Abstract The presence of the top electrode on hafnium oxide‐based thin films during processing has been shown to drive an increase in the amount of metastable ferroelectric orthorhombic phase and polarization performance. This “Clamping Effect,” also referred to as the Capping or Confinement Effect, is attributed to the mechanical stress and confinement from the top electrode layer. However, other contributions to orthorhombic phase stabilization have been experimentally reported, which may also be affected by the presence of a top electrode. In this study, it is shown that the presence of the top electrode during thermal processing results in larger tensile biaxial stress magnitudes and concomitant increases in ferroelectric phase fraction and polarization response, whereas film chemistry, microstructure, and crystallization temperature are not affected. Through etching experiments and measurement of stress evolution for each processing step, it is shown that the top electrode locally inhibits out‐of‐plane expansion in the HZO during crystallization, which prevents equilibrium monoclinic phase formation and stabilizes the orthorhombic phase. This study provides a mechanistic understanding of the clamping effect and orthorhombic phase formation in ferroelectric hafnium oxide‐based thin films, which informs the future design of these materials to maximize ferroelectric phase purity and corresponding polarization behavior.
more »
« less
Electrode Elastic Modulus as the Dominant Factor in the Capping Effect in Ferroelectric Hafnium Zirconium Oxide Thin Films
The discovery of ferroelectricity in hafnia based thin films has catalyzed significant research focused on understanding the ferroelectric property origins and means to increase stability of the ferroelectric phase. Prior studies have revealed that biaxial tensile stress via an electrode “capping effect” is a suspected ferroelectric phase stabilization mechanism. This effect is commonly reported to stem from a coefficient of thermal expansion (CTE) incongruency between the hafnia and top electrode. Despite reported correlations between ferroelectric phase fraction and electrode CTE, the thick silicon substrate dominates the mechanics and CTE-related stresses, negating any dominant contribution from an electrode CTE mismatch toward the capping effect. In this work, these discrepancies are reconciled, and the origin of these differences deriving from electrode elastic modulus, not CTE, is demonstrated. Pt/M/TaN/Hf0.5Zr0.5O2/TaN/Si devices, where M is platinum, TaN, iridium, tungsten, and ruthenium, were fabricated. Sin2(ψ)-based X-ray diffraction measurements of biaxial stress in the HZO layer reveal a strong correlation between biaxial stress, remanent polarization, and electrode elastic modulus. Conversely, a low correlation exists between the electrode CTE, HZO biaxial stress, and remanent polarization. A higher elastic modulus enhances the resistance to electrode elastic deformation, which intensifies the capping effect during crystallization, and culminates in the tandem restriction of out-of-plane hafnia volume expansion and preferential orientation of the polar c-axis normal to the plane. These behaviors concomitantly increase the ferroelectric phase stability and polarization magnitude. This work provides electrode material selection guidelines toward the development of high-performing ferroelectric hafnia into microelectronic devices, such as nonvolatile memories.
more »
« less
- Award ID(s):
- 2132918
- PAR ID:
- 10562902
- Publisher / Repository:
- American Chemical Society
- Date Published:
- Journal Name:
- ACS Applied Materials & Interfaces
- Volume:
- 16
- Issue:
- 50
- ISSN:
- 1944-8244
- Page Range / eLocation ID:
- 69588 to 69598
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Ferroelectric hafnium-zirconium oxide (HZO) is an excellent candidate for low-power non-volatile memory applications due to its demonstrated ferroelectricity at the nanoscale and compatibility with silicon-based technologies. The interface of HZO in contact with its electrode, typically TiN in a metal–ferroelectric–metal (MFM) capacitor configuration, is of particular interest because factors, such as volume confinement, impurity concentration, interfacial layers, thermal expansion mismatch, and defect trapping, are believed to play a crucial role in the ferroelectric performance of HZO-based devices. Processing variables, such as precursor type, oxygen source, dose duration, and deposition temperature, are known to strongly affect the quality of the oxide–metal interface. However, not many studies have focused on the effect of breaking or maintaining vacuum during MFM deposition. In this study, sequential, no-atmosphere processing (SNAP) is employed to avoid atmospheric exposure, where electrode TiN and ferroelectric HZO are deposited sequentially in the atomic layer deposition chamber without breaking vacuum. The effect of breaking vacuum during the sequential deposition steps is elucidated by fabricating and characterizing MFM capacitors with and without intentional vacuum breaks prior to the deposition of the HZO and top TiN. Using x-ray photoelectron spectroscopy and time-of-flight secondary ion mass spectrometry (ToF-SIMS), we reveal that breaking vacuum after bottom TiN electrode deposition leads to interfacial oxidation and increased carbon contamination, which preferentially stabilizes the non-ferroelectric tetragonal phase and lead to diminished remanent polarization. Avoiding carbon impurities and interfacial TiOx at the HZO and TiN interface using SNAP leads to heightened remanent polarization, reduced leakage current density, and elimination of the wake-up effect. Our work highlights the effect of vacuum breaking on the processing-structure-properties of HZO-based capacitors, revealing that maintaining vacuum can significantly improve ferroelectric properties.more » « less
