely used for research and industrial production. The benchmark data for mechanical properties of additively manufactured specimens is very useful for many communities. This data article presents a tensile testing dataset of ASTM D638 size specimens without and with embedded internal geometrical features printed using polylactic acid (PLA) in a Fused Filament Fabrication (FFF) additive manufacturing process. The added features can mimic defects of various shapes and sizes. This work is a supplement to the published research articleAssisted defect detection by in-process monitoring of additive manufacturing using optical imaging and infrared thermography(Additive Manufacturing, 2023, 103483). The printed specimens were tensile tested. Stress-strain graphs were developed and used to calculate the mechanical properties such as ultimate tensile strength (UTS) and strain at UTS. The mechanical properties, the correlations between mechanical properties and size, shape and location of geometrical features (defects), and the trends in mechanical properties can be useful in benchmarking the results of other researchers. 
    more » « less
  3. ; ; (, ACS Macro Letters)
    Developing effective recycling pathways for polyolefin waste, enabling a move to a circular economy, is an imperative that must be met. Post-use modification has shown promising results in upcycling polyolefins, removing the limitation of inertness, and improving the final physical properties of the recycled material while extending its useful lifetime. Grafting of maleic anhydride groups to polypropylene is an established industrial process that enhances its reactivity and provides a convenient route to further functionalization and upcycling. In this work, maleic anhydride grafted polypropylene (PPgMAH) was hydroxylated, and subsequently cured with a diisocyanate to form a thermoset polyurethane (PU). The crystal structure (unit cell and lamellar structure) of the polypropylene (PP) was preserved in the PU. At room temperature, the PU showed high modulus due to the crystallization behavior of the PP; upon increasing the temperature above the melting temperature, the modulus decreased to a rubbery plateau, consistent with formation of a network. The resulting PU showed higher glass transition temperature and lower degree of crystallinity than its PP predecessor due to the crosslinked nature of the polymer. The mechanical integrity of the PU was maintained through several reprocessing cycles due to the melt processability enabled by the presence of a urethane exchange catalyst. This functionalization and upcycling route thus offers a promising alternative to repurposing PP waste, in which the creation of melt-processable thermoset polymers expands applications for the materials. 
    more » « less
  4. (, Additive manufacturing)
    Additive manufacturing promises to revolutionize manufacturing industries. However, 3D printing of novel build materials is currently limited by constraints inherent to printer designs. In this work, a bench-top powder melt extrusion (PME) 3D printer head was designed and fabricated to print parts directly from powder-based materials rather than filament. The final design of the PME printer head evolved from the Rich Rap Universal Pellet Extruder (RRUPE) design and was realized through an iterative approach. The PME printer was made possible by modifications to the funnel shape, pressure applied to the extrudate by the auger, and hot end structure. Through comparison of parts printed with the PME printer with those from a commercially available fused filament fabrication (FFF) 3D printer using common thermoplastics poly(lactide) (PLA), high impact poly(styrene) (HIPS), and acrylonitrile butadiene styrene (ABS) powders (< 1 mm in diameter), evaluation of the printer performance was performed. For each build material, the PME printed objects show comparable viscoelastic properties by dynamic mechanical analysis (DMA) to those of the FFF objects. However, due to a significant difference in printer resolution between PME (X–Y resolution of 0.8 mm and a Z-layer height calibrated to 0.1 mm) and FFF (X–Y resolution of 0.4 mm and a Z-layer height of 0.18 mm), as well as, an inherently more inconsistent feed of build material for PME than FFF, the resulting print quality, determined by a dimensional analysis and surface roughness comparisons, of the PME printed objects was lower than that of the FFF printed parts based on the print layer uniformity and structure. Further, due to the poorer print resolution and inherent inconsistent build material feed of the PME, the bulk tensile strength and Young’s moduli of the objects printed by PME were lower and more inconsistent (49.2 ± 10.7 MPa and 1620 ± 375 MPa, respectively) than those of FFF printed objects (57.7 ± 2.31 MPa and 2160 ± 179 MPa, respectively). Nevertheless, PME print methods promise an opportunity to provide a platform on which it is possible to rapidly prototype a myriad of thermoplastic materials for 3D printing. 
    more » « less
  5. ; ; ; ; ; ; (, Polymer Chemistry)
    Post-polymerization modification (PPM) has been broadly employed to achieve functional polymer brush surfaces via immobilization of functional moieties on the brush using efficient organic tranformations. Here, we demonstrate the amine-anhydride reaction as a modular PPM route to functional brush surfaces using poly(styrene–maleic anhydride) (pSMA) copolymer brushes as a platform. The amine-anhydride reaction on pSMA surfaces proceeds to high conversions, with rapid kinetics, under ambient reaction conditions, and exploits a readily available library of functional amines. Using cystamine as a modifier, a convenient route to thiol-functionalized brushes was developed that enables sequential PPM modifications with a large library of alkenes using both base-catalyzed thiol-Michael and radical-mediated thiol–ene reactions. The high fidelity PPM reactions were demonstrated via the development of multifunctional, micropatterned brush surfaces. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email