-
Large remnant polarization and great reliability characteristics in W/HZO/W ferroelectric capacitorsIn this work, the effect of rapid thermal annealing (RTA) temperature on the ferroelectric polarization in zirconium-doped hafnium oxide (HZO) was studied. To maximize remnant polarization (2P r ), in-plane tensile stress was induced by tungsten electrodes under optimal RTA temperatures. We observed an increase in 2P r with RTA temperature, likely due to an increased proportion of the polar ferroelectric phase in HZO. The HZO capacitors annealed at 400°C did not exhibit any ferroelectric behavior, whereas the HZO capacitors annealed at 800°C became highly leaky and shorted for voltages above 1 V. On the other hand, annealing at 700 °C produced HZO capacitors with a record-high 2P r of ∼ 64 μ C cm −2 at a relatively high frequency of 111 kHz. These ferroelectric capacitors have also demonstrated impressive endurance and retention characteristics, which will greatly benefit neuromorphic computing applications.more » « less
-
In this work, hafnium zirconium oxide (HZO)-based 100 × 100 nm2 ferroelectric tunnel junction (FTJ) devices were implemented on a 300 mm wafer platform, using a baseline 65 nm CMOS process technology. FTJs consisting of TiN/HZO/TiN were integrated in between metal 1 (M1) and via 1 (V1) layers. Cross-sectional transmission electron microscopy and energy dispersive x-ray spectroscopy analysis confirmed the targeted thickness and composition of the FTJ film stack, while grazing incidence, in-plane x-ray diffraction analysis demonstrated the presence of orthorhombic phase Pca21 responsible for ferroelectric polarization observed in HZO films. Current measurement, as a function of voltage for both up- and down-polarization states, yielded a tunneling electroresistance (TER) ratio of 2.28. The device TER ratio and endurance behavior were further optimized by insertion of thin Al2O3 tunnel barrier layer between the bottom electrode (TiN) and ferroelectric switching layer (HZO) by tuning the band offset between HZO and TiN, facilitating on-state tunneling conduction and creating an additional barrier layer in off-state current conduction path. Investigation of current transport mechanism showed that the current in these FTJ devices is dominated by direct tunneling at low electric field (E < 0.4 MV/cm) and by Fowler–Nordheim (F–N) tunneling at high electric field (E > 0.4 MV/cm). The modified FTJ device stack (TiN/Al2O3/HZO/TiN) demonstrated an enhanced TER ratio of ∼5 (2.2× improvement) and endurance up to 106 switching cycles. Write voltage and pulse width dependent trade-off characteristics between TER ratio and maximum endurance cycles (Nc) were established that enabled optimal balance of FTJ switching metrics. The FTJ memory cells also showed multi-level-cell characteristics, i.e., 2 bits/cell storage capability. Based on full 300 mm wafer statistics, a switching yield of >80% was achieved for fabricated FTJ devices demonstrating robustness of fabrication and programming approach used for FTJ performance optimization. The realization of CMOS-compatible nanoscale FTJ devices on 300 mm wafer platform demonstrates the promising potential of high-volume large-scale industrial implementation of FTJ devices for various nonvolatile memory applications.more » « less
-
In this work, we investigate the device-to-device variations in the remanent polarization of metal–ferroelectric–insulator–metal stacks based on ferroelectric hafnium–zirconium–oxide (HZO). Our study employs a 3D dynamic multi-grain phase-field model to consider the effects of the polycrystalline nature of HZO in conjunction with the multi-domain polarization switching. We explore the dependence of variations on various design factors, such as the ferroelectric thickness and voltage stimuli (set voltage, pulse amplitude, and width), and correlate the trends to the underlying polarization switching mechanisms. Our analysis reveals a non-monotonic dependence of variations on the set voltage due to the coupled effect of the underlying polycrystalline structure variations and the voltage dependence of polarization switching mechanisms. We further report that collapsing of oppositely polarized domains at higher set voltages can lead to an increase in variations, while ferroelectric thickness scaling lowers the overall device-to-device variations. Considering the dynamics of polarization switching, we highlight the key role of voltage and temporal dependence of domain nucleation in dictating the trends in variations. Finally, we show that using a lower amplitude pulse for longer duration to reach a target mean polarization state results in lower variations compared to using a higher amplitude pulse for shorter duration.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1021/acsami.4c15934